Hydrocarbon displacement at the pore scale is mainly controlled by the wetness properties of the porous media. Consequently, several techniques including nanofluid flooding were implemented to manipulate the wetting behavior of the pore space in oil reservoirs. This study thus focuses on monitoring the displacement of oil from artificial glass porous media, as a representative for sandstone reservoirs, before and after nanofluid flooding. Experiments were conducted at various temperatures (25 – 50° C), nanoparticles concentrations (0.001 – 0.05 wt% SiO₂ NPs), salinity (0.1 – 2 wt% NaCl), and flooding time. Images were taken via a high-resolution microscopic camera and analyzed to investigate the displacement of the oil

The aim of this project was to study the in vitro effect of antineoplastic drugs (vincristine and vinblastine) on mice spermatozoa. Eighteen adult (age 8-9 weeks) male mice were divided into three groups equally. The animals in each group were slain by cervical dislocation, the testes were removed and two tails of epididymides isolated. Spermatozoa were obtained from the two tails of epididymides by mincing in 500 µl TCM-199.The first group non-treated (unadded) as a control group, second group added 10 µg/ml of vincristine to TCM-199 and the third group added 10 µg/ml of vinblastine to TCM-199. After 10 minutes from added of vincristine and vinblastin measured the following test: spermatozoa activity, percentage dead spermatozoa and mor

Irisin is a myokine that controls energy metabolism by making adipose tissue brown. The present goal in doing this research was to determine how irisin concentration relates to other biochemical markers of disease. Hemodialysis (HD) for chronic kidney failure. The study included 30 individuals with end-stage renal disease on HD and 30 healthy subjects as the control group. The ages of all patients and the control group ranged from (25 to 60) years. The excluded criteria included patients with viral hepatitis and diabetes. Serum irisin concentration and the level of fasting serum glucose (FSG), urea, creatinine (Cr), total protein (TP), albumin (Alb), albumin to creatinine ratio (ACR), total cholesterol (TC), alanine aminotransferase (ALT),

A factorial experiment was applied with four replicates on rosemary plants (Rosmarinus officinalis L.) grown in pots inside the glasshouse of the Department of Biology, College of Science, Salahaddin University, Erbil, Iraq, during April, 2019 to July, 2020, to determine the effects of soil moisture content ( SM1: 100% and SM2: 60% field capacity), nitrogen fertilizer (N1: 100, N2: 200 and N3: 300kg/hectare), and magnesium fertilizer (Mg1: 0.0, Mg2: 30 and Mg3: 60kg/hectare) and their interactions on some growth characteristics  and essential oil content of rosemary plants. Two cuttings were taken from rosemary shoots (on March, 2020 and July, 2020) after 12 and 15 months of planting respectively. Results showed that cutting 1:

n-Hexane conversion enhancement was studied by adding TCE (Trichloro-ethylene) on feed stream using 0.3%Pt/HY zeolite catalyst. All experiments were achieved at atmospheric pressure and on a continuous laboratory unit with a fixed bed reactor at a temperature range 240-270◦C, LHSV 1-3h-1, H2/nC6 mole ratio 1-4.
By adding 435 ppm of TCE, 49.5 mole% conversion was achieved at LHSV 1h-1, temperature of 270ºC and H2/nC6 mole ratio of 4, while the conversion was 18.3 mol% on the same catalyst without adding TCE at the same conditions. The activation energy decreased from 98.18 for pure Pt/HY zeolite to 82.83 kJ/mole by adding TCE. Beside enhancement the activity, selectivity and product distribution enhanced by providing DMB (Dimethyl b

The CdSe pure films and doping with Cu (0.5, 1.5, 2.5, 4.0wt%) of thickness 0.9μm have been prepared by thermal evaporation technique on glass substrate. Annealing for all the prepared films have been achieved at 523K in vacuum to get good properties of the films. The effect of Cu concentration on some of the electrical properties such as D.C conductivity and Hall effect has been studied.
It has been found that the increase in Cu concentration caused increase in d.c conductivity for pure CdSe 3.75×10-4(Ω.cm)-1 at room temperatures to maximum value of 0.769(Ω.cm)-1 for 4wt%Cu.All films have shown two activation energies, where these value decreases with increasing doping ratio. The maximum value of activation energy was (0.319)eV f