Wastewater discharge containing organic dyes may pose a hazard to the environment, which necessitates that dye removal must occur prior to wastewater release into water bodies. Herein, copper oxide nanoparticles (CuO NPs) were prepared by a green precipitation method to enable decolorization of a cationic dye (methyl violet; MV) from aqueous media. Complementary tools were employed to characterize the CuO NPs adsorbent: spectroscopy (FTIR and UV-VIS), microscopy (FESEM and TEM), XRD, BET surface area analysis, and point of zero charge (pHPZC) via potentiometry. The FTIR bands at 722, 663, 569, and 465 cm1 correspond to the vibrational modes of CuO NPs, along with the optical absorbance band at 275 nm that supports the formation of CuO NPs.

The adsorption of copper ions onto produced activated carbon from banana peels (with particle size 250 µm) in a single component system with applying magnetic field has been studied using fixed bed adsorber. The fixed bed breakthrough curves for the copper ions were investigated. The adsorption capacity for Cu (II) was investigated. It was found that 1) the exposure distance (E.D) and strength of magnetic field (B), affected the degree of adsorption; and 2) experiments showed that removal of Cu ions and accumulative adsorption capacity of adsorbent increase as the exposure distance and strength of magnetic field increase.
 

Desulfurization of a simulated diesel fuel by different adsorbents was studied in a fixed-bed adsorption process operated at ambient temperature and pressure.  Three different adsorption beds were used, commercial activated carbon, Cu-Y zeolite, and layered bed of 15wt% activated carbon followed by Cu-Y zeolite.Initially Y-zeolite was prepared from Iraqi rice husk and then impregnated with copper. In general, the adsorbents tested for total sulfur adsorption capacity at break through followed the order Ac/Cu-Y zeolite>Cu-Y zeolite>Ac. The best adsorbent, Ac/Cu-Y zeolite is capable of producing more than 30 cm3 of simulated diesel fuel per gram of adsorbent with a weighted average content of 5 ppm-S, while Cu-Y zeolite producing of

The development of low-cost, efficient, and environmentally friendly adsorbents capable of simultaneously removing both heavy metals and synthetic dyes from wastewater remains a critical challenge in environmental remediation. In this study, a novel chitosan/pumice (CS/PM) composite was synthesized and evaluated for its multifunctional adsorption performance toward four common and toxic pollutants: lead (Pb(II)), cadmium (Cd(II)), methylene blue (MB), and Congo red (CR). Characterization confirmed the successful integration of chitosan with pumice, resulting in reduced crystallinity, enhanced thermal stability, and active functional groups involved in adsorption. Adsorption experiments demonstrated optimal pollutant removal at a pH value of

This paper aims to study the chemical degradation of Brilliant Green in water via photo-Fenton (H2O2/Fe2+/UV) and Fenton (H2O2/Fe2+) reaction. Fe- B nano particles are applied as incrustation in the inner wall surface of reactor. The data form X- Ray diffraction (XRD) analysis that Fe- B nanocomposite catalyst consist mainly of SiO2 (quartz) and Fe2O3 (hematite) crystallites. B.G dye degradation is estimated to discover the catalytic action of Fe- B synthesized surface in the presence of UVC light and hydrogen peroxide. B.G dye solution with 10 ppm primary concentration is reduced by 99.9% under the later parameter 2ml H2O2, pH= 7, temperature =25°C within 10 min. It is clear that pH of the solution affects the photo- catalytic degradation

This research work involves the preparation of nano activated carbonand macro activated carbon from corn seeds with a various mixing ratio ofpotassium hydroxide (1:0, 1:0.2, 1:0.4, 1:0.6, 1:0.8 and 1:1) % using thermaland micro radiation carbonization to identify the best mixing ratio. At studyto confirmed that the efficiency and effectiveness of the prepared of activatedcarbon samples increase when ratio potassium hydroxide increase with athermal and micro radiation carbonization was used. The study of samplesexternal surface area was performed via studying the adsorption of methyleneblue from their aqueous solution, also measured the internal surface area wasperformed via studying the adsorption of iodine from their aqueous solution.Measu

Coagulation - flocculation are basic chemical engineering method in the treatment of metal-bearing industrial wastewater because it removes colloidal particles, some soluble compounds and very fine solid suspensions initially present in the wastewater by destabilization and formation of flocs. This research was conducted to study the feasibility of using natural coagulant such as okra and mallow and chemical coagulant such as alum for removing Cu and increase the removal efficiency and reduce the turbidity of treated water. Fourier transform Infrared (FTIR) was carried out for okra and mallow before and after coagulant to determine their type of functional groups. Carbonyl and hydroxyl functional groups on the surface of

Physical and chemical adsorption analyses were carried out by nitrogen gas using ASTM apparatus at 77 K and hydrogen gas using volumetric apparatus at room temperature respectively. These analyses were used for determination the effect of coke deposition and poisoning metal on surface area, pore size distribution and metal surface area of fresh and spent hydrodesulphurization catalyst Co-MoAl2O3 .Samples of catalyst (fresh and spent) used in this study are taken from AL-Dura refinery. The results of physical adsorption shows that surface area of spent catalyst reduced to third compare with fresh catalyst and these catalysts exhibit behavior of type four according to BET classification ,so, the pores of these samples are cylindrical, and the

This study was conducted in Animal Resources Department , College of Agriculture to estimate the effect of chemical and biological treatments to improve the nutritive value of poor quality roughages ( corn cobs and wild reed ) . The feeds were treated chemically with 4% NaoH solution ,whereas Aspergillus niger was used to ferment corn cobs and wild reed samples . The chemical analysis showed that protein percentages of corn cobs and wild reed was increased significantly (P<0.05) from 6.05% to 10.51% and 17.70% and from 3.10 %to 6.50% and 9.96% for both chemical and biological treatments respectively. The crude fiber percentages decreased significantly (P<0.05) from 29.19% and 26.10% to 23.60% and 20.10% for chemical treatment and was 20