The aim of this work is to evaluate some mechanical and physical
properties (i.e. the impact strength, hardness, flexural strength,
thermal conductivity and diffusion coefficient) of
(epoxy/polyurethane) blend reinforced with nano silica powder (2%
wt.). Hand lay-up technique was used to manufacture the composite
and a magnetic stirrer for blending the components. Results showed
that water had affected the bending flexural strength and hardness,
while impact strength increased and thermal conductivity decreased.
In addition to the above mentioned tests, the diffusion coefficient
was calculated using Fick’s 2nd law.

Tin Selenide (SnSe) Nano crystalline thin films of thickness 400±20 nm were deposited on glass substrate by thermal evaporation technique at R.T under a vacuum of ∼ 2 × 10− 5 mbar to study the effect of annealing temperatures (as-deposited, 100, 150 and 200) °C on its structural, surface morphology and optical properties. The films structure was characterized using X-ray diffraction (XRD) which showed that all the films have polycrystalline in nature and orthorhombic structure, with the preferred orientation along the (111) plane. These films was synthesized of very fine crystallites size of (14.8-24.5) nm, the effect of annealing temperatures on the cell parameters, crystallite size and dislocation density were observed.

A series of new coumarin and N-amino-2-quinolone derivatives have been synthesized. The reaction of coumarin (1) with excess of  Hydrazine hydrate 98% yielded 1-amino-2-quinolone (2), Compound (2) was reacted with different Sulfonyl chloride to yield Sulfonamides [ N-(2-oxoquinolin-1(2H)-yl) methane sulfonamide (3), N-(2-oxoquinolin-1(2H)-yl) Benzene sulfonamide (4) and 4-methyl-N-(2-oxoquinolin-1(2H)-yl) benzene sulfonamide (5) ], while  reaction of  2-(4-methyl-2-oxo-2H-chromen-7-yloxy) acetic acid (8) with different amines yielded compounds [  2-(4-methyl-2-oxo-2H-chromen-7-yloxy)-N-(2-oxoquinolin-1(2H)-yl) acetamide (9) and N-(5-methyl-1,3,4-thiadiazol-2-yl)-2-(4-methyl-2-oxo-2H-chromen-7-yloxy)acetamide (10) ] th

One of the most important processes to obtain gasoline with high octane numbers is isomerization. In this paper, Pt/TiO2 was prepared successfully by using the sol–gel method by hydrolysis of titanium tetraisopropoxide as a titania source with ethanol and then platinum was loaded on the synthesized catalyst; the result shows that the sample prepared has a good crystallinity with a surface area of about 85 m2 /g and a pore volume of 0.1938 cm3 /g, while XRD shows that the prepared sample was anatase phase. The efect of both temperature and liquid hourly space velocity of the prepared catalyst was achieved by hydroisomerization of n-hexane in a fxed bed reactor with a temperature of 200–275 °C and LHSV 0.5–2h−1. The results show

In this study, a platinum(II) complex ([Pt(H2L)(PPh3)] complex) containing a thiocarbohydrazone as the ligand was tested as an anti-proliferative agent against ovarian adenocarcinoma (Caov-3) and human colorectal adenocarcinoma (HT-29) through MTT assays. Apoptotic markers were tested by the AO/PI double staining assay and DNA fragmentation test. Flow cytometry was conducted to measure cell cycle distribution, while the p53 and caspase-8 pathways were tested via immunofluorescence assay. Results demonstrated that the cytotoxic effect of the Pt(II)- thiocarbohydrazone complexes against Caov-3 and HT-29 cells was highly significant, and this effect triggered the activation of the p53 and caspase-8 pathways. Besides, apoptosis stimulated by th

In this work, polyvinylpyrrolidone (PVP), Multi-walled carbon nanotubes (MWCNTs) nanocomposite was prepared and hybrid with Graphene (Gr) by casting method. The morphological and optical properties were investigated. Fourier Transformer-Infrared (FT-IR) indicates the presence of primary distinctive peaks belonging to vibration groups that describe the prepared samples. Scanning Electron Microscopy (SEM) images showed a uniform dispersion of graphene within the PVP-MWCNT nanocomposite. The results of the optical study show decrease in the energy gap with increasing MWCNT and graphene concentration. The absorption coefficient spectra indicate the presence of two absorption peaks at 282 and 287 nm attributed to the π-π* electronic tr