This paper investigated the fatigue life behavior of two composite materials subjected to different times of shot peening (2, 4 and 6 min).The first material prepared from unsaturated polyester with E-glass reinforcement by 33% volume fraction. While, the second one was prepared from unsaturated polyester with aluminum powder by2.5% volume fraction. The experimental results showed that the improvement in endurance limit was obtained (for the first material) at 2, 4 and 6 min shot peening times where the percentage of maximum improvement was 25% at shot peening time of 6 min. While, the endurance limit of the second material decreased at shot peening times of 2, 4 and 6 min where the percentage of maximum reduction was 29 % at shot peenin

Background: Lymphomas are a group of diseases caused by malignant lymphocytes that accumulate in lymph nodes and cause the characteristic clinical features of lymphadenopathy. Intercellular adhesion molecule-1 (ICAM-1) (CD54) is a transmembrane glycoprotein belonging to the immunoglobulin superfamily of adhesion molecules. Cortactin was first identified as one of the major substrates for src kinase. because it localized to Cortical actin structures, The aims of this study was to evaluate and compare the immunohistochemical of ICAM-1 expression as cell adhesion molecule marker and Cortactin expression as invasive marker. Material and Methods: This study was performed on (68) formalin-fixed, paraffin-embedded blocks, histopathologically diagn

To achieve sustainability, use waste materials to make concrete to use alternative components and reduce the production of Portland cement. Lime cement was used instead of Portland cement, and 15% of the cement's weight was replaced with silica fume. Also used were eco-friendly fibers (copper fiber) made from recycled electrical. This work examines the impact of utilizing sustainable copper fiber with different aspect ratios (l/d) on some mechanical properties of high-strength green concrete. A high-strength cement mixture with a compressive strength of 65 MPa in line with ACI 211.4R was required to complete the assignment. Copper fibers of 1% by volume of concrete were employed in mixes with four different aspect ratios

This study aims to find out the effect of the mediator on scaffolding fourth yearstudent- teachers' teaching competencies and their self-efficacy. The present study combines scaffolding and self-efficacy by using a mediator on scaffolding students affects teaching competencies and selfefficacy and from the results of which the existence of student-teachers’ selfawareness was ensured as an effect of the same independent variable. The model affects their teaching competencies and led them to be aware of the needs of their pupils and themselves. 

Impact strength of self-compacted concrete is a field of interest, mostly when the concrete is produced from sustainable materials. This research's main objective is to clarify the ability to use two types of Portland limestone cement (Karasta and Tasluja) in self compacted concrete under impact loading, further to the economic and environmental benefits of the limestone cement. The impact loading was applied by a low-speed test, using the drop ball on concrete. Moreover, the study reveals the resistance of the grids reinforced concrete to impact loading by using polymer grid, and steel grid reinforced concrete slabs. Mixes reinforced by steel mesh had the highest results, indicating that the steel mesh was more robust because it had

Background: This study aimed to assess the effect of tooth shape ratio on mandibular incisor arrangement. Materials and methods: The sample included dental casts of some dental students and orthodontic patients having Class I dental and skeletal patterns with normal occlusion and severe crowding. The sample was divided into two groups according to the severity of crowding into: group I had Class I normal occlusion with mild or no crowded mandibular dentition and group II had Class I malocclusion with severe crowded mandibular dentition. Each group comprising of 40 subjects (20 males and 20 females). The mesio-distal and facio-lingual crown diameters were measured manually for each cast using modified vernier caliper gauge. Descriptive sta

Study the effect of additives polymer polyvinyl alcohol (PVA) after solving in water by concentration 10% since represent a standard of PVA solution with added to cement – silica composite of ratio (1:2) with 5%, 10%, 15%, 20%, and 25% respectively to the standard quantity of water which using as a mortar of building. The results are demonstrate increasing on compression resistance with increase of PVA solution until 20%, and decreasing of thermal conductivity which represent a composite are increasing in thermal insulating. The results were recommended decreasing of water absorption with increase of PVA solution ratio as illustrated in this study.

     In the present work effect of recycled heating and cooling on the values of concrete compressive strength due to high temperature of 400⁰C was studied.

    The tests show that the percent of reduction in compressive strength of the samples which exposed to a temperature of 400⁰C for one cycle was 32.5%, while the reduction was 52.7% for the samples which were exposed to recycled heating and cooling of ten times .      

   Moreover a study of the effect of specimen sizes on the percentages of compressive strength reduction due to high temperature