CdS films were prepared by thermal evaporation technique at thickness 1 µm on glass substrates and these films were doped with indium (3%) by thermal diffusion method. The electrical properties of these have been investigated in the range of diffusion temperature (473-623 K)> Activation energy is increased with diffusion temperature unless at 623 K activation energy had been decreased. Hall effect results have shown that all the films n-type except at 573 and 623 K and with increase diffusion temperature both of concentration and mobility carriers were increased.

In this article, the influence of group nano transition metal oxides such as {(MnO₂), (Fe₂O₃) and (CuO)} thin films on the (ZnO-TiO2) electric characteristics have been analyzed. The prepared films deposited on glass substrate laser Nd-YAG with wavelength (ℷ =1064 nm) ,energy of (800mJ) and number of shots (400). The density of the film was found to be (200 nm) at room temperature (RT) and annealing temperature (573K).Using DC Conductivity and Hall Effect, we obtained the electrical properties of the films. The DC Conductivity shows that that the activation energies decrease while the σRT at annealing temperature with different elements increases the formation of mixed oxides. The Hall effect, the elec

tA novel synthesis procedure is presented for preparing triethanolamine-treated graphene nanoplatelets(TEA-GNPs) with different specific areas (SSAs). Using ultrasonication, the covalently functionalizedTEA-GNPs with different weight concentrations and SSAs were dispersed in distilled water to prepareTEA-GNPs nanofluids. A simple direct coupling of GNPs with TEA molecules is implemented to synthesizestable water-based nanofluids. The effectiveness of the functionalization procedure was validated by thecharacterization and morphology tests, i.e., FTIR, Raman spectroscopy, EDS, and TEM. Thermal conduc-tivity, dispersion stability, and rheological properties were investigated. Using UV–vis spectrometer, ahighest dispersion stability of 0.876

This paper reports an experimental study regarding the influence of vertical oscillations on the natural convection heat transfer from a vertical channel. An experimental set-up was constructed and calibrated; the vertical channel was tested in atmosphere at 25o
C. The channel-to-ambient temperature difference was varied with the power supply to the electrical heater ranging between
15W to 70W divided into five levels. Data sets were measured under different operating condition from a test rig under six vibrating velocities (VVs) levels ranging from (5-30 m/s) in addition to the stationary state. The results show that the maximum heat transfer enhancement factor (E) occurs at Rayleigh number (Ra=2.328×103 ) and vibrational Reynol

The study aimed to recommend a new spectrophotometric-kinetic method for determination of carbamazepine (CABZ) in its pure form and pharmaceutical forms. The proposed procedure based on the coupling of CABZ with diazotized sulfanilic acid in basic medium to yield a colored azo dye. Factors affecting the reaction yield were studied and the conditions were optimized. The colored product was followed spectrophotometrically via monitoring its absorbance at 396 nm. Under the optimized conditions, two method (the initial rate and fixed time (10 minute)) were applied for constructing the calibration graphs. The graphs were linear in concentration ranges 2.0 to 18.0 µg.mL^-1 for both methods. The proposed was applied successfully in

Nanostructure of chromium oxide (Cr₂O₃-NPs) with rhombohedral structure were successfully prepared by spray pyrolysis technique using Aqueous solution of Chromium (III) chloride CrCl₃ as solution. The films were deposited on glass substrates heated to 450°C using X-ray diffraction (XRD) shows the nature of polycrystalline samples. The calculated lattice constant value for the grown Cr₂O₃ nanostructures is a = b = 4.959 Å & c = 13.594 Å and the average crystallize size (46.3-55.6) nm calculated from diffraction peaks, Spectral analysis revealed FTIR peak characteristic vibrations of Cr-O Extended and Two sharp peaks present at 630 and 578 cm-1 attributed to Cr-O “stretching

A simple, accurate and sensitive spectrophotometric method for the determination of Procaine penicillin (PP) is described. The method is based on charge-transfer reaction of PP with metol (N-methyl-p-hydroxy aniline) in the presence of ferric sulphate to form a purple-water soluble complex ,which is stable and has a maximum absorption at 510 nm .A graph of absorbance versus concentration shows that Beer’s low is obeyed over the concentration range of 3-80 µg /ml of PP (i.e.,3-80 ppm) with a molar absorbativity of 4.945 ×103 L.mol-1.cm-1 ,Sandell sensitivity of 0.1190 µg cm-2 ,a relative error of (-1.57)-2.79 % and a standard deviation of less than 0.59 depending on the concentration of PP.The optimum conditions for full co