Background: This study was formulated to compare the effect of 5%hydrofluoric acid in comparison to 37%phosphoric acid with and without the application of silane on bond strength of composite to porcelain. Materials and Methods: Specimen preparation was divided in to two phases, metal-disks fabrication (8mm-diameter and 4mm-thickness) and ceramic veneering. Thirty two specimens were prepared, sandblasted with 50 μm aluminum oxide, and divided into four groups of eight samples. Groups I and III were etched with 37%phosphoric acid while groups II and IV were etched with 5%hydrofluoric acid; and groups I and II were silaneted while groups III and IV were not. Heliobond, and resin composite were applied to each specimen using a plastic transpa

Background: The geriatric patients wearing removable partial dentures are increasing in proportion. At the same time, the root caries prevalence accompanied by gingival recession is increasing. A variety of vehicles can deliver fluoride into the oral cavity, including fluoride mouth-rinse, fluoride dentifrice, topical fluoride, and fluoride-releasing restorative materials, all of which effectively prevent root caries and suppress recurrent caries. This study aimed to evaluate the effect of sodium fluoride addition on some mechanical properties of heat cure acrylic denture base material. Material and method: A total of 90 samples were prepared in this study, then divided into three main groups according to the type of test used (hardness, te

Carnitine is a regulatory amino acid, necessary for the metabolism of long-chain fatty acids in the ß - oxidation, and it is important in the organization of the work of the blood brain barrier, and is very important in the treatment of infertility and sexual apathy. This study was conducted at the Poultry Farm of the Department of Animal Resource, College of Agriculture, University of Baghdad during the period from 15/2/2011 to 1/8/2011. The aim of this study was to investigate the effect of dietary supplementation with different levels of L - carnitin e on semen characteristics of guinea fowl male. A total of 24 guinea fowl male, 30 weeks of old were used in this study. Birds were randomly distributed into 4 groups (C0, C100, C200, C300)

Labrotary experiment was conducted to study the effect of different levels of nematode population densities of Meloidogyne spp on seed germination percentage and seedling characteristics of Vigna sinensis, Ahelmoschus esculentus, Cicer arietinum, Helianthus annuus and Rap-hanus sativus. Four different levels of nematode populat-ion densities ranged from 1 to 4 prepared from radish in-fected roots and used as inoculating agent to infect all seed types in the experiment Seed germination percentage of Vigna sinensis and Ablemoschus eseulentus were highly reduced (at 0.01 level of significance) with increased nematode population level from 1 to 4. Seedling length of the remaining seed types were significantly reduced (at 0.01 level of signif

Four local hemolysin producer bacterial isolates were selected, tow of them gram negative bacteria (Escherichia coli ,Pseudomonas aeruginosa ) and the other two were gram positive bacteria (Staphylococcus aureus , Bacillus cereus ). Minimum inhibitory concentration of the aqueous and alcoholic extracts of Punica granatum L. pericarp were determined towards the four bacterial isolates ,results obtaind showed that MICs of the aqueous extract were 200 mg/ml for E .coli and P. aeruginosa isolates while were 5 mg/ml and 2 mg/ml for B. cereus, S. aureus , respectively The MICs for the ethanolic extract were 50 mg/ml , 20 mg/ml ,1 mg/ml ,0.5 mg/ml for E. coli ,P. aeruginosa ,B. cereus ,S. aureus , respectively. The effect of Sub-MICs o

In this work, varying compositions of SiO₂ micro filler were added
with the Polyvinyl Chloride (PVC) and samples have been prepared
using film casting technique. The results have been analyzed and
compared for PVC samples with (1 wt%, 3 wt%, 5 wt% and 10 wt%)
SiO2 micro filler. Mechanical characteristics such as tensile strength,
elongation at break and Young`s modulus were measured for all the
samples, where the tensile strength was increased from 8.39 Mpa for
purified PVC to 16 Mpa for 3% SiO₂/PVC composite. Also, thermal
conductivity measurement values illustrated that composite materials
have a good thermal insulation at 10 wt. %, thermal conductivity was
decreased from 0.1684 W/m.

The study was conducted to identify the toxicity of chromium on scenedesmus quadricauda algae alone and in the presence of nutrient metal (Nitrogen). Different concentrations of chromium (0.5, 1.5 , 2.5, 3.5 , 4.5mg/L) were used and the presence nitrogen is (5 ,10 ,50 ,100mg/L) on cultur media(chu-10) with used for cultivation of the algae in controlled conditions(25oC , light intensity 380 –?E/m2 /s. The results showed increasing in the toxicity of the metal when is alone , excess of concentrations an time of exposure. The growth rate decreased from 0.44 to 0.06 cell/ hour after 12 day of the biging of the experiment and of concentrate 4.5 mg/L of chromium. The intermediate active concentrations of the chromium(EC50) was increase

In this study, the effect of Nd: YAG laser on the activity of superoxide dismutase (SOD) and alcoholdehydrogenase (ADH) was investigated. The Saccharomyces cells were irradiated using 532nm Q-Switched Nd: YAG laser with (1Hz) frequency. Different fluences 11.3, 22.6 and 33.9mJ/cm2 and different number of pulses 15, 30 and 60 pulse were used. The irradiated cells were incubated in a liquid nutritive medium for 24 hours. After incubation, the cells were harvested and disrupted to extract the intracellular enzymes and their activities were assessed. In comparison with the control, the irradiated cells showed a significant increase in the activity and the specific activity of SOD at energy densities of 11.3 and 22.6mJ/cm2 at 30 and 60 pulses

Background Microorganisms and fungal growth especially Candida albicans, on soft denture lining material are the most common problem which can lead to chronic mucosal inflammation. The aim of this study was to evaluate the effect of zirconium nanoparticles into acrylic-based heat cured soft denture lining material against Candida albicans, and the amount of zirconium ion release of soft liner/ZrNPs composite. Furthermore, evaluate shear bond strength after ZrNPs addition to soft liner. Materials and methods: Zirconium nanoparticles were added into acrylic-based soft denture liner in various percentages (1%, and 1.5% by weight). Two hundred and fifty specimens were arranged and isolated into four groups as per the test to be done The antifu

         The house flies Musca domestica )Diptera:musidae) are the primary carrier of many pathogens such as cholera, typhoid, anthrax, and others. The use of chemical pesticides as a basic method of control leads to many problems at the environmental and health level. The use of safe alternatives to chemical pesticides has become an urgent necessity. The research aims to find biological alternatives that are environment-friendly and non-pathogenic to humans in controlling house flies through the possibility of extracting and diagnosing some secondary metabolites produced by the fungus Metarhizium anisopliae and testing their effects on the second larval stage of house flies using different treatment methods that include