Background: In this study we evaluate the effect of plasma treatment (oxygen and argon) gas in two different exposure times on the surface of heat cure and light cure acrylic resin. Materials and method: 100 specimens of heat cure and light cure acrylic resin were fabricated. The measurements of the samples were (75mm, 25mm and 4.5mm) length, width and depth respectively with stopper of 3mm depth. Two types of gas used oxygen and argon in (5,10) min by using (DC-glow discharge plasma device) then we apply cold cure soft lining material, with the help of Instron machine we test the shear stress value. Results: A highly significant effect after argon and oxygen gases treatment in both 5 and 10 min exposure times on shear bond strength to soft

Four Co(II), (C1); Ni(II), (C2); Cu(II), (C3) and Zn(II), (C4) chelates have been synthesized with 1-(4-((2-amino- 5‑methoxy)diazenyl)phenyl)ethanone ligand (L). The produced compounds have been identified by using spectral studies, elemental analysis (C.H.N.O), conductivity and magnetic properties. The produced metal chelates were studied using molar ratio as well as sequences contrast types. Rate of concentration (1 ×10􀀀 4 - 3 ×10􀀀 4 Mol/L) sequence Beer’s law. Compound solutions have been noticed height molar absorptivity. The free of ligand and metal chelates had been applied as disperse dyes on cotton fabrics. Furthermore, the antibacterial activity of the produced compounds against various bacteria had been investigated. F

The aim of this study was to evaluate the effects of local application of bisphosphonate gel and recombinant human bone morphogenic protein 2 gel, on titanium dental implant stability and marginal bone level. Twenty-seven patients with upper and lower missing posterior tooth/teeth were included in the study with a total of 71 implants that were used for rehabilitation. The implants were randomly divided into 4 groups: 3 study groups and 1 control. Group1; local application of bisphosphonate gel, group 2; local application of recombinant human bone morphogenic protein 2 gel, group 3; local application of a mixed formula of both gels. The gel application was immediately preimplant insertion, group 4; implant insertion without application of a

Background: The PMMA polymer denture base materials are low in thermal and strength properties. The aim of the study was to investigate the change in glass transition temperature, E-Moudulus and coefficient of thermal expansion of acrylic denture base material by addition of Al2O3, TiO2 and SiO2nano-fillers in 5% by weight. Materials and methods: The type of polymerization is free radical bulk polymerization. one hundred twenty (120) specimens were prepared , the specimens were divided into four groups according to the material had been added (one control and three for Al2O3, TiO2 and SiO2nanocomposite) each group was subdivided in to three groups according to the test had been done on it, the degree of transition (Tg) was measured by The d

Background: Diabetes mellitus is a major risk factor for chronic periodontitis (CP) and hyperglycemia has an important role in the enhancement of the severity of the periodontitis. It has been reported that the progression of CP causes shifting of the balance between bone formation and resorption toward osteoclastic resorption, and this will lead to the release of collagenous bone breakdown products into the local tissues and the systemic circulation. Cross-linked N-telopeptide of type I collagen (NTx) is the amino-terminal peptides of type I collagen which is released during the process of bone resorption. This study was conducted to determine the effects of nonsurgical periodontal therapy on serum level of NTx in type 2 diabetic patients

In this research, the X-ray diffraction pattern was used, which was obtained experimentally after preparation of barium oxide powder. A program was used to analyze the X-ray diffraction lines of barium oxide nanoparticles, and then the particle size was calculated by using the Williamson-Hall method, where it was found that the value of the particle size is 25.356 nm. Also, the dislocation density was calculated, which is equal to1.555 x1015 (lines/nm2), and the value of the unit cell number was also calculated, as it is equal to 23831.

Accelerates operating managements in the facilities contemporary business environment toward redefining processes and strategies that you need to perform tasks of guaranteeing them continue in an environment performance dominated by economic globalization and the circumstances of uncertainty attempt the creation of a new structure through multiple pages seek to improve profitability and sustainable growth in performance in a climatefocuses on the development of institutional processes, reduce costs and achieve customer satisfaction to meet their demands and expectations are constantly changing. The research was presented structural matrix performance combines methodology Alsigma in order to improve customer satisfaction significantly bet