In this work, the preparation of new multidentate Schiff-base lig and and its metal complexes are described. The formation of the lig and{ 2,2`((5-methyl-1,3-phenylene)-bis-(oxy))-bis-N`(E`)-2- hydroxybenzylideneacetohydrazide}[H2L] was prepared from the reaction {2,2-((5-methyl-1,3-phenylene)-bis-(oxy))- di-(acetohydrazide)}[M]precursor and salicylaldehyde in a 1:2 mole ratio, respectively. The reaction of the lig and [H2L] with (Cr+3 , Mn+2 and Fe+2 )metal ions in a 1:2 (L:M) mole ratio. Ligand and complexes were characterised via spectroscopic analyses; [FT-IR, UV-Vis spectroscopy,(C.H.N) microanalysis, chloride content, thermal analysis(TG), electrospray mass, magnetic susceptibility and conductivity measurements. The characterisation d

Abstract: In this research, nanofibers have been prepared by using an electrospinning method. Three types of polymer (PVA, VC, PMMA) have been used with different concentration. The applied voltage and the gap length were changed. It was observed that VC is the best polymer than the other types of polymers.

In this research, nanofibers have been prepared by using an electrospinning method. Three types of polymer (PVA, VC, PMMA) have been used with different concentration. The applied voltage and the gap length were changed. It was observed that VC is the best polymer than the other types of polymers.

Objective: The purpose of this work was to develop and optimize the emulgel formulation of piroxicam with two types of gelling agent chitosan and xanthan gum. The release profiles of prepared formulas were investigated. In addition, the rheology and stability of the best formula were investigated.Methods: Emulsified piroxicam was prepared to use oleic acid, tween 80 and PG with a ratio (3:10:10). In xanthan based emulgel, the xanthan gum (1% and 1.5%) was spread as powder on emulsified piroxicam with stirring until emulgel was formed. In chitosan-based emgels, Chitosan gel was added to emulsified piroxicam and stirring until the Emulgel was constructed. Chitosan gels were prepared by incorporating different concentration, 2%, 3%, 6%

In this investigation, the mechanical properties and microstructure of Metal Matrix Composites (MMCs) of Al.6061 alloy reinforced by ceramic materials SiC and Al₂O₃ with different additive percentages 2.5, 5, 7.5, and 10 wt.% for the particle size of 53 µ_m are studied. Metal matrix composites were prepared by stir casting using vortex technique and then treated thermally by solution heat treatment at 530 ⁰C for 1 hr. and followed by aging at 175 ⁰C with different periods. Mechanical tests were done for the samples before and after heat treatment, such as impact test, hardness test, and tensile test. Also, the microstructure of the metal matrix composites was examine

Atmospheric residue fluid catalytic cracking was selected as a probe reaction to test the catalytic performance of modified NaY zeolites and prepared NaY zeolites. Modified NaY zeolites have been synthesized by simple ion exchange methods. Three samples of modified zeolite Y have been obtained by replacing the sodium ions in the original sample with lanthanum and the weight percent added are 0.28, 0.53, and 1.02 respectively. The effects of addition of lanthanum to zeolite Y in different weight percent on the cracking catalysts were investigated using an experimental laboratory plant scale of fluidized bed reactor.

The experiments have been performed with weight hourly space velocity (WHSV) range of 6 to 24 h