Coblatcomplex has been prepared by reaction between C16H19N3O3S (L) as ligand and metal salt (II). The prepared complex were characterized by infrared spectra, electromic spectra, magnetic susceptibility, molar conductivity measurement and metal analysis by atomic absorption and (C.H.N) analysis. From these studies tetrahedral geometry structure for the complex was suggested. The photodegredation of complex were study using photoreaction cell and preparednanoTiO2 catalyst in different conditions (concentration, temperatures, pH).The results show that the recation is of a first order with activation energy equal to (6.6512 kJ /mol).

Herein, a biocomposite of crosslinked chitosan polyethylene glycol diglycidyl ether (CS-PEDGE), montmorillonite (MMT), and foodgrade algae (FGA) was successfully prepared by a hydrothermal technique. The resulting absorbent (CS-PEDGE/FGA/MMT) was assessed for its adsorption property with methyl violet 2B (MV 2B) a toxic cationic dye. The physicochemical properties of CS-EDGE/ FGA/MMT were assessed via various analytical techniques, including BET, Elemental analysis, pHpzc, and spectroscopy (FTIR, XRD, SEM-EDX). The influence of three adsorption variables, namely adsorbent dose (A: 0.02–0.1 g/100 mL), solution pH (B: 4–10), and contact time (C: 10–420 min) on the rate of MV 2B dye removal was examined using the Box-Behnken design (RSM-

SnS has been widely used in photoelectric devices due to its special band gap of 1.2-1.5 eV. Here, we reported on the fabrication of SnS nanosheets and the effect of synthesis condition together with heat treatment on its physical properties. The obtained band gap of the SnS nanosheets is in the rage of 1.37-1.41 eV. It was found that the photo-current density of a thin film comprised of SnS nanosheets could be enhanced significantly by annealing treatment. The maximum photo-current density of the stack structure of FTO/SnS/CdS/Pt was high as 389.5 mu A cm(-2), rendering its potential application in high efficiency solar hydrogen production.

A random laser is a non-conventional laser whose feedback mechanism is based on dissorder-induced light. However, random lasers occur in gain media with numerous scatterers and produce coherent laser emission without any predesigned cavity. The generation of coherent emission from multiple scattering is quite general and its basic principles are shown here using sulforhodamine B-TiO suspensions system. These suspensions were pumped with 337.1 nm pulses from N2 laser and the spectral and temporal behavior of light emitted from the pumped surface was recorded. When we pump power above a certain threshold a dramatic narrowing of the emission line width and a shortening of the emitted pulses were observed. We have experimentally found that i

Various Hall Effects have been successfully observed in samples of n-type indium antimonide with values for conductivity, energy gap, Hall mobility and Hall coefficient all agreeing with theory. A particular interest in developing a method for obtaining accurate values of carrier concentrations in semiconductor samples has been fulfilled with an experimental result of (1.6×1016 cm-3 ±10.7%) giving a percentage difference of (6.7%) to a quoted value of (1.5×1016cm-3) at (77K) using an (80mW C.W. CO2) laser beam at (10.6μm) to illuminate a similar sample of n-type indium antimonide, an "Optical" Hall effect has been observed. Although some doubt has been raised as to the validity of effect i.e. "thermal" rather than "Optical", values o

In this article, the detailed information was presented about azo-dyes, including a general description of this class of compounds, which included a historical overview, observations on the chemical structure of these compounds, particularly focusing on the azo group (-N=N-) responsible for their coloring properties. In addition, we provided a schematic of the first synthesized azo-compound. Furthermore, we mentioned the general properties of them and viewed a detailed explanation for the categorization of them either aliphatic or aromatic, subdivisions for each category or which category is the most widespread, and then illustrated the types for this class of organic compounds. The effective operator in these compounds called diazonium-sal

In this research, titanium dioxide nanoparticles (TiO₂ NPs) were prepared through the sol-gel process at an acidic medium (pH3).TiO₂ nanoparticles were prepared from titanium trichloride (TiCl₃) as a precursor with Ammonium hydroxide (NH₄OH) with 1:3 ratio at 50 °C. The resulting gel was dried at 70 °C to obtain the Nanocrystalline powder. The powder from the drying process was treated thermally at temperatures 500 °C and 700 °C. The crystalline structure, surface morphology, and particle size were studied by using X-ray diffraction (XRD), Atomic Force Microscopy (AFM), and Scanning Electron Microscope (SEM). The results showed (anatase) phase of titanium dioxide with the average grain size

Production of fatty acid esters (biodiesel) from oleic acid and 2-ethylhexanol using sulfated zirconia as solid catalyst for the production of biodiesel was investigated in this work.

       The parameters studied were temperature of reaction (100 to 130°C), molar ratio of alcohol to free fatty acid (1:1 to 3:1), concentration of catalyst (0.5 to 3%wt), mixing speed (500 to 900 rpm) and types of sulfated zirconia (i.e modified, commercial, prepared  catalyst according to literature and reused catalyst). The results show the best conversion to biodiesel was 97.74% at conditions of 130°C, 3:1, 2wt% and 650 rpm using modified catalyst respectively. Also, modified c