The catalytic activity of faujasite type NaY catalysts prepared from local clay (kaolin) with different Si/Al ratio was studied using cumene cracking as a model for catalytic cracking process in the temperature range of 450-525° C, weight hourly space velocity (WHSV) of 5-20 h1, particle size ≤75μm and atmospheric pressure. The catalytic activity was investigated using experimental laboratory plant scale of fluidized bed reactor.
It was found that the cumene conversion increases with increasing temperature and decreasing WHSV. At 525° C and WHSV 5 h-1, the conversion was 42.36 and 35.43 mol% for catalyst with 3.54 Si/Al ratio and Catalyst with 5.75 Si/Al ratio, respectively, while at 450° C and at the same WHSV, the conversion w

Thirty five samples were collected from patients (1-30) years old, suffered from, infected skin , rushes, boils , oral thrush, anal & vaginal itches.  Candida albicans 57.3% (20 isolates) and Candida tropicalis 22.5% (8 isolates) Aspergillus  fumegatus 11.5% (4 isolates)   Aspergillus nigar 8.7%(3 isolates) , were isolated & identified from these samples.  Alcoholic & water hot extracts of the punica granatum (Pomegranate) peels as well as the dried powder were prepared.  The anti-fungal activity of the extracts was evaluated by means of the agar-well diffusion assay. The extract exhibited potent activity against yeast. The Minimum inhibitory concentra

  Foot and ankle movements are essential in various activities like walking, running, and balance, where the mechanics of these movements are affected by the muscles around the ankle joint [1,2]. In this study, the correlations between isometric ankle torque and muscle activity of the tibialis anterior (TA) and gastrocnemius (GAS) in the course of dorsiflexion and plantarflexion was investigated. Eight healthy participants were enrolled for the study, where the ankle torque and surface Electromyography (sEMG) of the main flexors were measured and analyzed. The results showed that ankle torque is higher in plantarflexion than dorsiflexion. In addition, the TA has greater muscle activity during dorsiflexion, while the GAS presents higher ac

Used cooking oil was undergoing trans-esterification reaction to produce biodiesel fuel. Method of production consisted of pretreatment steps, trans-esterification, separation, washing and drying. Trans-esterification of treated oils was studied at different operation conditions, the methanol to oil mole ratio were 6:1, 8:1, 10:1, and 12:1, at different temperature 30, 40, 50, and 60 ^º C, reaction time 40, 60, 80, and 120 minutes, amount of catalyst 0.5, 1, 1.5, and 2 wt.% based on oil and mixing speed 400 rpm. The maximum yield of biodiesel was 91.68 wt.% for treated oils obtained by trans-esterification reaction with 10:1 methanol to oil mole ratio, 60 ^º C reaction temperature, 80 minute reactio

Background: Calcaneus is a spongy cancellous bone with rich blood supply , its fracture heals more rapidly providing no occurrence of infection and soft tissue injury around ,no gross malposition of fragments. The associated pain leads to a major impairment in life quality. The aim of treatment for calcaneal fractures is the decrease of pain and rebuilding of walking ability for patients with normal foot shape and the ability to wear normal foot wear. To reduce complications, a minimally invasive technique for the treatment of displaced intra-articular fractures of the calcaneus was preferred to use.

The purpose of this study was to determine whether the closed reduction and percutaneous K. wire fixation of displ

were prepared by condensation of 6-R-2amino bcnzothiazol with Salicyldehyde.These Schiff bases were found to reach with maleic anhydride and citraconic to give

Impact strength of self-compacted concrete is a field of interest, mostly when the concrete is produced from sustainable materials. This research's main objective is to clarify the ability to use two types of Portland limestone cement (Karasta and Tasluja) in self compacted concrete under impact loading, further to the economic and environmental benefits of the limestone cement. The impact loading was applied by a low-speed test, using the drop ball on concrete. Moreover, the study reveals the resistance of the grids reinforced concrete to impact loading by using polymer grid, and steel grid reinforced concrete slabs. Mixes reinforced by steel mesh had the highest results, indicating that the steel mesh was more robust because it had

This paper presents a study to investigate the behavior of post-tensioned segmental concrete beams that exposed to high-temperature. The experimental program included fabricating and testing twelve simply supported beams that divided into three groups depending on the number of precasting concrete segments. All specimens were prepared with an identical length of 3150 mm and differed in the number of the incorporated segments of the beam (9, 7, or 5 segments). To simulate the genuine fire disasters, nine out of twelve beams were exposed to a high-temperature flame for one hour. Based on the standard fire curve (ASTM – E119), the temperatures of 300◦C (572◦F), 500◦C (932◦F), and 700◦C (1292◦F) were adopted. Consequently,