The purpose of this research is to test the ability of the true strength index To time and manage trading in the financial market to select the best stocks and achieve a higher return than the Simple buy and hold strategy. And To achieve the objectives of the research, it relied on the main hypothesis, which is By using the True Strength Index to manage trading decisions buying and selling, can be achieved higher returns than the buy and hold strategy . The research community has been identified with all stocks listed on the Iraq Stock Exchange. Implementing the financial research tests requires selecting a sample from the research community that fulfills the test requirements according to a number of conditions So (38) companies we

Effect of nano and micro SiO2 particles with different weight percent (2,4,6,8 and 10) %wt on the Interlaminar fracture toughness (GIc) of 16-plies of woven roving glass fiber /epoxy composites prepared by hand lay – up technique were investigated. The specimens were tested using DCB test (mode I).
Area method was used to compute the interlaminar fracture toughness. The results show that, GIc would increase with the increasing in the filler content, the main failure in microcomposites and nanocomposites was delamination in the layers, the delamination reduced with increasing in the filler content.

In this work, excess properties (eg excess molar volume (VE), excess viscosity (ȠE), excess Gibbs free energy of activation of viscos flow (ΔG* E) and molar refraction changes (ΔnD) of binary solvent mixtures of tetrahydrofurfuryl alcohol (THFA) with aromatic hydrocarbons (benzene, toluene and p-xylene) have been calculated. This was achieved by determining the physical properties including density ρ, viscosity Ƞ and refraction index nD of liquid mixtures at 298.15 K. Results of the excess parameters and deviation functions for the binary solvent mixtures at 298.15 K have been discussed by molecular interactions that occur in these mixtures. Generally, parameters showed negative values and have been found to fit well to Redlich-Kister

New, simple and sensitive batch and Flow-injecton spectrophotometric methods for the determination of Thymol in pure form and in mouth wash preparations have been proposed in this study. These methods were based on a diazotization and coupling reaction between Thymol and diazotized procaine HCl in alkaline medium to form an intense orange-red water-soluble dye that is stable and has a maximum absorption at 474 nm. A graphs of absorbance versus concentration show that Beer’s law is obeyed over the concentration range of 0.4-4.8 and 4-80 µg.ml-1 of Thymol, with detection limits of 0.072 and 1.807 µg.ml-1 of Thymol for batch and FIA methods respectively. The FIA procedure sample throughput was 80 h-1. All different chemical and physical e

Proteinases (E.C.3.4.21) family are widely distributed in the nature; it was present in animals tissues , plants and microbial cell . Protease was purified from Zahdi seed (Phoenix dactylifera L.) by several steps included ammonium sulphite ppt (75%) saturation and dialyzed against the 80mM sodium phosphate buffer at pH 7.5 . The enzyme specific activity was 407.62 unit/mg protein. The obtained extract was purified by DEAE-Cellulose column followed by gel filtration through Sephacyl S-200 column .The enzyme specific activity ,yield and purification fold were 1873.49 unit/mg protein, 22.99 and 58.42% respectively. The results of protease characterization showed that the molecular weight was 25118 daltons as determined by gel f

The purpose of the current work was to evaluate the effect of Radiation of Gamma on the superconducting characteristics of the compound PbBr2Ca1.9Sb0.1Cu3O8+δ utilizing a 137Cs source at doses of 10, 15, and 20MRad. Solid state reaction technology was used to prepare the samples. Before and after irradiation, X-ray diffraction (XRD) and superconductor properties were examined. Results indicated that the tetragonal structure of our chemical corresponds to the Pb-1223 phase with an increase in the ratio c/a as a result of gamma irradiation. (Tc (onset) ) and on set temperature Tc (offset)) were also dropping from 113 to the 85.6 K and 129.5 to 97 K, respectively, for a transition temperatu

Solid waste generation and composition in Baghdad is typically affected by population growth, urbanization, improved economic conditions, changes in lifestyles and social and cultural habits.

A burning chamber was installed to burn cellulosic waste only. It was found that combustion reduced the original volume and weight of cellulosic waste by 97.4% and 85% respectively.

A batch composting study was performed to evaluate the feasibility of co-composting organic food waste with the cellulosic bottom ash in three different weight ratios (w/w) [95/5, 75/25, 50/50].

The composters were kept in controlled aerobic conditions for 7 days. Temperature, moisture, and pH were measured hourly as process succe

􀀑􀀃Pure Cu (CZTSe) and Ag dopant CZTSe (CAZTSe) thin films with Ag content of 0.1 and 0.2 were fabricated on coring glass substrate at R.T with thickness of 800nm by thermal evaporation method. Comparison between the optical characteristics of pure Cu and Ag alloying thin films was done by measuring and analyzing the absorbance and transmittance spectra in the range of (400-1100)nm. Also, the effect of annealing temperature at 373K and 473K on these characteristics was studied. The results indicated that all films had high absorbance and low transmittance in visible region, and the direct bang gap of films decreases with increasing Ag content and annealing temperature. Optical parameters like extinction coefficientrefractive index, and

In this work the effect of annealing temperature on the structure and the electrical properties of Bi thin films was studied, the Bi films were deposited on glass substrates at room temperature by thermal evaporation technique with thickness (0.4 µm) and rate of deposition equal to 6.66Å/sec, all samples are annealed in a vacuum for one hour. The X-ray diffraction analysis shows that the prepared samples are polycrystalline and it exhibits hexagonal structure. The electrical properties of these films were studied with different annealing temperatures, the d.c conductivity for films decreases from 16.42 ? 10-2 at 343K to 10.11?10-2 (?.cm)-1 at 363K. The electrical activation energies Ea1 and Ea2 increase from 0.031 to 0.049eV and