The objectives of this paper was the development of a novel ligand, L, which was achieved in two stages: ligand is synthesised by reducing the result of the reaction between cyclohexane-1,2-diamine and 4-hydroxy-3,5-dimethoxycy clohexane-1-carbaldehyde, followed by the production of the 4,4’-((1E,1’E)-(1,2 phenylenebis(azanylylidene))bis(methanylylidene))bis(2,6-dimethoxyphenol) precursor (P). While studying corrosion inhibition (copper alloy) in acid solution by weight loss, compounds were characterised using 1H, 13CNMR (for ligand (L) and (P)), FT-IR and UV spectra, melting point, molar conductivity, %C, %H and %N, %M, and magnetic susceptibility. The complex’s octahedral structure is inferred from the bidentate coordination of the metal ion. The molar ratio of type [Pt(L)Cl2 (H2 O)2 ] seemed to be 1:1(M:L). Using the weight loss method, the corrosion inhibitory ef fects of the platinum complex on copper alloy in a nitric acid solution (0.5 M HNO3 ) were studied. Adsorption of inhibitor molecules onto the surface of the copper alloy was the primary mechanism by which corrosion activity was reduced and active sites were blocked. The results demonstrated that the efficacy of inhibition was improved with increasing inhibitor concentrations. The inhibitor had its maximum inhibitory effectiveness of 97.5% at a concentration of 700 ppm. Calculated values of the Gibbs free energy corroborated with the results of adsorption investigations, which showed that the process mostly included physical adsorption and Langmuir adsorption iso therm. The development of protective coatings was validated by scanning electron microscopy analyses of surface morphology.
In the ongoing series of our research, we prepared a new multifunctional azo-vanillin ligand (HL) and its Cu(II) complex to investigate their potential as versatile compounds for industrial/pharmaceutical purposes. Structural integrity was determined through spectroscopic analyses (FT-IR, NMR, Mass and UV-Vis), highlighting a distorted square planar geometry for the metal complex. The ligand was examined for its dyeing potential on wool and cotton with the latter showing better substantivity to cellulosic fibers and behaving as a good direct dye having excellent washing fastness. Furthermore, leveraging its surface-active properties, the ligand was tested as a green corrosion inhibitor for C-45 steel in a saline medium (3.5% NaCl) acr
... Show More
In this work, studying the effect of ethylenediamine as a corrosion inhibitor was investigated for carbon steel in aerated HCl solution in range of 0.1-1N under dynamic conditions, i.e., rotational velocity of 400–1200 rpm in the temperature range 35 – 65 ºC. Weight loss method was employed in absence and presence of the inhibitor as an adsorption type in concentration range 1000 – 5000 ppm using rotating cylinder specimens. The experimental results showed that corrosion rate in absence and presence of inhibitor is increased with increasing temperature, rotational velocity and concentration of acid. It is decreased with increasing inhibitor concentration for the whole range of temperature, rotational velocity and concentrati
... Show More
(5)
(4)
A new poly chain derivative of polyacrolein has been synthesized from the two basic precursors, polyacrolein and aromatic amine/substituted amine in chloroform to prepare poly Schiff base compounds (A1-A4). The novel poly subs.β-lactam derivative is obtained via coupling of poly schiff base with chloroacetyl chloride and trimethylamine (B1-B4). Newly synthesized compound was identified via spectral methods; their [13C-NMR, 1H-NMR, and FTIR] also measurement of some of its physical properties. Furthermore the inhibition effect of synthesized compounds (B1-B4) on the corrosion of stainless steel in 1N HCl was studied by wight loss method. The results of weight loss measurements showed that corrosion inhibition efficiency by increasing the co
... Show More
(3)
(3)
In current research Copper was employed for preparing a ternary system of Al–Si alloy in different (0.2–2.5 wt. %) the best was taken is (1.5%wt) of copper that circumstances of solidification for improving the mechanical performance of the available in aluminium alloy. Cast iron molds were prepared to obtain tensile strength testing specimens. Alloys were prepared by employing gas furnaces. The molten metal was poured into a preheated cast-iron mold. The obtained alloy structures were studied using an X-ray diffractometer and optical microscopy. The mechanical performance of the prepared alloys was examined under the influence of different hardening conditions in both heat and non-heat-treated conditions. The outcomes showed at the
... Show More
(2)
The inhibitive power of Polyvinyl Alcohol (PVA) was investigated toward the corrosion of carbon steel in 0.2N H2SO4 solution in the temperature range of 30-60˚C and PVA concentration range of 150-2000 ppm.
The corrosion rate was measured using both the weight loss and the electrochemical techniques. The weight loss results showed that PVA could serve as a corrosion inhibitor but its inhibition power was found to be low for the corrosion of carbon steel in the acidic media. Electrochemical analysis of the corrosion process of carbon steel in an electrochemical corrosion cell was investigated using 3-Electrode corrosion cell. Polarization technique was used for carbon steel corrosion in 0.2N H
The electrochemical behavior of Al-17%Si alloy is investigated in 3.5wt% NaCl solution. Many alloys with addition of the different wt% magnesium metal of 1wt%, 2%, 3wt% ,4.5wt% ,and 9wt% were prepared by gravity die casting . The microstructures of prepared alloys were examined by optical and SEM microscopes. Corrosion behavior was investigated by using potentiostat instrument under static potentials test and corrosion current was recorded to determine corrosion resistance of all prepared samples. It was found that the addition of Mg metal improves the corrosion resistance of Al-17%Si alloy in 3.5%NaCl solution. The alloy containing 1%Mg shows less corrosion rate than the others while the alloys containing 4.5%Mg, 9%Mg content have
... Show More
(2)
The corrosion behavior of low carbon steel in washing water of crude oil solution has been studied potentiostatically at five temperatures in the range (30–70)°C .The corrosion potential shifted to more negative values with increasing temperature and the corrosion current density increased with increasing temperature. Folic acid had on inhibiting effect on the corrosion of low carbon steel in washing water at a concentration (5× 10-4-- 5× 10-3 ) mol/dm3 over the temperature range (30–70)°C. Values of the protection efficiency were calculated from the corrosion current density .From the general results for this study, it can be seen that thermodynamic and kinetic function were also calculated (?G, ?S, ?H and Ea )
... Show More
(3)
In this study many specimen s were prepared from 2024-T3 Aluminum alloy for corrosion test by the dimensions of (15*15*3) mm according to ASTM G71-31 and then subjected to shot peening process at different time (15, 30, 45) minutes using steel ball having a diameter of 2.75 mm and Rockwell Hardness of 55RC to induce compressive residual stress which were measured using X-Ray diffraction method, surface roughness and hardness were tested before and after peening. Electrochemical corrosion test by Tafel extrapolation method was carried out in an environment of 3 .5% NaCl solutions (sea water) where Corrosion rate calculated using Tafle equation.
The obtained results show a favorable influence of SP treatment
... Show MoreIn this work, the copper metal was treated using Nd:YAG laser with energy 1Joul to enhance corrosion resistance and improve surface properties. The copper metal has many applications in industry as well as water, oil and gas pipes. The same conditions, (laser power density, scan speed, distance between paths, medium gas-air) were applied in the laser surface treatment, After laser treatment, the samples microstructures were investigated using optical microscope (OM) to examine micro structural changes due to laser irradiation. Specimen surfaces were investigated using atomic force microscopy (AFM), X-ray diffraction (XRD), macro hardness, and corrosion test before and after laser treatment to
... Show More
(6)