This study reports the fabrication of tin oxide (SnO₂) thin films using pulsed laser deposition (PLD). The effect of ⁶⁰Co (300, 900, and 1200 Gy) gamma radiation on the structural, morphological, and optical features is systematically demonstrated using X-ray diffraction (XRD), field emission scanning electron microscopy (FE-SEM), atomic force microscopy (AFM), and ultraviolet-visible light analysis (UV-Vis), respectively In XRD tests, the size of the crystallites decreased from 45.5 to 40.8 nm for the control samples and from 1200 Gy to 60Co for the irradiated samples. Using FESEM analysis, the particle diameter revealed a similar trend to that attained using XRD; in particular, the average diameters were 93.8 and

This study involves the synthesis of a new class of silicon polymers, designated as P1-P7, derived from dichlorodimethylsilane (DCDMS) in combination with various organic compounds (Schiff bases prepared from different amines and appropriate aldehydes or ketones) [I-V] through condensation polymerization. The structures of all monomers and polymers were characterization by FTIR and 1HNMR spectroscopy (for some polymers). The results of thermogravimetric analysis (TGA) and differential scanning calorimetry DSC test show stable thermal behaviour. Polymers with a higher concentration of aromatic rings in their repeating structural units exhibited a higher temperature for weight loss, indicating increased thermal stability. Thermal meas

This study involves the synthesis of a new class of silicon polymers, designated as P1-P7, derived from dichlorodimethylsilane (DCDMS) in combination with various organic compounds (Schiff bases prepared from different amines and appropriate aldehydes or ketones) [I-V] through condensation polymerization. The structures of all monomers and polymers were characterization by FTIR and 1HNMR spectroscopy (for some polymers). The results of thermogravimetric analysis (TGA) and differential scanning calorimetry DSC test show stable thermal behaviour. Polymers with a higher concentration of aromatic rings in their repeating structural units exhibited a higher temperature for weight loss, indicating increased thermal stability. Thermal meas

Nanocomposite was prepared using unsaturated polyester (UP) resin as a matrix and graphene nanoparticles as a reinforcement material in six percentage weights (0, 0.1, 0.2, 0.3, 1 and 1.5%). Mechanical, calorimetric and thermal studies were performed on the (UP) resin/graphene nanocomposite. All tests showed a clear improvement of all mechanical properties examined (hardness, flexural strength (F.S), impact strength (I.S) and tensile strength (T.S)) with increasing graphene percentage. In addition, the temperature of glass transition and thermal conductivity of this composite increased with increasing graphene content.

It is known that the oral administration of ibuprofen caused an irritation of stomach as a side effect due to its carboxylic moiety. Ibuprofen ester was synthesized by linking the carboxylic moiety of ibuprofen and the hydroxylic group of paracetamol to reduce its side effect. Study the kinetic hydrolysis of prepared ester was examined at different values of physiological pH (1.0, 5.8, 6.4 and 7.4) at 37 ± 0.1 of 1 hour period. Measurements of absorbance were carried out by UV-Visible spectrophotometer to follow the stability of ester, it showed Pseudo first order hydrolysis. The pH- apparent rate profiles of ester was exhibited a good stability at pH 1.0 and pH 5.8. Pharmacological activity in vivo of prepared ester was evaluated in re

The species Vitex agnus-castus is an important medicinal plants and it is one of the cultivated and dicotyledon plants in Iraq. The anatomical of stem, petiole, midrib area, epidermis, veins, type of leaf stomata and seeds were studied by light microscope. In this research, shows the knowledge of anatomical characteristics of the studied plant, showing its importance as taxonomic characteristics through the sections of the stem, petiole, the midrib and the petals.

Introduction: This study aimed to evaluate the impact of ozonated water on water sorption and solubility of heat-cure acrylic resin. Methods: Thirty-three samples of heat-cured acrylic resin were manufactured and divided into three groups: control, immersion for 10 and 20 minutes in ozonated water. Water sorption and water solubility tests were carried out in line with ADA Standard No. 12 for denture-base acrylic resin. Data were analyzed using one-way ANOVA at a significance level of 5%. Results: There was a nonsignificant difference between the control and experimental groups regarding water sorption (P