Cu-Al-Ni shape memory alloy specimens has been fabricated using powder metallurgy technique with tube furnace and vacuum sintering environment , three range of Nb powder weight percentage (0.3,0.6,0.9)% has been added. Micro hardness and sliding wear resist has been tested followed by X-ray diffraction, scanning electron microscope (SEM) and energy dispersive X-ray spectroscope (EDX) for micro structure observation. The experimental test for the samples has showed that the increase of Nb powder weight percentage in the master alloy has a significant effect on increasing the hardness and decreasing the wear resist therefore it will enhance the mechanical properties for this alloy.

The technical of Flame Thermal Spray had been used in producing a cermet
composite based on powders of stabilized zirconium oxide containing amount of
Yatteria oxide (ZrO2- 8Y2O3) reiforced by minerals powders of bonding material
(Ni-Cr- Al- Y) in different rates of additions (25, 35, 50) on stainless steel base type
(304) after preparing it by the way of Grit Blasting.
Before heat treatment, the coated cermet layers were characterized for porosity
and electric resistivity. All samples were heat treated in vacuum furnace at different
temperature and times. The physical tests had been operated after heat treatment
and gave best results especially porosity, which found to be reduced dramatically
and producing hig

In this work; copper oxide films (CuO) were fabricated by PLD. The films were analyzed by UV-VIS absorption spectra and their thickness by using profilometer. Pulsed Nd:YAG laser was used for prepared CuO thin films under O₂ gas environment with varying both pulse energy and annealing temperature. The optical properties of   as-grown film such as optical transmittance spectrum, refractive index and energy gap has been measured experimentally and the effects of laser pulse energy  and annealing temperature on it were studied. An inverse relationship between energy gap and both annealing temperature and pulse energy was observed.

In diabetes, impaired wound healing and other tissue abnormalities are considered major concerns. Many factorsaffect the time and quality of wound healing. One of the purposes of medical sciences is wound healing in a short time withreduced side effects. The herbal products are more precious in both prophylaxis as well as curative in delayed diabetic woundhealing activity when compared to synthetic drugs.A wide range of evidence has shown that capers plant possesses differentbiological effects, including antioxidant, anticancer and antibacterial effects. Phytochemical analysis shows thatC. spinosahashigh quantities of bioactive constituents, including polyphenolic compounds, which are responsible for its health-promotingeffects. The healing

Background: Low-level laser therapy (LLLT) has been extensively applied to improve wound healing due to some biostimulatory properties presented by laser arrays apparently able to accelerate the repair of soft tissue injuries. However, the role of proinflammatory interlukines not been studied yet. IL_1 ? represent one of the most important poroinflammatory interlukines that involved in wound healing. The goal of this study was to investigate the effect of 790-805nm diode laser on the expression of IL_1 ? during wound healing in mice. Materials and Methods: Standard-sized wounds (1.5cm) were carried out in the face of 96 white albino mice. Half of them underwent LLLT treatment (360 J/cm 2) at 790-805 nm delivered immediately after wound pro

Advancements in horizontal drilling technologies are utilized to develop unconventional resources, where reservoir temperatures and pressures are very high. However, the flocculation of bentonite in traditional fluids at high temperature and high pressure (HTHP) environments can lower cuttings transportation efficiency and even result in problems such as stuck pipe, decreased rate of penetration (ROP), accelerated bit wear, high torque, and drag on the drill string, and formation damage. The major purpose of the present research is to investigate the performance of low bentonite content water-based fluids for the hole cleaning operation in horizontal drilling processes. Low bentonite content water-based drilling fluids were formulated by re

This study was conducted in Al-Salam station for Dairy cattle/private sector, for the period from 1-11-2016 to 1-11-2017, to determine the association between BTN1A1 gene polymorphism and reproductive efficiency indicator and heat tolerance in 50 Holstein cows. The results of BTN1A1 gene analysis showed a highly significant Different (P<0.01) between genotypes of BTN1A1 gene’s genotypes AA, AB the percentage were 72.00, 28.00 % respectively. Results showed that services per conception and days open was significantly (P<0.05) affected by polymorphism of BTN1A1 gene and for cows with AA genotype, there was also a significant difference (P<0.05) between the genotypes of BTN1A1 gene for IgG concentration in calves blood who belong to mother