The synthesis of zeolite NaX from locally available kaolin has been studied. The operating conditions for zeolite NaX production from kaolin with good crystallinity were as follows; a gel formation step of metakaolin in alkaline medium in presence of additional silica to crystallize the zeolite was achieved at 60 oC for 1 hr,and with stirring. In ageing step of the reactants at room temperature for 5 days and crystallization step at 87±2 oC for 24 hr. The catalytic activity of catalyst prepared from local kaolin was studied by using cumene cracking as a model for catalytic cracking and compared with standard HY zeolite and HX zeolite catalysts. The activity test was carried out in a laboratory continuous flow unit with fixed bed re

The aim of this study is to evaluating the antibacterial activity of Laurus nobilis leaves extract in hospital environment isolates. Maceration and Soxhlet apparatus were used to prepare aqueous and methanolic extracts. The total phenolic content and high-performance liquid chromatography (HPLC) were conducted to determine the active compounds in the extracts. The results showed that the methanolic and aqueous extracts contain four flavonoids derivatives (kaempferol, luteolin, quercetin and Rutin) were identified on the basis of matching retention time with the standards. The total phenolic contents were 56.81 and 81.56 mg/g in 50 mg/ml, in aqueous and methanolic extracts respectively. The antibacterial activity of Laurus nobilis leaves ext

In the current study, three types of algae namely Tetradesmus nygaardi (MZ801740), Scenedesmus quadricauda (MZ801741) and Coelastrella sp (MZ801742) were extracted by 95% ethanol and hexane against two types of gram positive and two types of gram negative bacteria by wells diffusion methods. Eleven concentrations from the extract of algae (2, 5, 10, 15, 20, 25, 30, 35, 40, 45 and 50 mg/ml) were utilized. It was noticed that ethanolic extraction was more effective than hexane in Scenedesmus quadricauda than the two other mentioned algal species against all pathogenic bacteria, Acintobacter baumanii (ATCC: 19606), Klebsiella pneumonia (ATCC: 13883) Enterococcus faecalis (ATCC: 29212) and Staphylococc

The synthesis of zeolite NaX from locally available kaolin has been studied. The operating conditions for zeolite NaX production from kaolin with good crystallinity were as follows; a gel formation step of metakaolin in alkaline medium in presence of additional silica to crystallize the zeolite was achieved at 60 oC for 1 hr,and with stirring. In ageing step of the reactants at room temperature for 5 days and crystallization step at 87±2 oC for 24 hr. The catalytic activity of catalyst prepared from local kaolin was studied by using cumene cracking as a model for catalytic cracking and compared with standard HY zeolite and HX zeolite catalysts. The activity test was carried out in a laboratory continuous flow unit with fixed bed reactor

In this work, zinc oxide nanoparticles (ZnONPs) and sawdust/epoxy composite (20:80) were mixed using a simple molding method with different ZnONPs concentrations of (0.1, 0.3, 0.5, 0.7, and 1.0 %). The samples of the nanocomposites were characterized by the Scanning Electron Microscopy (SEM) technique to demonstrate the homogeneity of the prepared ZnONPs/nanocomposites. The photocatalytic activity of the samples was examined using the methylene blue (MB) dye as a pollutant solution, through evaluation of the efficiency of the prepared compound in the treatment of organic pollutants under illumination by sunlight. The photocatalytic results showed that after 240 minutes of exposure to sunlight, the sample prepared using (0.5 vol.% of ZnON