The anatomic characteristics of the leaves of 22 taxa of Stachys L. representing seven of the currently recognized sections distributed in northern Iraq, were examined. The study did not found any variations in the characteristics of the stomata system of the leaves.Therewere variations with a good taxonomic value in other anatomic characteristics.Thevariations in characters of the mesophyll tissue in S.kurdica var.brevidens Bom ex Bhattacharjeewas bifacial but in S.kurdica var.kurdica Boiss. & Hohen.was unifacial .The study also found that the taxa S.benthamiana Bioss., S.lanigera (Bornm.) Rech.f. andS.kotscyi Bioss. with 3 vascular bundles in the middle vein while the taxa S.ballotiformis Vatke., S.megalodonta Hausskn. &Bo

The anatomic characteristics of the leaves of 22 taxa of Stachys L. representing seven of the currently recognized sections distributed in northern Iraq, were examined. The study did not found any variations in the characteristics of the stomata system of the leaves.Therewere variations with a good taxonomic value in other anatomic characteristics.Thevariations in characters of the mesophyll tissue in S.kurdica var.brevidens Bom ex Bhattacharjeewas bifacial but in S.kurdica var.kurdica Boiss. & Hohen.was unifacial .The study also found that the taxa S.benthamiana Bioss., S.lanigera (Bornm.) Rech.f. andS.kotscyi Bioss. with 3 vascular bundles in the middle vein while the taxa S.ballotiformis Vatke., S.megalodonta Hausskn. &Bornm.exP.H.Davis

An Indirect simple sensitive and applicable spectrofluorometric method has been developed for the determination of Cefotaxime Sodium (CEF), ciprofloxacin Hydrochloride (CIP) and Famotidine (FAM) using reaction system bromate-bromide and acriflavine (AF) as fluorescent dye. The method is based on the oxidation of drugs with known excess bromate-bromide mixture in acidic medium and subsequent determination of unreacted oxidant by quenching fluorescence of AF. Fluorescence intensity of residual AF was measured at 528 nm after excitation at 402 nm. The fluorescence-concentration plots were rectilinear over the ranges 0.1-3.0, 0.05-2.6 and 0.1-3.8 µg ml^-1 with lower detection limits of 0.013, 0.018 and 0.021 µg ml^-1 an

Todays, World is faced an energy crisis because of a continuous increasing the consumption of fuels due to intension demand for all types of vehicles. This study is one of the efforts dealing with reduce the weight of vehicles by using a new material of sandwich steel, which consists of two skin steel sheets with core of a polymer material. Resistance spot welding (RSW) can be easily implemented on metals; however a cupper shunt tool was designed to perform the resistance welding of sandwich steel with DP800 cover sheets to resolve a non-conductivity problem of a polymer core. Numerical simulations with SORPAS^®3D were employed to test the weldability of this new material and supported by many practical experiments. In conclus

Magnesium hydroxide was used as flame inhibitor to increased flame resistance for tires .Magnesium hydroxide was adding with (5%,10%) weight percents to rubber master batch of tire and then exposed the resulting material to a flame generated from gas torch with (10 mm) exposure distance . Method of measuring the surface temperature opposite to the flame was used to determine the heat transferred through tire material. The results were obtained shows enhanced flame resistance for tire by added magnesium hydroxide and this resistance increased by increasing hydroxide Percentage .

Mortar of ordinary Portland cement was blended with cockles shell
powder at different weight ratios to investigate the effect of powder
admixture on their strength and thermal conductivity. Results showed
that addition of cockles shell powder at 50% of mortar weight
improves hardness and compressive strength notably and reduces the
thermal conductivity of the end product. Results suggest the
possibility to incorporate cockles shell powders as constituents in
cement mortars for construction and plastering applications.

In this work, porous silicon gas sensor hs been fabricated on n-type crystalline silicon (c-Si) wafers of (100) orientation denoted by n-PS using electrochemical etching (ECE) process at etching time 10 min and etching current density 40 mA/cm2. Deposition of the catalyst (Cu) is done by immersing porous silicon (PS) layer in solution consists of 3ml from (Cu) chloride with 4ml (HF) and 12ml (ethanol) and 1 ml (H2O2). The structural, morphological and gas sensing behavior of porous silicon has been studied. The formation of nanostructured silicon is confirmed by using X-ray diffraction (XRD) measurement as well as it shows the formation of an oxide silicon layer due to chemical reaction. Atomic force microscope for PS illustrates that the p