We report a method of converting non-conductive plastic surfaces into conductive by plating either copper electroless or copper electroplating -carbon black containing bending Agent onto Perspex plastics . Various approaches have been studied in order to comparing properties of the plated copper for two methods such as scanning electron microscopy (SEM),thickness, roughness, porosity, tensile Strength and elongation. The results show that the surface of electroplating was uniform, compact, and continuous and it had an obvious metallic sheen, while the surface of plated copper for electroless for it had many pores. Also observed that the coating was composed of small cells. Thes

The performance of a condenser in a domestic refrigerator system without wires and a condenser with a novel design consisted of number of loops as elliptical shape is investigated experimentally in this work. The experiment was conducted with a refrigerator designed to work with HFC134a, under no load and with loads of (1.5,3 and 12 liters of water). In particular, the effects of shape change of the condenser were very important in heat transfer enhancement and reduce of the frictional loss as a result of reducing the pressure drop in the condenser. The results shown that compressor work decreases with elliptical condenser about (8.6% to 11.3%), and then the power consumption decreases also. The performance of household refrigerator with

An atomic force microscope (AFM) technique is utilized to investigate the polystyrene (PS) impact upon the morphological properties of the outer as well as inner surface of poly vinyl chloride (PVC) porous fibers. Noticeable a new shape of the nodules at the outer and inner surfaces, namely "Crater nodules", has been observed. The fibers surface images have seen to be regular nodular texture at the skin of the inner and outer surfaces at low PS content. At PS content of 6 wt.%, the nodules structure was varied from Crater shape to stripe. While with increasing of PS content, the pore density reduces as a result of increasing the size of the pore at the fiber surface. Moreover, the test of 3D-AFM images shows that the roughness of both su

The ZnO nanoparticles were synthesized at various precursor concentrations i.e. 0.05, 0.1, and 0.5 M by biosynthesis method based on Pometia pinnata Leaf Extracts. Initial nanoparticle concentration influenced the optical bandgap, shape, and structure of nanoparticles. The photodegradation process was carried out under UV illumination. The efficiency of MB degradation was determined by measuring the decrease in MB concentration and by analyzing the optical absorption at 663 nm recorded by UV-Vis spectroscopy. Results showed that the biosynthesized ZnO nanoparticles exhibited efficient photodegradation of MB, with a maximum degradation rate of 80% after 90 minutes of exposure to UV-C light. The study highlights the potential of Pometia pi

Electrochemical Grinding (ECG) process is a mechanically assisted electrochemical process for material processing. The process is able to successfully machine electrically conducting harder materials at faster rate with improved surface finish and dimensional control. This research studies the effect of applied current, electrolyte concentration, spindle speed and the gap between workpiece and tool on hardness and material removal rate during electrochemical grinding for stainless steel 316. The characteristic features of the electrochemical grinding process are explored through Taguchi-design-based experimental studies. The better hardness can be obtained at 10 A of the current, 150 g/l of the electrolyte concentration, 0.3 mm of gap an