In this work, chemical spray pyrolysis deposition (CSP) technique was used to prepare a mixed In2O3-CdO thin films with different CdO content (10, 30 and 50)%volume ratio on glass substrates at 150 ᵒC substrate temperature. The surface morphology and structural properties were measured to find the optimum conditions to improve thin films properties for using as photo detector. Current –Time, the sensitivity and response speed vary for each mixture. Samples with 10% vol. CdO content has square pulse response with average rise time nearly 1s and fall time 1s.

 This project introduces a prospective material for photonic laser applications. The material is olive oil which is classified as organic compound, having a good nonlinear optical properties candidate to be used in photonic applications. A high purity sample of olive oil has been used. The theoretical calculation to generate third harmonic wave using olive oil has been determine using MATLAB program. THG (λ=355nm) intensity has been determined at two cases of sample thicknesses 1mm and 10mm. The minimum threshold incident intensity to obtain THG intensity are equal I_ω=7530 mW/cm² at L=1mm and I_ω= 6220 mW/cm² at L=10mm. The possibility of generation of third harmonic in olive oil inside

           The current study aims to show the importance of plant products as mosquitocides against Culex quinquefasciatus. Castor oil Nanoemulsions were subedit in various ratios including castor oil, ethanol, tween 80, and deionized water by using ultrasonication. Thermodynamic, centrifugation, PH, assay which improved that the formula  of 10 ml  of castor  oil, ethanol  5ml, tween 80 (14 ml) and deionized water 71ml was more stable than other formulas. The stable formula of castor oil nanoemulsion was characterized by transmission electron microscopy (TEM) and dynamic light scattering (DLS). Nanoemulsion droplets were spherical in shape and were found to have a Z-average diameter of 87.4nm. A concentration of ca

In this research, a number of the western al-Anbar clays (red iron clays, Attapulgite) were modified by treating them thermally with a temperature of 650^oC. After that, these clays reflux with sodium hydroxide 5% for 1 hour by using microwave as a power supply. The research included fractionation alqayaira crude oil the fractionation included removing the asphaltene by precipitation from the crude using a simple paraffin solvent (normal hexane) as a non-soluble substance. After that it was filtered using the ash-free filter paper 42, the dissolved part, maltinate, was taken, drying a temperature of 75^oC and weight, and to find the percentage of the two parts. Malatine was divided into three main parts (paraf

ABSTRACT

This research included the preparation and characterization of new demulsifies from natural and synthetic polymers of chitosan and polyvinyl alcohol that are environmentally friendly and at the same time have high efficacy comparable to emulsifiers. imported foreign. The prepared compounds were examined using infrared spectroscopy and nuclear magnetic resonance spectroscopy, and all the spectral signals of the polymers were in good agreement with the chemical composition of the polymers. And the melting and decomposition that occur on polymers at high temperatures. The effect of the length and type of side chain in the compositions of polymers on the process of water separation of oil emulsions w

The process for preparing activated carbon (AC) made from tea residue was described in this paper. Investigated were the physicochemical characteristics and adsorption efficiency of the produced AC. Activation with potassium hydroxide (KOH) and carbonization at 350 °C are the two key steps in the manufacturing of AC. The activated carbon was used to adsorb Tetracycline (TC). Different parameters were studied at room temperature to show their effects on the adsorption efficiency of TC. These parameters are the initial concentration of adsorbate TC, solution acidity pH, time of adsorption, and adsorbent dosage. The prepared active carbon was characterized using Fourier transform infrared spectroscopy (FTIR), scanning electron microscopy (