We studied the effect of certain environmental conditions for removing heavy metal elements from contaminated aqueous solutions (Cd, Cu, Pb, Fe, Zn, Ni, Cr) using the bacterium Bacillus subtilis to appoint the optimal conditions for removal ,The best optimum temperature range for two isolate was 30-35○C while the hydrogen number for the maximum mineral removal range was 6-7. The best primary mineral removal was 100 mg/L, while the maximum removal for all minerals was obtained after 6 hrs of Cu element time and the maximum removal efficiency was obtained after 24 hrs of Cu element. The results have proved that the best aeration for maximum removal was obtained at rotation speed of 150 rpm/minute. Inoculums of 5ml/100ml which contained 1

Electrocardiogram (ECG) is an important physiological signal for cardiac disease diagnosis. With the increasing use of modern electrocardiogram monitoring devices that generate vast amount of data requiring huge storage capacity. In order to decrease storage costs or make ECG signals suitable and ready for transmission through common communication channels, the ECG data
volume must be reduced. So an effective data compression method is required. This paper presents an efficient technique for the compression of ECG signals. In this technique, different transforms have been used to compress the ECG signals. At first, a 1-D ECG data was segmented and aligned to a 2-D data array, then 2-D mixed transform was implemented to compress the

Halobacterium saccharovorum was isolated from local highsalinity souls named Al-Massab Al-Aam. A growth curve was determined. The average generation time during logarith- mic phase was 17.80±0.62 hr. Bacteriorhodopsin was 1808 lated from the purple membrane, its concentration was 4.8 mg/ml and H.W was 26000. The pattern of other membrane Bpoteins was studied and compared with those of other Boletes. Several unique proteins were isolated and their molecular weights were determined.

Polymer matrix composites are suitable materials for medical applications, such as denture base resin polymethyl methacrylate (PMMA). This includes light weight and high strength. This paper describes the effect of selected weight fractions (1, 2, 3, 4 & 5) % wt of nano(Alumina AL2O3, Zirconia ZrO2, Hydroxyapatite HA and Halloysite nanoClay) reinforcements on the biopolymer matrix (PMMA). Some tribology tests were used to evaluate the prepared system (impact strength, hardness surface, and wear rate) tests. The samples were fabricated by (Hand Lay-Up) with different particle reinforcement percentages. All tests were accomplished at room temperature, and samples were developed according to the ASTM standard. The weight fraction of (4% for AL

Polymer matrix composites are suitable materials for medical applications, such as denture base resin polymethyl methacrylate (PMMA). This includes light weight and high strength. This paper describes the effect of selected weight fractions (1, 2, 3, 4 & 5) % wt of nano(Alumina AL2O3, Zirconia ZrO2, Hydroxyapatite HA and Halloysite nanoClay) reinforcements on the biopolymer matrix (PMMA). Some tribology tests were used to evaluate the prepared system (impact strength, hardness surface, and wear rate) tests. The samples were fabricated by (Hand Lay-Up) with different particle reinforcement percentages. All tests were accomplished at room temperature, and samples were developed according to the ASTM standard. The weight fraction o

This article reviews the construction of organic solar cell (OSC) and characterized their optical and electrical properties, where indium tin oxide (ITO) used as a transparent electrode, “Poly (3-hexylthiophene- 2,5-diyl) P3HT / Poly (9,9-dioctylfluorene-alt-benzothiadiazole) F8BT” as an active layer and “Poly(3,4-ethylenedioxythiophene)-poly (styrene sulfonate)” PEDOT: PSS which is referred to the hole transport layer. Spin coating technique was used to prepared polymers thin film layers under ambient atmosphere to make OSC.  The prepared samples were characterized after annealing process at (80 ͦ C) for (30 min) under non-isolated circumference. The results show a value of filling factor (FF) of (2.888), (0.233) and (0.28

3D‐printed scaffolds loaded with healing directed agents could be employed for better treatment outcome in regenerative dentistry. The aim of this study was to fabricate and characterize simple 3D‐printed poly lactic acid (PLA) scaffolds coated with nanoHydroxyapatite (nHA), Naringin (NAR), or their combination, and testing their morphological, chemical, mechanical, antibacterial, biocompatible and bioactive properties. Methodology: Two variants pore sizes, 300 and 700 μm, of 3D‐printed PLA disc scaffolds measuring (10 × 1 mm) were fabricated. These scaffolds were dip‐coated with nHA, NAR, or both (nHA/NAR). Field emission scanning electron microscopy (FeSEM), energy‐dispersive X‐ray spectroscopy (EDX), Fourier transfo

In this paper the process of metal ions extraction (Zn(II) and Cu(II)) was studied in PEG-KCl aqueous two phase system was investigated without using an extracting agent. The experimental runs were performance at constant temperature (25 ^oC), constant mixing time (30 min), and constant PH of the solution (about 3). The effect of KCl salt concentration (from 10% to 25%), volumetric phase ratio of PEG solution to KCl solution (from 0.5 to 2), and the initial metal ion concentration (from 0.25 ml to 2 ml of 1 gm/L solution) were investigated on the percent extraction of Zn(II) and Cu(II). The results indicated that the percent extraction of metal ions increase with increasing of salt concentration and phase ratio, and slightly de

A research include of synthesized five member ring, which has been synthesized by condensation of 2-(1-(4- hydroxyphenyl) ethylidene)hydrazine-1-carbothioamide[I] with α-chloro ethylacetate in sodium acetate (fused) to form ethyl 2-(4-(1-((4-oxo-2-thioxopyrrolidin-3-ylidene)hydrazono) ethyl)phenoxy)acetate [II]. After that reacted [II]with hydrazine hydrate to resulting compound [III]. Compound [III] was refluxed with 4-aminobenzoicacid in excess of phosphorus oxy chloride give compound [IV],the later compound [IV] interact with acetyl acetone or ethylacetoacetate give to pyrazole and pyrazoline derivatives[V],[VI]. While when reacted with different aromatic aldehydes and one ketone consistence Schiff base derivatives [VII]a-e . The FTIR a

A research include of synthesized five member ring, which has been synthesized by condensation of 2-(1-(4- hydroxyphenyl) ethylidene)hydrazine-1-carbothioamide[I] with α-chloro ethylacetate in sodium acetate (fused) to form ethyl 2-(4-(1-((4-oxo-2-thioxopyrrolidin-3-ylidene)hydrazono) ethyl)phenoxy)acetate [II]. After that reacted [II]with hydrazine hydrate to resulting compound [III]. Compound [III] was refluxed with 4-aminobenzoicacid in excess of phosphorus oxy chloride give compound [IV],the later compound [IV] interact with acetyl acetone or ethylacetoacetate give to pyrazole and pyrazoline derivatives[V],[VI]. While when reacted with different aromatic aldehydes and one ketone consistence Schiff base derivatives [VII]a-e . The FTIR a