The performance and lifetime of the flexible asphalt pavement are mainly dependent on the interfacial bond strength between layer courses. To enhance the bond between layers, adhesive materials, such as tack coats, are used. The tack coat itself is a bituminous material, which is applied on an existing relatively non-absorbent surface to ensure a strong bond between the old and newly paved layer. The primary objective of this study was to evaluate the effects of various types of tack coat materials on interlayer bond strength and to determine the optimal application rate for each type. The tack coat types used in this paper were RC-70, RC-250, and CSS-1h. Both laboratory-prepared and field-constructed hot mix asphalt concrete pavements usin

Films of PMMA and copper sulphate doped PMMA have been prepared by casting method. Absorbance and transmittance spectra were recorded in the wavelength range (300-900) nm in order to calculate, single oscillator energy, dispersion energy, average oscillator strength, the refractive index at infinite wavelength, M-1 and M -3 moments of the optical spectra, it was found that all these parameters were effected by doping.

Cefixime is an antibiotic useful for treating a variety ofmicroorganism infections. In the present work, tworapid, specific, inexpensive and nontoxic methods wereproposed for cefixime determination. Area under curvespectrophotometric and HPLC methods were depictedfor the micro quantification of Cefixime in highly pureand local market formulation. The area under curve(first technique) used in calculation of the cefiximepeak using a UV-visible spectrophotometer.The HPLC (2nd technique) was depended on thepurification of Cefixime by a C18 separating column250mm (length of column) × 4.6 mm (diameter)andusing methanol 50% (organic modifier) and deionizedwater 50% as a mobile phase. The isocratic flow withrate of 1 mL/min was applied, the temper

This research is presented experimental and numerical investigations of composite concrete-steel plate shear walls under axial loads to predicate the effect of both concrete compressive strength and aspect ratio of the wall on the axial capacity, lateral displacement and axial shortening of the walls. The experimental program includes casting and testing two groups of walls with various aspect ratios. The first group with aspect ratio H/L=1.667 and the second group with aspect ratio H/L=2. Each group consists of three composite concrete -steel plate wall with three targets of cube compressive strength of values 39, 54.75 and 63.3 MPa. The tests result obtained that the increase in concrete compressive strength results in increasing

Background: White spot lesions (WSLs) are subsurface enamel demineralization manifested as white opacities which had an esthetic problem. The purpose of this in-vitro study was to evaluate the lesion depth improvement of WSLs following application of fluoride varnish, tooth mousse and resin infiltration (ICON). Materials and methods: Artificial WSLs were created on 120 premolar teeth using demineralization solution with pH (4-4.5). Samples randomly allocated into four groups; fluoride varnish, tooth mousse, ICON and untreated group. Groups were discolored in Cola and orange juice for 24 hours. Teeth were ground sectioned by longitudinal cutting then these sections examined and photographed under stereomicroscope at 12X magnification then an

The notion of a Tˉ-pure sub-act and so Tˉ-pure sub-act relative to sub-act are introduced. Some properties of these concepts have been studied.

Phosphorus and dye (direct black) removal for small – scale wastewater applications were investigated using oven dried alum sludge (ODS).The use of alum sludge not only provides a low cost technique but also reduces the hazard and the cost related to the disposal of large amount of alum sludge. Phosphorus and dye removal exceeds 90% for all operating conditions applied in the research.
The residuals generated during the treatment of wastewater were further tested to study the possibility of aluminum leaching from oven dried alum sludge during the adsorption of phosphorus and dye. These tests observed a reduction in aluminum leaching indicating a lower risk imposed on land and surface water based on disposal options rather than on al

The present research  investigates joints welding of 304L austenitic stainless steel using metal inert gas (MIG) welding method. The research explores the effect of process parameters (arc voltage, wire feed rate, and electrode wire diameter) on the mechanical properties of stainless steel.  The above variables are varied  respectively with 18.5, 19, 19.5 V, 116, 127, 137 mm/s, and 0.8, 1, 1.2 mm, with E308L as a filler electrode. The design matrix of the experiments was determined using the design of experiment (DOE) program Minitab 17 based on the levels of input elements used. The Taguchi orthogonal matrix methodology (Taguchi) technique was used to develop some empirical analysis for the maximum tensile strength and proper surface