Semiconductor-based metal oxide gas detector of five mixed from zinc chloride Z and tin chloride S salts Z:S ratio 0, 25, 50, 75 and 100% were fabricated on glass substrate by a spray pyrolysis technique. With thickness were about 0.2 ±0.05 μm using water soluble as precursors at a glass substrate temperature 500 ºC±5, 0.05 M, and their gas sensing properties toward CH4, LPG and H2S gas at different concentration (10, 100, 1000 ppm) in air were investigated at room temperature which related with the petroleum refining industry.
Furthermore structural and morphology properties were scrutinize. Results shows that the mixing ratio affect the composition of formative oxides were (ZnO, Zn2SnO4, Zn2SnO4+ZnSnO3, ZnSnO3, SnO2) ratios ment

Semi-empirical methods were applied for calculating the vibration frequencies and IR absorption intensities for normal coordinates of the {mono (C₅₆H₂₈), di (C₈₄H₂₈), tri (C₁₁₂H₂₈) and tetra (C₁₄₀H₂₈)} -rings layer for (7,7) armchair single wall carbon nanotube at their equilibrium geometries which were all found to have D₇d symmetry point group.

Assignment of the modes of vibration (3N-6) was done depending on the pictures of their modes by applying (Gaussian 03) program. Comparison of the vibration frequencies of (mono, di, tri and tetra) rings layer which are active in IR, and inactive in Ramman spectra. For C-H stretching vibrat

This research aims at identifying the communicative habits and content reflections on the communication process, especially the young audience which is one of the main group for whom the announcements are made. Because young people face life with passion and aspiration making them respond to each effect used by the media in the design of the advertising using all the effective techniques, attractive methods for young children like depending on drama, technical tricks, music and logos easily to be remembered and responded to the desires of the young in their entertainment. This research also aims at identifying the impact of the internet as a channel of commercial advertising on the purchasing behavior of young people at the universities

The use of the word “war” alone raises horror and fear in the hearts of the recipients, especially if this war aimed at human’s life, his health and his future. It is the electronic advertising war among rival international companies that use cyberspace to create fear and horror in the hearts of the recipients because it connects the use of the product with human’s death or serious illness.
The problem of this research sheds light on the new uses of cyberspace which fucked by international companies to strike the interests of each other by displaying the defects of their products and its negative impact on citizen’s life. Despite the fact that those wars have opposed strongly, there are supporters for those wars. Their argu

In this study , Iraqi Bentonite clay was used as a filler for polyvinyl chloride polymer. Bentonite clay was prepared as a powder for some certain particle size ,followed by calcinations process at (300,700,900) OC ,then milled and sieved. The selected sizes were D ~75 µm and D ~150. After that polyvinyl Al-Cohool solution prepared and used as a coated layer covered the Bentonite powder before applied as a filler ,followed by drying , milling and sieving for limited recommend sizes. polyvinyl chloride solutions were prepared and adding of modified Bentonite power at certain quantities were followed .Sheet of these variables on the mechanical and thermal properties of the prepared reinforced particular polyvinyl chloride composite

In this research thin films from SnO2 semiconductor have been prepared by using chemical pyrolysis spray method from solution SnCl2.2H2O at 0.125M concentration on glass at substrate temperature (723K ).Annealing was preformed for prepared thin film at (823K) temperature. The structural and sensing properties of SnO2 thin films for CO2 gas was studied before and after annealing ,as well as we studied the effect temperature annealing on grain size for prepared thin films .

The dual nature of asphalt binder necessitates improvements to mitigate rutting and fatigue since it performs as an elastic material under the regime of rapid loading or cold temperatures and as a viscous fluid at elevated temperatures. The present investigation assesses the effectiveness of Nano Alumina (NA), Nano Silica (NS), and Nano Titanium Dioxide (NT) at weight percentages of 0, 2, 4, 6, and 8% in asphalt cement to enhance both asphalt binder and mixture performance. Binder evaluations include tests for consistency, thermal susceptibility, aging, and workability, while mixture assessments focus on Marshall properties, moisture susceptibility, resilient modulus, permanent deformation, and fatigue characteristics. NS notably im

The dual nature of asphalt binder necessitates improvements to mitigate rutting and fatigue since it performs as an elastic material under the regime of rapid loading or cold temperatures and as a viscous fluid at elevated temperatures. The present investigation assesses the effectiveness of Nano Alumina (NA), Nano Silica (NS), and Nano Titanium Dioxide (NT) at weight percentages of 0, 2, 4, 6, and 8% in asphalt cement to enhance both asphalt binder and mixture performance. Binder evaluations include tests for consistency, thermal susceptibility, aging, and workability, while mixture assessments focus on Marshall properties, moisture susceptibility, resilient modulus, permanent deformation, and fatigue characteristics. NS notably im