In the present work, asphaltenes and resins separated from emulsion samples collected from two Iraqi oil wells, Nafut Kana (Nk) and Basrah were used to study the emulsion stability. The effect of oil resins to asphaltene (R/A) ratio, pH of the aqueous phase, addition of paraffinic solvent (n-heptane), aromatic solvent (toluene), and blend of both (heptol) in various proportions on the stability of emulsions had been investigated. The conditions of experiments were specified as an agitation speed of 1000 rpm for 30 minutes, heating at 50 °C, and water content of 30%.  The results showed that as the R/A ratio increases, the emulsion will be unstable and the amount of water separated from emulsion increases. It was noticed that the em

Nano gamma alumina was prepared by double hydrolysis process using aluminum nitrate nano hydrate and sodium aluminate as an aluminum source, hydroxyle poly acid and CTAB (cetyltrimethylammonium bromide) as templates. Different crystallization temperatures (120, 140, 160, and 180) ⁰C and calcinations temperatures (500, 550, 600, and 650) ⁰C were applied. All the batches were prepared at PH equals to 9. XRD diffraction technique and infrared Fourier transform spectroscopy were used to investigate the phase formation and the optical properties of the nano gamma alumina. N₂ adsorption-desorption (BET) was used to measure the surface area and pore volume of the prepared nano alumina, the particle size and the

Faujasite type NaY zeolite catalyst was prepared from locally available kaolin, then the prepared NaY zeolite have been modified by exchanging of sodium ion with ammonium to produce NH4Y zeolite. NH4Y zeolite was converted to HY zeolite by ion exchanging with oxalic acid. Zinc and nickel promoters have been added to the prepared HY zeolite catalyst, and the effect of these promoters on the catalytic activity of the prepared HY catalyst was studied in fluid catalytic cracking process using light gas oil as a feedstock. The experimental results show that the promoted catalyst gives higher gas oil conversion and gasoline yield than HY zeolite catalyst at the same reaction temperature and WHSV. It was also found that the promoted catalyst gi

The aim of this research is to find out the influence of Daniel's model on the skills of the twenty-first century among the students of the scientific-fifth grade at the secondary and preparatory government morning schools for the academic year 2022- 2023. Two groups were chosen out of five groups for the fifth-scientific grade, one of which represents the experimental group that is taught by the Daniel model, and the other is the control group that is taught in the traditional method. The equivalence of the two research groups was verified with a set of variables. As for the research tool, a scale was developed by the researchers for the skills of the twenty-first century, in which they adopted the framework of the Partnership Organizat

The performance of photovoltaic (PV) panel having staggered metal foam fins was examined experimentally in Baghdad, Iraq. Three staggered metal foam fin configurations attached to the backside of the PV panel were studied. The measured parameters were front and back surfaces temperature, open voltage and current circuits, maximum power, and PV efficiency. It was noted that the maximum electrical efficiency enhancement was 4.7% for staggered metal foam fins (case III) than the reference PV panel. The operating temperature of the cell was increased when the value of solar intensity was high. Thereby, the electrical efficiency was decreased. It was found that the metal foam fins decreased the PV temperature by 2-3 ^o

to study the discribrion and the pollution in the environment in the south of baghdad samples of waste water from industrail units using the mercury in its process also

Abstract

The current research aims to identify the typical effect of Flower and Coscroft on expressive performance and the development of lateral thinking among literary fifth-grade students. To achieve the research objective, the researcher chose a sample of (90) female students from the fifth literary grade, with two experimental groups and a control group. The research groups are of six subjects. The research found that the two experimental groups have more expressive performance than the control group. Students of the first experimental group outperformed the students of the second experimental group in expressive performance and lateral thinking tests. In light of the findings of the research, the researcher

Objective: The aim of this study was to evaluate the effect of pumice, burning investment material
and black sand on the surface roughness of heat cure acrylic resin.
Methodology: Sixty specimens were prepared from pink heat cure acrylic resin, the specimens
where grouped into; 20 specimens which polished with pumice and water (control group); 20
specimens which polished with investment material (after burning it) and water; and 20 specimens
which polished with black sand and water. The average surface roughness of specimens after
polishing procedure had been determined by profilometer (surface roughness tester).
Results: Through the application of ANOVA and LSD tests, the result of this study showed that there