A first step in this research was to synthesize Schiff's bases(1-3)using an Amoxcilline intensification reaction with different aromatic aldehydes in absolute ethanol. In benzene and refluxing conditions,Schiff's bases were cyclized with succinic and Phthalic anhydride to give a new sequence of 1,3-oxazepine derivatives(4-6) and (7-9),respectively.The last step,cyclization reactions with sodium azide in THF solvent resulted in the formation of [10 and 11], which are supposed to be biologically significant.FT.IR, 1H-NMR and 13C-NMR (for compound 4,7,9, and 11),as well as melting points reported, were used to characterize these prepared compounds ,Bacillus (G+), Staphylococcus (G+), and E.Coli (G-)were screened against these compounds. . To i

The research included preparation of new Schiff base (L) by two steps: preparation of precursor [bis(2-formyl-6-methoxyphenyl) succinate] (P) by reacting (3-methoxy salicyl aldehyde) with (succinoyl dichloride) as first step then react the prepared precursor (P) with (ethanethioamide) to have the new Schiff base [bis(2-((ethane thioyl imino) methyl)-6-methoxy phenyl) succinate] (L) as second step. Characterized compounds based on Mass spectra, 1 H, 13CNMR (for ligand (L)), FT-IR and UV spectrum, melting point, molar conduct, %C, %H, and %N, the percentage of the metal in complexes %M, magnetic susceptibility, while study corrosion inhibition (mild steel) in acid solution by weight loss. These measurements proved that by (Oxygen, Nitrogen, a

Amoxicillin 1 was treated with thiosemicarbazide and Phosphoryl chloride to obtain a new derivatives that contains 1,3,4-thiadiazole moiety 2. Schiff bases compounds were synthesized by the reaction of compound 2 with different aldehydes such as benzaldehyde and some substituted Benzaldehyde; p-hydroy, p-Chloro, p-Nitro, p-Dimethylamino, p-Methyl, p-Methoxy, p-Ethoxy to give compounds 3a-h. The obtained compounds have tested towards gram -ve and gram +ve bacteria. The compound shows good to moderate result towards the bacteria.

In this paper, some chalcone derivatives (C1, C2) were synthesized based on the reaction of equal amount of substituted acetophenone and substituted banzaldehyde in basic medium. Oxazine and thiazine derivatives were prepared from the reaction of chalcones (C1-C2) with urea and thiourea respectively in a basic medium. Pyrazole derivatives were prepared based on the reaction of chalcones with hydrazine mono hydrate or phenyl hydrazine in the presence of glacial acetic acid as a catalyst. The new synthesized compounds were identified using various physical techniques like1 H-NMR and FT-IR spectra.

This work deals with preparation of zeolite 5A from Dewekhala kaolin clay in Al-Anbar region for drying and desulphurization of liquefied petroleum gas. The preparation of zeolite 5A includes treating kaolin clay with dilute hydrochloric acid 1N, treating metakaolin with NaOH solution to prepare 4A zeolite, ion exchange, and formation. For preparation of zeolite 4A, metakaolin treated at different temperatures (40, 60, 80, 90, and 100 °C) with different concentrations of sodium hydroxide solution (1, 2, 3, and 4 N) for 2 hours. The zeolite samples give the best relative crystallinity of zeolite prepared at 80 °C with NaOH concentration 3N (199%), and at 90 and 100°C with NaOH concentration solution 2N (184% and 189%, respectively). Ze

Abstract:
              In this study a type of polymeric composites from melting poly propylene as a basic substance with Palm fronds powder were prepared. Evaluation of polymeric composites was done by studying some of it is mechanical properties, which included:Yong modulus (E), Impact Strength (I.S), Brinell hardness (B.H) and Compression Strength (C.S). The polymeric composites were studied before and after reinforcment by comparing between them. There was an increase in resistance of Yong modulus (E), Impact Strength (I.S), Brinell hardness (B.H) and compression Strength (C.S). Also, the effect of some acids were studied such as (HCl, H₂

            In this study, pure SnO₂ Nanoparticles doped with Cu were synthesized by a chemical precipitation method. Using SnCl₂.2H₂O, CuCl₂.2H₂O as raw materials, the materials were annealed at 550°C for 3 hours in order to improve crystallization. The XRD results showed that the samples crystallized in the tetragonal rutile type SnO₂ stage. As the average SnO₂ crystal size is pure 9nm and varies with the change of Cu doping (0.5%, 1%, 1.5%, 2%, 2.5%, 3%),( 8.35, 8.36, 8.67, 9 ,7, 8.86)nm respectively an increase in crystal size to 2.5% decreases at this rate and that the crystal of SnO₂ does not change with the introduction of Cu, and S

PPSU hollow fiber nanofiltration membranes are prepared by applying two concentrations and various extrusion pressures according to the phase inversion method. Cross-sectional area and outer structures were characterized by using scanning electron microscope (SEM) and atomic force microscopy (AFM). In additional to the pore size distribution, either the mean roughness or the mean pore size of the PPSU hollow fiber surfaces was evaluated by AFM. It was found that the morphology of the PPSU fibers had both sponge-like and finger-like structures through different extrusion pressures and PPSU concentrations. The mean pore size and mean roughness for inner and outer surfaces were seen to be decreased with the increase of extrusion pressure at