Pore volume, pore diameter, and pore volume distribution of three of Iraqi natural clay deposites were measured using mercury intrusion porosimetry .The clays are white kaolin, colored kaolin, and bentonite .The results showed that the variation of the pore area of the clay deposites followed the following order :- Coloured Kaolin > White Kaolin > Bentonite While the pore volume may be arranged as in the following sequence:- White Kaolin > Coloured Kaolin >Bentonite Also , Bentonite exhibits the narrow range pore size distribution than the white and coloured kaolin.

Pharmaceutical-instigated pollution is a major concern, especially in relation to aquatic environments and drugs such as meropenem antibiotics. Adsorbents, such as multi-walled carbon nanotubes, offer potential as means of removing polluting meropenem antibiotics and other similar compounds from water. In order to evaluate the effectiveness of multi-walled carbon nanotubes in this capacity, various experimental parameters, including contact time, initial concentration, pH, temperature and the dose of adsorbent have been investigated. The Langmuir and the Freundlich isotherm models have been used. The data obtained using a modified Langmuir model have been consistent with the experimental ones; the best pH value has been obtained to have the

The pollution producing from textile industries effluents is growing since the years, due to at discharged lots of it in water without treatment. The resulting effluent is colourful, highly toxic, and poses a significant environmental hazard. This problem can be solved by using enzymic biological treatment, where the Congo red dye was used with concentrations (100,200,300,500) mg /L, pH values (3,4,5,6,7,8), and variable temperatures (25,35,45)°C, the best removal of Congo red (CR) dye  under optimum conditions for degradation was at  concentration of 100 mg/L, at (pH 6, 25 °C) with efficiency of 99.85 % using the peroxidase enzyme extracted from red radish plant, while the removal percentage decreased when increase dye concentration

The removal of yellow(W6GS) dye has been studied, by using Nano chitosan . Adsorption isotherms were studied under different Temperatures , the effect of salt ions and Equilibrium time were investigated . Adsorption isotherms were found to be comparable to the Langmuir equation .the adsorption results were evidently increased with the high temperature (Endothermic process ). The functions were calculated (ΔH, ΔG, ΔS) were calculated. The Kinetics of the adsorption was studied. The results were treated according to (Lagergren equation). The Kinetic experimental data properly correlated with the pseudo First order kinetic model

The oxidative degradation of Orange G dye by nanosized CeO₂ catalyst has been performed in this study. The catalyst was prepared by precipitation method. Various characterization techniques were carried out to study the physical and chemical properties of the synthesized catalyst. The XRD result confirms well the formation of CeO₂ cubic phase.  The FTIR result showed the effect of calcination temperature for CeO₂ was clearly observed due to reduction in band intensity compared to uncalcined Ce nitrate sample. Meanwhile, the diffused reflection spectra recorded reflection spectra at 414 nm with an energy gap of 3.2 ev. The decolorization of Orange G dye by oxidation process were carried out  unde

The nanostructured Manganese dioxide/Carbon fiber (CF) composite electrode was prepared galvanostatically using a facile method of anodic electrodeposition by varying the reaction time and MnSO4 concentration of the electrochemical solution. The effects of these parameters on the structures and properties of the prepared electrode were evaluated. For determining the crystal characteristics, morphologies, and topographies of the deposited MnO2 films onto the surfaces of carbon fibers, the X-ray diffraction (XRD), field emission scanning electron microscopy (FESEM), and atomic force microscopy (AFM) techniques were used, respectively. It found that the carbon fibers were coated with γ-MnO2 with a density that increased with increasing the de