In this work, silicon nitride (Si₃N₄) thin films were deposited on metallic substrates (aluminium and titanium sheets) by the DC reactive sputtering technique using two different silicon targets (n-type and p-type Si wafers) as well as two Ar:N₂ gas mixing ratios (50:50 and 70:30). The electrical conductivity of the metallic (aluminium and titanium) substrates was measured before and after the deposition of silicon nitride thin films on both surfaces of the substrates. The results obtained from this work showed that the deposited films, in general, reduced the electrical conductivity of the substrates, and the thin films prepared from n-type silicon targets using a 50:50 mixing ratio and deposited on both

Titanium dioxide (TiO2) thin films were prepared under different pressures with values (15, 30, 60 and 120) Pa using the DC reactive magnetron homemade system with mixed gases of argon and oxygen in ratio (50:50). The result of X-ray diffraction patterns discovered that the structure of the deposited films was polycrystalline, including the phase of anatase. All the appeared peaks were matched to the planes (101), (004), (105), and (211) of diffracted states. Both the intensities and the number of the appeared peaks are declined according to the increased pressure, and the plane of (101) is be considered the preferential grown plane, it is taking a maximum texture factor. Both the lattice constant and the atomic inter-planer spacing take th

In this study, Al2O3 thin films were prepared by dc reactive sputtering technique using different gas mixtures of argon and oxygen gases (90:10, 70:30, 50:50, 30:70, and 10:90). These films were characterized to introduce their surface morphology and elemental composition as functions of the oxygen content in the gas mixture. The gas mixing ratio plays a crucial role in controlling the nanoscale morphology of the prepared thin films. The [Al]/[O] ratio varies non-linearly with the Ar:O2​ mixing ratio. Increasing the oxygen content leads to a progressive decrease in surface roughness, resulting in smoother and more uniform films with finer granular features. These results presented herein are useful to optimize the sputtering process to ac

 In this work, nanostructure aluminum oxide thin films were deposited on glass substrates using a direct current (DC) magnetic reactive sputtering (MRS) technique. A gaseous mixture of argon and oxygen at different mixing ratios was used to synthesize Al2O3 nanoparticles. After extracting Al2O3 powder from the glass substrate, X-ray diffraction (XRD), field-emission scanning electron microscopy (FE-SEM), and energy-dispersive spectroscopy (EDS) were used to analyze the structural and morphological properties of the synthesized thin films. The effect of deposition time on the spectral properties, as well as on the size of the nanoparticles, was determined.

Hybrid bilayer heterojunction Zinc Phthalocyanine (ZnPc) thin-film P-type is considered as a donor active layer as well as the Zinc Oxide (ZnO) thin film n-type is considered as an acceptor with (Electron Transport Layer). In this study, using the technique of Q-switching Nd-YAG Pulsed Laser Deposition (PLD) under vacuum condition 10-3 torr on two ITO (Indium Tin Oxide) and (AL) electrodes and aluminum, is used to construct the hydride bilayer photovoltaic solar cell heterojunction (PVSC). The electrical properties of hybrid heterojunction Al/ZnPc/ZnO/ITO thin film are studied. The results show that the voltage of open circuit (V_oc=0.567V), a short circuit (I_sc=36 ?A), and the fill factor (FF) of 0.443. In addition, the conversion