Background: This study was formulated to compare the effect of 5%hydrofluoric acid in comparison to 37%phosphoric acid with and without the application of silane on bond strength of composite to porcelain. Materials and Methods: Specimen preparation was divided in to two phases, metal-disks fabrication (8mm-diameter and 4mm-thickness) and ceramic veneering. Thirty two specimens were prepared, sandblasted with 50 μm aluminum oxide, and divided into four groups of eight samples. Groups I and III were etched with 37%phosphoric acid while groups II and IV were etched with 5%hydrofluoric acid; and groups I and II were silaneted while groups III and IV were not. Heliobond, and resin composite were applied to each specimen using a plastic transpa

An attempt to synthesize the benzoimidazol derivatives from the reaction of o-phenylenediamine and benzoic acid derivatives in the presence of ethanol and various ketones under microwave irradiation, 1 , 5 - benzodiazepinum salt derivatives were obtained instead of them. Unexpected reaction was happened for synthesis a new series of benzodiazepinium salt derivatives in a selective yield . The reaction mechanism was also discussed. The new compounds were purified and identified their structures were elucidated using various physical techniques like; FT- IR spectra, micro elemental analysis (C.H.N) and 1H NMR spectra.

This work is concerned with the study of the effect of cement types, particularly OPC and SRPC, which are the main cement types manufactured in Iraq. In addition, study the effect of mineral admixtures, which are HRM and SF on the resistance of high performance concrete (HPC) to internal sulphate attack. The HRM is used at (10%) and SF is used at (8 and 10)% as a partial replacement by weight of cement for both types. The percentages of sulphate investigated are (1,2 and 3)% by adding natural gypsum as a partial replacement by weight of fine aggregate. The tests carried out in this work are: compressive strength, flexural strength, ultrasonic pulse velocity, and density at the age of 7, 28, 90 and 120 days.

The r

Health service institutions suffer from challenges resulting from the great changes that our world is witnessing today.  This has affected the value that these institutions add to the patient.

This research aims to identify the effect of integrating each of the techniques of QFD and value engineering for the health services provided to the patient to improve the value for him and thus obtain his satisfaction, which is reflected in the reputation of the surveyed hospitals. To achieve this, the descriptive analytical method was used, and a questionnaire was designed to collect the necessary data, which represents a measure of this research. The questionnaire was distri

Porous silicon (P-Si) has been produced in this work by photoelectrochemical (PEC) etching process. The irradiation has been achieved using diode laser of (2 W) power and 810 nm wavelength. The influence of various irradiation times on the properties of P-Si material such as P-Si layer thickness, surface aspect, pore diameter and the thickness of walls between pores as well as porosity and etching rate was investigated by depending on the scanning electron micrograph (SEM) technique and gravimetric measurements.

Films of pure Poly (methyl methacrylate) (PMMA) doped by potassium iodide (KI) salt with percentages (1%) at different thickness prepared by casting method at room temperature. In order to study the effect of increasing thickness on optical properties, transmission and absorption spectra have been record for five different thicknesses(80,140,210,250,320)µm. The study has been extended to include the changes in the band gap energies, refractive index, extinction coefficient and absorption coefficient with thickness.