A novel series of chitosan derivatives were synthesized via reaction of chitosan with carbonyl compounds and grafted it’s by with different amine compounds substituted hydrogen. The produced polymers were characterized by different analyses FTIR, 1HCNMR, XRD, DSC and TGA. Solubility in water as well as many solvent was investigated, antibacterial activity of chitosan and its derivatives against two types of bacteria E. coli and S. aureus was also investigated. The results showed that derivatives sort of have antibacterial activities against Esherichia coli (Gram negative) better than chitosan whilst compound IX has better antibacterial against Staphylococcus aureus (Gram positive). SEM analysis showed that increase of surface roughness wi

One of the most important , compound which have active hydrogen is the compound possessing (thiol group) Biphenyl-4,4-dithiol is agood example utilized in a wide field for preparation mannich bases , avariety of new acetylenic mannich bases have been Synthesized and all proposed structure were Supported by FTIR , 1H – NMR, 13C-NMR , Elemental analysis and microbial study .

The work includes synthesis and characterization of some new heterocyclic compounds, as flow: The compound (3) (5-(4-chlorophenyl) -2-hydrazinyl-1,3,4-oxadiazole was synthesized by using two methods; the first method includes the direct reaction between hydrazine hydrate 80% and 5-(4-chlorophenyl)-2- (ethylthio) 1,3,4-oxadiazole (1), the second method involves converting 5-(4-chlorophenyl)-1,3,4-oxadiazol-2-amine (2) to diazonium salt then reducing this salt to compound (3) by stannous chloride. Compound (3) was used as starting material for synthesizing several fused heterocyclic compounds. The compound 6-(4- chlorophenyl)[1,2.4] triazolo [3,4,b][1,3,4] oxadiazole-3-(2H) thione (compound 4) was synthesized from the reaction of compo

A novel series of chitosan derivatives were synthesized via reaction of chitosan with carbonyl compounds and grafted it’s by with different amine compounds substituted hydrogen. The produced polymers were characterized by different analyses FTIR, 1HCNMR, XRD, DSC and TGA. Solubility in water as well as many solvent was investigated, antibacterial activity of chitosan and its derivatives against two types of bacteria E. coli and S. aureus was also investigated. The results showed that derivatives sort of have antibacterial activities against Esherichia coli (Gram negative) better than chitosan whilst compound IX has better antibacterial against Staphylococcus aureus (Gram positive). SEM analysis showed that increase of surface roughness wi

ABSTRACT Background: This study measured the effects of three parameters pH value, length of immersion and type of archwire on metal ions released from orthodontic appliances. Materials and Methods: Ninety maxillary halves simulated fixed orthodontic appliances that were immersed in artificial saliva of different pH values (6.75, 5 and 3.5) during 28 day period. Three types of archwires were used: stainless steel, nickel titanium and thermal activated nickel titanium. The quantity of nickel and chromium ions was determined with the use of atomic force spectrophotometer while iron ions by spectrophotometer. Each orthodontic set was weighted two times, before the ligation and immersion in the artificial saliva and after 28 days at the end of

Background: Studying and investigating the transverse strength(Ts), impact strength(Is), hardness (Hr) and surface roughness(Ra) of conventional and modified autopolymerizing acrylic resin with different weight percentages of biopolymer kraftlignin, after curing in different water temperatures; 40°C and 80°C. Material and Methods: Standard acrylic specimens were fabricated according to ADA specification No.12 for transverse strength, ISO 179 was used for impact testing, Shore D for hardness and profilometerfor surface roughness. The material lignin first dispersed in the monomer, then the powder PMMA is immediately added. Ligninadded in different weight percentages. Then cured using pressure pot (Ivomet) in two temperatures;40°C a

Electrophoretic Deposition (EPD) process offers various advantages like the fabrication of the ceramic coatings and bodies with dense packing, good sinterability and homogenous microstructure. The variables namely (applied potential, deposition time and sintering temperature) affected the development of hydroxyapatite (HAP) coatings. The coating weight and thickness were found to increase with the increase in applied potential or coating time. Sintering temperature was found to affect in change phases of the metal, furthermore the firing shrinkage of the HAP coating on a constraining metal substrate leads to serve cracking. XRD Characterization indicates the formation of a contamination free phase pure, and the optical micrographs show th