Background: Dental casts come into direct contact with impression materials and other items that are contaminated by saliva and blood from a patient's mouth, leaving the casts susceptible to cross-contamination. The disinfectant solutions of the impression materials cause various adverse reactions. Therefore, disinfection of dental casts may be effective in preventing cross infection. This study was carried out to evaluate the surface hardness, dimensional accuracy, reproduction of details and surface porosity of type III, type IV and type IV extra hard dental stone after immersion in and spray by using SOLO and Sodium hypochlorite disinfectant solutions. Materials and methods: 240 Stone samples were prepared in rubber rings, A total of 60 test block were prepared for each test (surface hardness, dimensional accuracy, reproduction of details and surface porosity).the samples were divided into three groups (20 for each type of stone) type (III, IV, IV extra hard); SOLO and Sodium hypochlorite disinfectant by 2 methods (immersion and spray) were used in each test. Results: the results of dimensional accuracy, reproduction of details, surface hardness and surface porosity revealed no significant difference for all types of tested stone samples after immersion or spraying in SOLO and NaOCl except the surface hardness of type IV extra hard showed significant difference after spray with SOLO and the surface porosity of type IV extra hard showed significant difference after immersed in both SOLO and NaOCl solutions. Conclusions: Based on the results of this study immersion in and spray by using SOLO and NaOCl disinfectant solutions produced no adverse effect on dimensional accuracy, reproduction of details, surface hardness and surface porosity for type III, type IV dental stone and for type IV extra hard dental stone except for the surface hardness for type IV extra hard when sprayed with SOLO and the surface porosity when type IV extra hard stone immersed in the SOLO and NaOCl solutions.
The experiment was conducted to investigate the effect of prey type (Artemia nauplii, mosquito larvae and paramecium) on some reproductive aspects in crustacean zooplankton M. albidus which included reproductive period, post reproductive period, period spend to egg appearance and the period from appearance of egg to nauplii releasing. Results revealed that females fed on mosquito larvae had the highest mean of postreproductive period and lowest mean of the period spend to egg appearance, which differed significantly (P < 0.05) compared with the means of females who fed on Artemia nauplii and paramecium on the other hand the differences were not significant in reproductive period and the period from appearance of egg to nauplii releasing.
Portland cement concrete is the most commonly used construction material in the world for decades. However, the searches in concrete technology are remaining growing to meet particular properties related to its strength, durability, and sustainability issue. Thus, several types of concrete have been developed to enhance concrete performance. Most of the modern concrete types have to contain supplementary cementitious materials (SCMs) as a partial replacement of cement. These materials are either by-products of waste such as fly ash, slag, rice husk ash, and silica fume or from a geological resource like natural pozzolans and metakaolin (MK). Ideally, the utilization of SCMs will enhance the concrete performance, minimize
... Show More
(7)
The field efficacy of Actellic (organophosphate), Neporex (insect growth regulator) and
Ficam (carbamate), at the application rates of 2-4, 0.4-0.8 and 0.1-0.2 g AI/m2 respectively,
was studied against the larvae of Musca domestica L. Results of treatments involving horse
manure indicated that Actellic and Neporex produced sharp decrease of larval numbers (close
to zero) for 21d. But there was a slight recovery in larval numbers 14 d following treatment
with Ficam. The populations of predator mites were not affected due to insecticidal
applications.
Bioethanol produced from lignocellulose feedstock is a renewable substitute to declining fossil fuels. Pretreatment using ultrasound assisted alkaline was investigated to enhance the enzyme digestibility of waste paper. The pretreatment was conducted over a wide range of conditions including waste paper concentrations of 1-5%, reaction time of 10-30 min and temperatures of 30-70°C. The optimum conditions were 4 % substrate loading with 25 min treatment time at 60°C where maximum reducing sugar obtained was 1.89 g/L. Hydrolysis process was conducted with a crude cellulolytic enzymes produced by Cellulomonas uda (PTCC 1259).The maximum amount of sugar released and hydrolysis efficiency were 20.92 g/L and 78.4 %, respectively. Sugars
... Show More
(1)
(8)
(3)
(27)
(24)
This research aims to investigate and evaluate a reactive powder concrete (RPC) cast using economical materials. Its mechanical properties were investigated and evaluated by studying the effects of using different cement and silica fume contents and locally steel fibers aspect ratios as reinforcement for this concrete. A compressive strength of about 155.2MPa, indirect tensile strength of 16.0MPa, modulus of elasticity of 48.7GPa, flexural strength of 43.5MPa, impact energy of 3294.4kN.m and abrasion loss 0.59% have been achieved for reinforced RPC contains 910 kg/m3 cement content, silica fume content 185 kg/m3 of cement weight and fiber volume fraction 2%. The water absorption values w
... Show MorePorous Silicon (PSi) has been produced in this work by using Photochemical (PC) etching process by using a hydrofluoric acid (HF) solution. The irradiation has been achieved using quartz- tungsten halogen lamp. The influence of various irradiation times on the properties of PSi اmaterial such as layer thickness, etching rate and porosity was investigated in this work too.
The XRD has been studied to determine the crystal structure and the crystalline size of PSi material
Abstract:Porous Silicon (PSi) has been produced in this work by using Photochemical (PC) etching process by using a hydrofluoric acid (HF) solution. The irradiation has been achieved using quartz- tungsten halogen lamp. The influence of various irradiation times on the properties of PSi اmaterial such as layer thickness, etching rate and porosity was investigated in this work too. The XRD has been studied to determine the crystal structure and the crystalline size of PSi material