A new series of 5-methoxy-2-mercapto benzimidazole derivatives were synthesized by the reaction of 5-methoxy- 2-mercaptobenzimidazole with chloroacetic acid and affords 2-((5-methoxy-1H-benzo[d]imidazol-2-yl)thio) acetic acid (1),which on cyclization with acetic anhydride and pyridine gives 7- methoxybenzo[4,5]imidazo[2,1-b]thiazol- 3(2H)-one(2), which on condensation with different aryl aldehydes in the presence of anhydrous sodium acetate in glacial acetic acid, furnishes a arylidene thiazolidinone. The purity of the synthesized compounds was confirmed by melting point and TLC.The structures were established by different spectral analysis such as FTIR,1HNMR, and CHN analysis. The newly synthesized compounds (3a-d) were in vivo evaluated f

Objective: Synthesis, Characterization of formazan derivatives and studies the antioxidant activity of prepared compounds and molecular docking. Methods: In this study, formazan compounds (III–XIV) were produced by combining Schiff base compounds (I), (II) with diazonium salts resulting from reactions of different aromatic amines with sodium nitrate in the presence of Con.HCl at 0–5°C. When isonicotinic acid hydrazide reacts with (N,N-dimethylbenzaldehyde, 4-hydroxy-3-methoxybenzaldehyde) in the presence glacial acetic acid as a solvent Schiff base compounds are created. Results: The prepared compounds were identified by FT-IR, 1H NMR, 13C NMR, then the antioxidant activity of the derivatives and molecular docking were studied. D

Two Schiff base ligands L1 and L2 have been obtained by condensation of salicylaldehyde respectively with leucylalanine and glycylglycine then their complexes with Zn(II)were prepared and characterized by elemental analyses , conductivity measurement , IR and UV-Vis .The molar conductance measurement indicated that the Zn(II) complexes are 1:1 non-electrolytes. The IR data demonstrated that the tetradentate binding of the ligands L1 and L2 . The in vitro biological screening effect of the investigated compounds have been tested against the bacterial species Staphlococcus aureus, Escherichia coil , Klebsiella pneumaniae, Proteus vulgaris and Pseudomonas aeruginosa by the disc diffusion method . A comparative study of inhibition values of

In this work, studying the effect of ethylenediamine as a corrosion inhibitor was investigated for carbon steel in aerated HCl solution in range of 0.1-1N under dynamic conditions, i.e., rotational velocity of 400–1200 rpm in the temperature range 35 – 65 ºC.  Weight loss method was employed in absence and presence of the inhibitor as an adsorption type in concentration range 1000 – 5000 ppm using rotating cylinder specimens. The experimental results showed that corrosion rate in absence and presence of inhibitor is increased with increasing temperature, rotational velocity and concentration of acid. It is decreased with increasing inhibitor concentration for the whole range of temperature, rotational velocity and concentrati

   Rotating cylinder electrode (RCE) is used . in weight loss technique , the salinity is 200000 p.p.m, temperatures are (30,5060,7080Co) . the velocity of (RCE) are (500,1500,3000 r.p.m). the water cut (30% , 50%). The corrosion rate of carbon steel increase with increasing rotating cylinder velocity. In single phase flow, an increase im rotational velocity from 500 to 1500 r.p.m, the corrosion rate increase from 6.88258 mm/y to 10.11563 mm/y respectively.

   In multiphase flow, an increase in (RCE) from 500 to 1500 r.p.m leads to increase in corrosion rate from 0.786153 to 0.910327 mm/y respectively. Increasing brine concentration leads to increase in corrosion rate at water cut 30%.

The corrosion behavior of carbon steel at different temperatures 100,120,140 and 160 Cͦ under different pressures 7,10 and 13 bar in pure distilled water and after adding three types of oxygen scavengers Hydroquinone, Ascorbic acid and Monoethanolamine in different concentrations 40,60 and 80 ppm has been investigated using weight loss method. The carbon steel specimens were immersed in water containing 8.2 ppm dissolved oxygen (DO) by using autoclave. It was found that corrosion behavior of carbon steel was greatly influenced by temperature with high pressure. The corrosion rate decreases, when adding any one of oxygen scavengers. The best results were obtained at a concentration of 80 ppm of each scavenger. It was observed that