In this work, the effect of the addition of bright nickel plating and silver carried out by the electroplating method has been studied, on the coating of copper nanoparticles on the copper base metal via the process of thermal evaporation. The improvement of the solar absorber using CuNP in combination with the bright nickel and silver was obtained to be better than copper nanoparticles individually. A bright nickel enhanced the absorbed thermal stability. Also, other optical properties, absorptions, and emissivity slightly decreased from (93% to 87%), while the existence of silver had a slight impact on absorption of about (86.50%). On the other hand, thermal conductivity was evaluated using hot disk analyzer. The results showed a good

Abstract. In this work, Bi2O3 was deposited as a thin film of different thickness (400, 500, and 600 ±20 nm) by using thermal oxidation at 573 K with ambient oxygen of evaporated bismuth (Bi) thin films in a vacuum on glass substrate and on Si wafer to produce n-Bi2O3/p-Si heterojunction. The effect of thickness on the structural, electrical, surface and optical properties of Bi2O3 thin films was studied. XRD analysis reveals that all the as deposited Bi2O3 films show polycrystalline tetragonal structure, with preferential orientation in the (201) direction, without any change in structure due to increase of film thickness. AFM and SEM images are used to investigate the influences of film thickness on surface properties. The optical measur

This work is divided into two parts first part study electronic structure and vibration properties of the Iobenguane material that is used in CT scan imaging. Iobenguane, or MIBG, is an aralkylguanidine analog of the adrenergic neurotransmitter norepinephrine and a radiopharmaceutical. It acts as a blocking agent for adrenergic neurons. When radiolabeled, it can be used in nuclear medicinal diagnostic techniques as well as in neuroendocrine antineoplastic treatments. The aim of this work is to provide general information about Iobenguane that can be used to obtain results to diagnose the diseases. The second part study image processing techniques, the CT scan image is transformed to frequency domain using the LWT. Two methods of contrast

Background The traditional management of appendicular mass is an initial conservative treatment followed by interval appendectomy. Recently interval appendicectomy has been questioned.
Objective: The purpose of this study was to clarify the need and the role of interval appendicectomy after successful initial conservative treatment.
Method: This is a prospective study conducted in a major hospital in Basra from April 2006 to Septemper2010, included 65 patients with appendicular mass which subsequently proved postinflammmatory (phlegmonous) changes of the appendix were treated conservatively.
Results: Routine interval appendicectomy was not performed and needed after successful treatment in the majority of the patients (84.6%). F

Bacterial water pollution is a genuine general wellbeing concern since it causes various maladies. Antimicrobial nanofibers can be integrated by incorporating nanobiocides, for example, silver nanoparticles into nanofibers. Nylon 6 was dissolved in formic acid at a concentration of (25 wt. %) and tough antibacterial (AgNO₃/Nylon) nanofibers were produced utilizing electrospinning system. Polymer solution was tested before accomplishing electrospinning process to acquire its surface tension, electric conductivity and viscosity, where every one of those parameters increased relatively with increasing concentration of (AgNO₃) additions. SEM and EDX spectra were utilized to focus on the morphology, surface elemental mem

The present work reports a direct experimental comparison of the catalytic hydrodesulfurization of
thiophene over Co-Mo/Al2O3 in fixed- and fluidized-bed reactors under the same conditions. An
experimental pilot plant scale was constructed in the laboratories of chemical engineering department,
Baghdad University; fixed-bed unit (2.54 cm diameter, and 60cm length) and fluidized-bed unit (diameter of 2.54 cm and 40 cm long with a separation zone of 30 cm long and 12.7 cm diameter). The affecting
variables studied in the two systems were reaction temperature of (308 – 460) oC, Liquid hourly space
velocity of (2 – 5) hr-1, and catalyst particle size of (0.075-0.5) mm. It was found in both operations that the
conversion

Nitrogen heterocycles are of a special interest because they constitute an important class of natural and non natural products, many of which exhibit useful biological activities.Among these nitrogen heterocycles are 1, 3, 4-thiadiazole containing compounds. The therapeutic effects of these derivatives have been well studied for a number of pathological conditions including inflammation, pain, or hypertension. Moreover, synthesis of thiadiazoles has attracted wide-spread attention due to their diverse applications as antibacterial, anticancer, antifungal anti-inflammatory and antidepressant agents.According to this information’s new derivatives of 1, 3, 4-thiadiazole were designed and synthesized and in the hope of having some act

The fabrication of Solid and Hollow silver nanoparticles (Ag NPs) has been achieved and their characterization was performed using transmission electron microscopy (TEM), zeta potential, UV–VIS spectroscopy, and X-ray diffraction (XRD). A TEM image revealed a quasispherical form for both Solid and Hollow Ag NPs. The measurement of surface charge revealed that although Hollow Ag NPs have a zeta potential of -43 mV, Solid Ag NPs have a zeta potential of -33 mV. According to UV-VIS spectroscopy measurement Solid and Hollow Ag NPs both showed absorption peaks at wavelengths of 436 nm and 412 nm, respectively. XRD pattern demonstrates that the samples' crystal structure is cubic, similar to that of the bulk materials, with

In this work, chemical spray pyrolysis deposition (CSP) technique was used to prepare a mixed In2O3-CdO thin films with different CdO content (10, 30 and 50)%volume ratio on glass substrates at 150 ᵒC substrate temperature. The surface morphology and structural properties were measured to find the optimum conditions to improve thin films properties for using as photo detector. Current –Time, the sensitivity and response speed vary for each mixture. Samples with 10% vol. CdO content has square pulse response with average rise time nearly 1s and fall time 1s.

Proteinases (E.C.3.4.21) family are widely distributed in the nature; it was present in animals tissues , plants and microbial cell . Protease was purified from Zahdi seed (Phoenix dactylifera L.) by several steps included ammonium sulphite ppt (75%) saturation and dialyzed against the 80mM sodium phosphate buffer at pH 7.5 . The enzyme specific activity was 407.62 unit/mg protein. The obtained extract was purified by DEAE-Cellulose column followed by gel filtration through Sephacyl S-200 column .The enzyme specific activity ,yield and purification fold were 1873.49 unit/mg protein, 22.99 and 58.42% respectively. The results of protease characterization showed that the molecular weight was 25118 daltons as determined by gel f