The study included adding antimony oxide to mixtures of coating metal surfaces (Enameling), after it was selected ceramic materials used in the coating metal pieces of the type of steel and cast iron in two layers. The first is called a ground coat and the second is a cover coat.
Ceramic materials layer for ground coat have been melted down in
platinum crucible at a temperature of 1200oC to prepare the glass
mixture (Frit). It was coated on metals at a temperature of 780oC for
two minutes, while the second layer was prepared glass mixture
(Frit) at a temperature of 1200oC, but was coated at a temperature of
760oC for two minutes.
Underwent tests crystalline state of powders (Frits) and enameled samples using X-ray di

The semiconductor ZnO is one of II – VI compound group, it is prepare as thin films by using chemical spray pyrolysis technique; the films are deposited onto glass substrate at 450 °C by using aqueous zinc chloride as a spray solution of molar concentration 0.1 M/L. Sample of the prepared film is irradiating by Gamma ray using CS 137, other sample is annealed at 550°C. The structure of the irradiated and annealed films are analyzed with X-ray diffraction, the results show that the films are polycrystalline in nature with preferred (002) orientation. The general morphology of ZnO films are imaged by using the Atomic Force Microscope (AFM), it constructed from nanostructure with dimensions in order of 77 nm.
The optical properties o

The presence of alkaloids in Crassula ovata is a topic that is still unexplored, as there are no published studies on the matter. This study demonstrates the presence of an alkaloid compound (and its class) for the first time in Crassula ovata. The plant material was defatted with n-hexane, and a Soxhlet apparatus was used for the extraction process, while the acid-base method was used for the isolation of alkaloids from the chloroform fractions. The quaternary alkaloid was precipitated from the aqueous layer spontaneously, in high quantity. By using standard spectroscopic methods (including liquid chromatography - mass spectroscopy) we were able to clarify the structure of the precipi¬tated compound as a tetrahydroprotoberberine a

The synthesis of zeolite NaX from locally available kaolin has been studied. The operating conditions for zeolite NaX production from kaolin with good crystallinity were as follows; a gel formation step of metakaolin in alkaline medium in presence of additional silica to crystallize the zeolite was achieved at 60 oC for 1 hr,and with stirring. In ageing step of the reactants at room temperature for 5 days and crystallization step at 87±2 oC for 24 hr. The catalytic activity of catalyst prepared from local kaolin was studied by using cumene cracking as a model for catalytic cracking and compared with standard HY zeolite and HX zeolite catalysts. The activity test was carried out in a laboratory continuous flow unit with fixed bed re

Nanosponges (NS) of etodolac(ETO) was prepared using the emulsion solvent diffusion method ; the effects of drug: polymer ratio, the effect of level concentration of internal phase and stirring time and other variables that effect on the physical characteristics of NS were investigated and characterized, The selected formula was lyophilized then incorporated into hydrogel ; which also evaluated .The results show that the formulation that contain Drug: PVA:EC in ratio 1:3:2 is the best with smallest particle size 40.2±0.098 with polydispersibility0.005 and in vitro release 97.6±0.11%, , ETO NS Carbopol hydrogel produced a significant(p<0.05) improvement of the in vitro release than pure ETO hydrogel.

The objective of this study was to isolate and identify the asparaginase-producing bacteria, then purify and characterize the enzyme in order to investigate their properties in the future. Fifteen local bacterial isolates were isolated from various sites in the city of Baghdad, identified by conventional morphological and biochemical procedures, and confirmed using vitek 2 methods, and submitted to primary screening processes for asparaginase production. For secondary screening, eight isolates with the greatest yellow zone ability on a specific solid medium were chosen. Bacillus sp. was reported to have the highest enzyme production (7.5 U/mg proteins). After 24 hours of incubation, submerged fermentation yielded optimal conditi