Background: Calcium hydroxide and calcium-silicate materials used as direct pulp capping materials. The aims of this in vitro study is to compare among these materials in, the calcium ion release and pH change in soaking water after immersion of materials’ specimens in deionized water. Also Solubility and water sorption of materials’ specimens measured after soaking time. Calcium-silicate materials used were Biodentine, TheraCal and MTA Plus. Materials and methods: Four materials used in this study; Urbical lining (as control group), Biodentine, TheraCal and MTA Plus. Ten discs fabricated from each tested material, by using plastic moulds of 9 mm diameter and 1 mm thickness. Each specimen was immersed in 10 ml of d

Background: One of the major problems in endodontics is micro-leakage of root canal fillings which might contribute to the failure of endodontic treatment. To avoid this problem, a variety of sealers have been tested. The objective of this, in vitro, study was to evaluate the shear bond strength of four resin based sealers (AH plus, silver free AH26, RealSeal SE and Perma Evolution permanent root canal filling material) to dentin. Materials and Methods: Forty non-carious extracted lower premolars were used. The 2mm of the occlusal surfaces of teeth were sectioned, to expose the dentin surface. The exposed dentin surfaces of teeth were washed with 5ml of 2.5% NaOCl solution followed by 5ml of 17 % EDTA then rinsed by deionized water to remov

The role of the green areas lies in being one of the systems that plays the vital role in achieving the environmental dimension besides the socio-cultural body and the economic dimension in the hidden value of ecosystem services. However, many developing countries are characterized by a state of low community environmental awareness, which coincides with the basic need for land for housing and other uses, to take precedence over nature protection strategies. In the absence of clear planning and long-term planning strategies, all this led to abuses and violations of urban land use. In Iraq, the situation became more apparent due to the political, security and social conditions that followed the year 2003. Hence, the resea

Objectives: This study aims to evaluate the role of social media in promoting awareness of green university initiatives and assess the effectiveness of sustainability reports in engaging students at Baghdad University. In alignment with Sustainable Development Goal 12 (Responsible Consumption and Production),It seeks to provide recommendations for enhancing digital platforms for sustainability communication.   Theoretical Framework: The study is grounded in the Green University Model, Social Media Engagement Theory, and the Sustainability Reporting Framework, which emphasize integrating sustainable practices in education, using digital platforms for community engagement, and leveraging sustainability reports for transparency and

The Corrosion protection effectiveness of Alimina(Al2O3,50nm)and Zinc oxide (ZnO,30nm) nanoparticales were studied on carbon steel and 316 stainless steel alloys in saline water (3.5%NaCl)at four temperatures: (20,30,40,50 OC)using three electrodes potentiostat. An average corrosion protection efficiencies of 65 %and 80% was achieved using Al2O3 NP's on carbon steel and stainless steel samples respectively, and it seems that no effect of rising temperature on the performances of the coated layers. While ZnO NP'S showed protection efficiency around 65% for the two alloys and little effected by temperature rising on the performanes of the coated layers. The morphology of the coated spesiemses was examined by Atomic force microscope.

This study focused on extracting the outer membrane nanovesicles (OMVs) from Escherichia coli BE2 (EC- OMVs) by ultracentrifugation, and the yield was 2.3mg/ml. This was followed by purification with gel filtration chromatography using Sephadex G-150, which was 2mg/ml. The morphology and size of purified EC-OMVs were confirmed by transmission electron microscopy (TEM) at 40-200 nm. The nature of functional groups in the vesicle vesicle was determined by Fourier transforms infrared spectroscopy (FT-IR) analysis. The antitumor activity of EC-OMVs was conducted in vitro by MTT assay in human ovarian (OV33) cancer cell line at 24,48 and 96hrs. The cytotoxicity test showed high susceptibility to the vesicles in ovarian compared to normal

The cost-effective carbon cross-linked Y zeolite nanocrystals composite (NYC) was prepared using an eco-friendly substrate prepared from bio-waste and organic adhesive at intermediate conditions. The green synthesis method dependent in this study assures using chemically harmless compounds to ensure homogeneous distribution of zeolite over porous carbon. The greenly prepared cross-linked composite was extensively characterized using Fourier transform infrared, nitrogen adsorption/desorption, Field emission scanning electron microscope, Dispersive analysis by X-ray, Thermogravimetric analysis, and X-ray diffraction. NYC had a surface area of 176.44 m2/g, and a pore volume of 0.0573 cm3/g. NYC had a multi-function nature, sustained at a long-

Background: To investigate the effect of different types of storage media on enamel surface microstructure of avulsed teeth by using atomic force microscope.Materials and methods : Twelve teeth blocks from freshly extracted premolars for orthodontic treatment were selected . The study samples were divided into three groups according to type of storage media :A-egg white , B- probiotic yogurt , and C-bovine milk . All the samples were examined for changes in surface roughness and surface granularity distribution  using atomic force microscope, at two periods: baseline, and after 8 hours of immersing in the three types of storage media. Results: Milk group had showed a significant increase in the mean of the  roughness values at

Background: Cleaning and shaping of root canals successfully requires high volumes of irrigation solutions that can only be applied to the apical third of root canal after enlargement with instrument, so the aim of this study was to evaluate and to compare the efficiency of Maxi-I-probe (side-vented needle), in the amount of root canal irrigant penetration for five different master apical file sizes (MAF) and four different degrees of coronal and middle thirds flaring. Materials and Methods: Two hundred resin blocks with simulated root canals were used in this study and divided into 5 major groups (40 for each) based on the size of master apical files (#20, #25, #30, #35, and #40). Each major group was subdivided into 4 subgroups depending