Study the effect of additives polymer polyvinyl alcohol (PVA) after solving in water by concentration 10% since represent a standard of PVA solution with added to cement – silica composite of ratio (1:2) with 5%, 10%, 15%, 20%, and 25% respectively to the standard quantity of water which using as a mortar of building. The results are demonstrate increasing on compression resistance with increase of PVA solution until 20%, and decreasing of thermal conductivity which represent a composite are increasing in thermal insulating. The results were recommended decreasing of water absorption with increase of PVA solution ratio as illustrated in this study.

The study included adding antimony oxide to mixtures of coating metal surfaces (Enameling), after it was selected ceramic materials used in the coating metal pieces of the type of steel and cast iron in two layers. The first is called a ground coat and the second is a cover coat.
Ceramic materials layer for ground coat have been melted down in
platinum crucible at a temperature of 1200oC to prepare the glass
mixture (Frit). It was coated on metals at a temperature of 780oC for
two minutes, while the second layer was prepared glass mixture
(Frit) at a temperature of 1200oC, but was coated at a temperature of
760oC for two minutes.
Underwent tests crystalline state of powders (Frits) and enameled samples using X-ray di

The consequences of ionizing radiation-induced oxidative stress on radiographers in X-ray and CT-scan departments utilizing several biochemical were analyzed. The study found highly considerable discrepancies in the interplay between radiation levels and gender in terms of mean Malondialdehyde (MAD), Vitamin D3 (Vit.D3), Triiodothyronine (T3), Thyroxine (T4), and High-Density Lipoprotein (HDL), but not Thyroid Stimulating Hormone (TSH), cholesterol, triglyceride (TG) and Low-Density Lipoprotein (LDL). The findings indicated that malondialdehyde is a useful biomarker for assessing oxidative stress in radiographers with exposure to ionizing radiation.

This study was designed to show the inhibitory effect of different concentrations of alcoholic extract of Borage officinalis on the Monoamine oxidase (MAO) and Acetylcholinesterase (AChE) enzymes in human serum. The results obtained from the study exhibited that alcoholic extract of Borage officinalis caused inhibition to enzymes activity with all concentrations of the extract. The results also showed that when the concentration of the extract was (0.001 mg/ml), the percentage of inhibition was (4.3% with MAO and 15.2% with AChE) and this percentage increases until reaching up to (74.7% with MAO and 84.18% with AChE) when the concentration of the extract was (0.1 mg/ml). From the kinetic parameters, studies found that alcoholic extract o

Background: Dental erosion is a common oral condition which results due to consumption of high caloric and low pH acidic food such as carbonated drinks and fruit juices. It is expected that these food types can cause irreversible damage to dental hard tissues and early deterioration of the dental restorations. So, this study aimed to evaluate and compare the erosive potential effects of orange fruit juice and Miranda orange drink on the microhardness of an orthodontic composite material. Materials and methods: Thirty discs with a thickness of 2 mm and a diameter of 10 mm were prepared from orthodontic bonding composite. The prepared discs were equally divided into three groups (n=10). Microhardness analysis was carried out both prior to

In this study, composite materials consisting of Activated Carbon (AC) and Zeolite were prepared for application in the removal of methylene blue and lead from an aqueous solution. The optimum synthesis method involves the use of metakaolinization and zeolitization, in the presence of activated carbon from kaolin, to form Zeolite. First, Kaolin was thermally activated into amorphous kaolin (metakaolinization); then the resultant metakaolin was attacked by alkaline, transforming it into crystalline zeolite (zeolitization). Using nitrogen adsorption and SEM techniques, the examination and characterization of composite materials confirmed the presence of a homogenous distribution of Zeolite throughout the activated carbon.

The aim of this work is to study the effect of diesel fuel percentage on the combustion processes in compression ignition engine using dual – fuel (diesel and LPG).

 The brake thermal efficiency increased with the increase of diesel fuel rate at low loads, and decreased when load increased. To get sufficient operation in engine fueled with dual fuel, it required sufficient flow rate of diesel fuel, if the engine fueled with insufficient diesel fuel erratic operation with miss fire cycles presented.

Dual-fuel operation at part load showed higher specific fuel consumption than straight diesl operation. At full loads, brake specific fuel consumption of duel fuel engine approaches that for diesel fuel values.

Receipt date:3/13/2021 accepted date:5/26/2021 Publication date:12/31/2021

 This work is licensed under a Creative Commons Attribution 4.0 International License.

energy is one of the strategic resources within international politics, and this is through the existing competition between the international powers on it, and the global powers have begun to rely on interest in new areas, such as import, depending on new projects an

ABSTRACT

Naproxen(NPX) imprinted liquid electrodes of polymers are built using polymerization precipitation. The molecularly imprinted (MIP) and non imprinted (NIP) polymers were synthesized using NPX as a template. In the polymerization precipitation involved, styrene(STY) was used as monomer, N,N-methylenediacrylamide (N,N-MDAM) as a cross-linker and benzoyl peroxide (BPO) as an initiator. The molecularly imprinted membranes and the non-imprinted membranes were prepared using acetophenone(AOPH) and di octylphathalate(DOP)as plasticizers in PVC matrix. The slopes and detection limits of the liquid electrodes ranged from)-18.1,-17.72 (mV/decade and )4.0 x 10^-