Abstract: Reflection optical fibre Humidity sensor is presented in this work, which is based on no core fibre prepared by splicing a segment of no core fibre (NCF) at different lengths 1-6 cm with fixed diameter 125 µm and a single mode fibre (SMF). The range of humidity inside the chamber is controlled from 30% to 90% RH at temperature ~ 30 °С. The experimental result shows that the resonant wavelength dip shift decreases linearly with an increment of RH% and the sensitivity of the sensor increased linearly with an increasing in the length of NCF. However, a high sensitivity 716.07pm/RH% is obtained at length 5cm with good stability and reputability.  Furthermore, the sensor is shif

This work deals with thermal cracking of three samples of extract lubricating oil produced as a by-product from furfural extraction process of lubricating oil base stock in AL-Dura refinery. The thermal cracking processes were carried out at a temperature range of 325-400 ºC and atmospheric pressure by batch laboratory reactor. The distillation of cracking liquid products was achieved by general ASTM distillation (ASTM D -86) for separation of gasoline fraction up to 220 ºC from light cycle oil fraction above 220 ºC. The comparison between the conversions at different operating conditions of thermal cracking processes indicates that a high conversion was obtained at 375°C, according to gasoline production. According to gasoline produ

Stumpff functions are an infinite series that depends on the value of z. This value results from multiplying the reciprocal semi-major axis with a universal anomaly. The purpose from those functions is to calculate the variation of the universal parameter (variable) using Kepler's equation for different orbits. In this paper, each range for the reciprocal of the semi-major axis, universal anomaly, and z is calculated in order to study the behavior of Stumpff functions C(z) and S(z). The results showed that when z grew, Stumpff functions for hyperbola, parabola, and elliptical orbits were also growing. They intersected and had a tendency towards zero for both hyperbola and parabola orbits, but for elliptical orbits, Stumpff functions

Since more than a decade, human rights dialogue in the European Mediterranean Region has been marked by a number of tensions. Although a number of factors contribute to such disputes, the effect of human rights conditionality, which ties EU economic cooperation progression with partner countries human rights advancement, on the dialogue has not been studied. Understanding the aspects, impacts, and effects of conditionality on Euro-Med relations is crucial for furthering dialogue. Yet this variable has been almost entirely neglected in academic and policy research. The research concludes several direct and indirect impacts of conditionality on human rights dialogue using a mixed methodology approach. Direct effects are reflected in the wi

Nanostructure of chromium oxide (Cr₂O₃-NPs) with rhombohedral structure were successfully prepared by spray pyrolysis technique using Aqueous solution of Chromium (III) chloride CrCl₃ as solution. The films were deposited on glass substrates heated to 450°C using X-ray diffraction (XRD) shows the nature of polycrystalline samples. The calculated lattice constant value for the grown Cr₂O₃ nanostructures is a = b = 4.959 Å & c = 13.594 Å and the average crystallize size (46.3-55.6) nm calculated from diffraction peaks, Spectral analysis revealed FTIR peak characteristic vibrations of Cr-O Extended and Two sharp peaks present at 630 and 578 cm-1 attributed to Cr-O “stretching

Providing Iraqi students with proficiency in English is the ultimate goal of the educational system which is a way of getting knowledge in the fields of arts, sciences, transferring knowledge and sciences to other communities. Therefore, conducting such a type of study is very important because the contents of English textbooks have a huge influence on learning of the students. Once the content of English textbooks contain errors as the correct one, this will effect on his/her learning. The present study is an attempt to evaluate the new course entitled “English for Iraq” for fifth grade students for secondary schools, by Olivia Johnston and Mark Farell. It aims to answer eleven questions relating to the following domains: strength, obj

An atomic force microscope (AFM) technique is utilized to investigate the polystyrene (PS) impact upon the morphological properties of the outer as well as inner surface of poly vinyl chloride (PVC) porous fibers. Noticeable a new shape of the nodules at the outer and inner surfaces, namely "Crater nodules", has been observed. The fibers surface images have seen to be regular nodular texture at the skin of the inner and outer surfaces at low PS content. At PS content of 6 wt.%, the nodules structure was varied from Crater shape to stripe. While with increasing of PS content, the pore density reduces as a result of increasing the size of the pore at the fiber surface. Moreover, the test of 3D-AFM images shows that the roughness of both su

    A total of 680 fish specimens belonging to 31 species from the Yemeni coastal waters of the Red Sea were inspected for the isopod infestations. Four isopod species belonging to three families of the suborder Cymothoida were detected. These are: Aega psora (Linnaeus, 1758) from Lethrinus lentjan, Natatolana insignis Hobbins and Jones, 1993 from Abalistes stellatus, Excorallana tricornis (Hansen, 1890) from Epinephelus fuscoguttatus, E. guttatus and E. tauvina and Alcirona krebsi Hansen, 1890 from Epinephelus microdon. All these isopod species are reported here for the first time from the Yemeni coastal waters of the Red Se