Glass Ionomer Cement (GIC) is one of the important dental temporary filing materials. The aim of this study is to evaluate the effect of adding 3, 5 and 7 wt. % of TiO₂ microparticles to conventional GIC powder (Riva Self Cure) on mechanical properties and its effect on absorption and solubility processes. TiO₂ particles additives improved compressive strength and biaxial flexural strength, where the compressive strength increased with increasing in the added ratio, while the highest value of the biaxial flexural strength was at 3 wt.%. The addition of TiO₂ particles improved the surface Vickers microhardness values, with highest value at 5 wt. %. On other hand TiO₂ addition im

This study included the preparation of the mixture aquatic extracts of Peganum harmala seeds and Pericarp of Punica granutum at concentration (10+50) ?(15+55)? (20+60) mgml .To study the influence of the mixture on the percentage of vitality of the protoscolices of E. granulosus In vitro, as the vitality of protoscolices had caused complete death when the using concentration at time 120,90,60 minute respectively. Also study the effect of mixture in white mice with infectious protoscolices In vivo and study the change occurred in the averages of the weights of the liver and spleen and the averages of its distension In vivo in processed group with mixture at concentration (15+55) , (10+50)mgml ,as which was approach to the negative gro

Background:The demand for esthetic orthodontic appliances is increasing so that the esthetic orthodontic archwires were introduced. This in vitro study was designed to evaluate the surface roughness offiber-reinforced polymer composite (FRPC) archwires compared to coated nickel-titanium (NiTi) archwires immersed in artificial saliva. Materials and Methods:Three types of esthetic orthodontic archwires were used: FRPC (Dentaurum), Teflon coated NiTi (Dentaurum) and epoxy coated NiTi (Orthotechnology). They were round (0.018 inch) in cross section and cut into pieces of 15 mm in length.Forty pieces from each type were divided into four groups; one group was left at a dry condition and the other three groups were immersed in artificial saliva (

The study was conducted in the poultry field of the Department of Animal Production/ College of Agricultural Engineering Sciences/ University of Baghdad/ Abu Ghraib, for the period from 28/04/2022 to 08/06/2022 to demonstrate the effect of adding a mixture of Lion’s mane Hericium erinaceus and Reishi Mushroom Ganoderma lucidum to broiler's diets on productive performance, 120 one day old Ross 308 breed broiler chicks were used in the experiment, with (10 birds / replicate) with an average starting weight of 49.95 g. The experiment treatments were as follows:(T1) basic diet control treatment free of any addition. (T2) the basic diet with the addition of 0.5 g/kg fodder of Lion's Mane mushroom with 0.5 g/kg fodder of the Reishi Mus

Zinc Oxide thin film of 2 μm thickness has been grown on glass substrate by pulsed laser deposition technique at substrate temperature of 500 oC under the vacuum pressure of 8×10-2 mbar. The optical properties concerning the absorption, and transmission spectra were studied for the prepared thin film. From the transmission spectra, the optical gap and linear refractive index of the ZnO thin film was determined. The structure of the ZnO thin film was tested with X-Ray diffraction and it was formed to be a polycrystalline with many peaks.

In this research an experimental study has done for testing the thermal performance of selective surfaces used in solar collectors for substrate of iron, galvanized iron and aluminum which are commercially available. The coating process for the samples has done in two ways, the electroplating and the chemical spray pyrolysis. The results of the thermal performance test of these samples are comparing with the thermal performance of a sample without paint and other paint with black paint without shines commercially available. For the electroplated samples, the performance study has done for different immersion time in plating bath, the
distance between electrical poles, the current density, and area ratio of the sample plated area to

The synthesis and bioactivity of zinc oxide nanoparticles has been extensively studied. The antibacterial activity of different antibiotics individually (ceftriaxone (C), chloramphenicol (CRO), penicillin (P) and amoxicillin (Ax)) and Zinc oxide nanoparticles (60μg/ml) in combination with the previously mentioned antibiotics has been demonstrated in the present study by using the disk diffusion assay method. The results showed a synergistic effect between Zinc oxide nanoparticles (ZnO NPs) and both Ax and P for most of the studied Gram-positive isolates (Staphylococcus aureus1, Staphylococcus aureus2, Staphylococcus epidermidis1, Staphylococcus epidermidis2, Enterococcus faecalis1, Enterococcus faecalis2 ) and between ZnO NPs and both C

This research studied the effect of magnetized water in concrete preparation and its effect on the presenting of cement in concrete mixtures also to find the ability of reducing the amount of cement in preparing one cubic meter, this is not exceed than 10% in one mixture , The experiments showed the preparation of standard cubes from the concrete which was used two kind of water magnetized water which was prepared by passing the tap water through the systems of different magnetic strength in terms of (6000,9000) Gauss and the ordinary water . The velocity of water through the magnetic field, which gives us the highest value for the compressive strength, was up to 1m/sec. to determine the best magnetic intensity, we examined The comp