Background: This study evaluated the influence of different fiber formulations incorporation in resin composite on cuspal deflection (CD) of endodontically-treated teeth with mesio-occluso-distal (MOD) cavities. Materials and Methods: Thirty-two freshly extracted maxillary premolar teeth received MOD cavity preparation followed by endodontic treatment using single cone obturation technique, and divided into: Group I: direct composite resin only using a centripetal technique, Group II: direct composite resin with short fiber-reinforced composite (everX Flow), Group III: direct composite resin with leno wave ultra-high molecular weight polyethylene (LWUHMWPE) fibers placed on the cavity floor, and Group IV: direct composite resin with LWUHMWPE fibers placed circumferentially around the cavity walls (wallpapering technique). The CD was measured using a novel digital evaluation method, whereby each tooth was scanned by a desktop scanner (Medit T710) at three different time intervals: before and after cavity preparation, and after restoration. The intercuspal distance (ICD) was measured digitally in μm at each interval using Medit compare metrology software, followed by measurement of the CD by subtracting the ICD after cavity preparation; and after restoration from the before preparation one to obtain the “after cavity preparation CD1” and “the after restoration CD2”, respectively. The data were analyzed using one-way ANOVA and Tukey HSD tests at a significance level of 0.05. Results: The highest CD was recorded in Group I with statistically significant differences with all other groups (P<0.05). No statistically significant differences were found between the other groups (Groups II, III, and IV) (P>0.05). Conclusions: There was an inward deflection of the cusps in all groups following cavity preparation and restoration as elicited by the negative CD1 and CD2 values. The incorporation of fibers, regardless of their type or orientation, resulted in a significant reduction in CD of endodontically treated premolar teeth as compared with those restored with resin composite alone.
(1)
In this work, the elemental constituents of smoker and nonsmoker
teeth samples of human were analyzed by Laser induced breakdown
spectroscopy method (LIBS). Many elements have been detected in
the healthy teeth samples, the important once are Ca, P, Mg, Fe, Pb
and Na. Many differences were found between (female and male)
teeth in Ca, P, Mg, Na and Pb contents. The concentrations of most
toxic elements were found significantly in the smoker group. The
maximum concentrations of toxic elements such as Pb, Cd and Co
were found in older male age above 60 year. Also, it was found that
the minimum concentrations of trace elements such as Ca, P and Na
exist in this age group. From these results it is clear that the
Dielectric barrier discharges (DBD) can be described as the presence of contact with the discharge of one or more insulating layers located between two cylindrical or flat electrodes connected to an AC/pulse dc power supply. In this work, the properties of the plasma generated by dielectric barrier discharge (DBD) system without and with a glass insulator were studied. The plasma was generated at a constant voltage of 4 kV and fixed distance between the electrodes of 5 mm, and with a variable flow rate of argon gas (0.5, 1, 1.5, 2 and 2.5) L/min. The emission spectra of the DBD plasmas at different flow rates of argon gas have been recorded. Boltzmann plot method was used to calculate the plasma electron temperature (Te), and Stark broadeni
... Show More
(4)
(4)
Aim of the study: This study's goal was to determine how laser surface alteration affected wettability of injectable thermoplastic acrylic and heat cure acrylic denture base materials. Materials and methods: Injectable thermoplastic acrylic resin (Deflex) and heat cure acrylic (Procryla) were used in this study to produce forty-disc shaped specimens, 20 specimens for each material type. The control group was made up of ten samples of each type of plastic denture base material. The other ten samples were treated with a nano-pulse fiber-optic lens Nd:YAG laser. The results were looked at with the Kruskal-Wallis test and the unpaired t-test (a=.05). Results: Compared to the control groups, the laser-treated groups were more likely to sti
... Show More
This paper displays the effect of uncoated and coated chopped carbon fibers with alumina Al2O3 or Tri calcium phosphate (TCP) on the impact strength of acrylic poly methyl methacrylate (PMMA) denture base resin. To improve bonding between carbon fibers and coating materials powders, the surface of carbon fibers has been treated with Para amino benzoic acid (C9H10N2O3) and poly vinyl alcohol (PVA) was also used. The morphology of the coating layers has been examined by field emission scanning electron microscope (FE-SEM). From the results, PMMA reinforced with uncoated chopped carbon fiber has high impact strength value but still have bad aesthetic. Samples prepared b
... Show More
(5)
Background: This in vitro study was carried out to investigate the effect of post space regions (coronal, middle and apical), the effect of post types ( Manually Milled Zirconia post, Prefabricated Fiber post, prefabricated Zirconia post) and the type of cement used (GIC, self-adhesive resin cement) on the bond strength between the posts and root dentin by using push-out test. Material and methods: Forty eight mandibular premolars extracted for orthodontic reasons (single rooted) were instrumented with ProTaper system (hand use) and obturated with gutta percha for ProTaper using AH26® root canal sealer following the manufacturer instructions. After 24 hours, post space was prepared using Zirix and Glassix drills no.3 creating 8 mm dept
... Show More
(8)
(2)
The utilization and incorporation of glass fiber-reinforced plastics (GFRP) in structural applications and architectural constructions are progressively gaining prominence. Therefore, this paper experimentally and numerically investigates the use of GFRP I-beams in conjunction with concrete slabs to form composite beams. The experimental design incorporated 2600 mm long GFRP I-beams which were connected compositely to concrete slabs with a 500 mm width and 80 mm thickness. The concrete slabs are categorized into two groups: concrete slabs cast using normal-strength concrete (NSC), and concrete slabs prepared using high-strength concrete (HSC). Various parameters like the type of concrete (normal and high-strength concrete), type of
... Show More
(35)
(34)