A hand lay-up method was used to prepare Epoxy/ metal composites. Epoxy resin (EP) was used as a matrix with metal particles (Al, Cu, and Fe) as fillers.
The preparation method includes preparing square panels of composites with different weight percentage of fillers (10, 20, 30, 40, and 50%). Standard specimens (88mm in diameter) for thermal conductivity tests were prepared to measure thermal conductivity kexp.The result of experimental thermal conductivity kexp, for EP/metal composites show that, kexp increase with increasing weight percentage, For EP/ Al and EP/Cu composites, and it have have maximum values of 0.33 and 0.35 W/m.K, respectively. While kexp for EP/ Fe composite show slight increase with maximum value of 0.186 W/m.K.

EP/ metal composites were prepared as adhesives between two steel rods. Epoxy resin (EP) was used as a matrix with metal as fillers (Al, Cu, Fe,).
The preparation method for tensile adhesion tests includes two steel rods with adhesive composites between the rods to measure adhesion strength Sad and adhesion toughness Gad.
Results of tensile adhesion tests show that EP/ metals composite have maximum strength Sad for certain weight percentage of metals 2.95 and 9MPa at 10% for EP/Al and EP/Cu composite and 8.2MPa at 40% for EP/Fe composites

    The research aims to shed light on the impact of the application of the electronic services system on electronic banking activities in a sample of Iraqi banks, as investment in technology is the most important factor for the success and future growth of administrative companies in general, and banking in particular, as global economic developments in the field of Technology has led the majority of banking sectors in the world to undergo deep reforms and radical changes in the entity of their systems and mechanisms to confront competition and keep pace with economic changes, as the concept of banking services and its diversity changed with it, especially since persistence in the traditional approach no longer gi

حصاة الحالب واعراضها تؤثر على حياة المريض بصوره سلبيه، عدة علاجات متوفرة لعلاج حصاة الحالب من ضمنها مراقبه المريض، استخدام ادويه تفتيت الحصاة، استخدام موجات الفوق الصوتية تفتيت الحصاة بناظور الحالب، استخراج الحصاة جراحيا او بالناظور البطني, استخدام ناظور الحالب وتفتيت الحصاة بالليزر هي الطريقة المفضلة لعلاج حصاة اسفل الحالب. الهدف من الدراسة:لمقارنه تأثير ومضاعفات استخدام تقنيه الطحن او تقنيه التكسي

The current study presents an experimental investigation of heat transfer and flow characteristic for subcooled flow boiling of deionized water in the microchannel heat sink. The test section consisted of a single microchannel having 300μm wide nominal dimensions and 300μm height (hydraulic diameter of 300μm). The test section formed of oxygen-free copper with 72mm length and 12mm width. Experimental operation conditions spanned the heat flux (78-800) kW/m², mass flux (1700 and 2100) kg/m².s at 31˚C subcooled inlet temperature. The boiling heat transfer coefficient is measured and compared with existing correlations. Also, the experimental pressure drop is measured and compared with microscale p

Lorraine Hansberry’s A Raisin in the Sun (1959) appeared at the beginning of renewed political activity on the part of the blacks; it is a pamphlet about the dream of recognition of black people and the confusion of purposes and means to reach such recognition. It embodies ideas that have been uncommon on the Broadway stage in any period. Situations such as a black family moving into an all-white neighborhood were not familiar before this time; they were just beginning to emerge. In depicting this so realistically, Hansberry depends more on her personal experience as an African American embittered by social prejudices and discrimination. 

The study included adding antimony oxide to mixtures of coating metal surfaces (Enameling), after it was selected ceramic materials used in the coating metal pieces of the type of steel and cast iron in two layers. The first is called a ground coat and the second is a cover coat.
Ceramic materials layer for ground coat have been melted down in
platinum crucible at a temperature of 1200oC to prepare the glass
mixture (Frit). It was coated on metals at a temperature of 780oC for
two minutes, while the second layer was prepared glass mixture
(Frit) at a temperature of 1200oC, but was coated at a temperature of
760oC for two minutes.
Underwent tests crystalline state of powders (Frits) and enameled samples using X-ray di