A new series of chalcone derivatives featuring an oxadiazole-quinoline moiety were successfully synthesized through a multi-step reaction sequence, commencing with quinoline-2-carboxylic acid as the starting material. First, the carboxylic group was chlorinated to form an acid chloride, following reacted with hydrazine hydrate. The resulting product underwent cyclization with carbon disulfide in an alkaline solution to produce 5-(quinolin-2-yl)-1,3,4-oxadiazole-2-thiol, followed by alkylation using chloroacetone. In the final step, an aldol condensation reaction was carried out by grinding the acetone derivative with various aromatic aldehydes, yielding the desired chalcones. The synthesized compounds were characterized by Rf, FTIR,

This paper reports a.c., d.c. conductivity and dielectric behavior of Ep-hybrid composite with12 Vol.% Kevlar-Carbon hybrid . D.C. conductivity measurements are conducted on the graded composites by using an electrometer over the temperature range from (293-413) K. It was shown then that conductivity increases by increasing number of Kevlar –Carbon fiber layers (Ep1, Ep2, Ep3), due to the high electrical conductivity of Carbon fiber. To identify the mechanism governing the conduction, the activation energies at low temperature region (LTR) and at high temperature region (HTR) have been calculated. The activation energy values for hybrid composite decrease with increasing number of fiber layers. The a.c. conductivity was measured over fr

Spin coating technique used to prepare ZnPc, CdS and ZnPc/CdS blend thin films, these films annealed at 423K for 1h, 2h and 3h. Optical behavior of these films were examined using UV-Vis. and PL. The absorption spectrum of ZnPc shows a decreasing in absorption with the increase of annealing time while CdS spectrum give a clearly absorption peak at~510 nm. Energy gap of ZnPc increases from 1.41 to 1.52 eV by increasing the annealing time. E_g of CdS decrease by increasing annealing time, from 2.3 eV to 2.2 eV. The intensities of the peaks obtained from PL spectra were strongly dependent on annealing time and confirmed the results obtained from UV-Vis. D.C. conductivity measurement showed that all the thin films have two differen