The work concerned with studying the effect of (SiO2) addition as a
filler on the adhesive properties of (PVA). Samples were prepared as
sheets by using casting method. The mechanical properties showed
that increase in tensile strength from (34MPa) to (68MPa) when
(SiO2) added to (PVA). The adhesive strength showed that joint
properties depend upon specific adhesive characteristic of material
(PVA) and (SiO2\PVA)composites at different concentrations (1.5%,
2.5%, 3.5%, 4.5wt%), the cohesive strength of the adhesive material,
the joint design, and adherent type (Sponge Rubber(SR), Natural
leather (NL), Vulcanized Rubber(VR), and Cartoon). The results
proved the tensile strength increased with (SiO2) ratio, so

Volumetric chemical adsorption was done in a volumetric apparatus using hydrogen gas at room temperature on eleven platinum catalyst, commercial catalysts (RG-412,RG-402 ,RG-432, RG-451, RG-482, and PS-10) and prepared platinum catalysts with 0.1, 0.2 , 0.45 , and 0.55% by weight of Pt supported with Y-alumina. The results show that the metal crystallite area increases with increasing platinum content. The dispersion and particle size of metal crystallite located between 48.2-96.1% and 3.85-12.72 nm, respectively. For bimetallic catalysts, the hydrogen intake decrease in the following order : Re < Sn < Ir.

In this study, gold nanoparticles (AuNPs) were synthesized using a plasma jet system at different exposure times. Using ultraviolet, visible spectra, X-ray diffraction, the nanoparticles were characterized (XRD). A Plasmon surface resonance concentrated at 530, 540, and 533 nm for the prepared AuNPs. The pattern of XRD showed that the extreme peaks of the film reflect crystalline existence. The face-centered cubic structure of the gold nanoparticles was prepared for all samples, with an average crystallite size of 25-40 nm. The effect of AuNPs in vivo on liver function levels was measured. For all doses, we notice an increase in the ranks of liver function in the blood during the period of dosing, and it begins to decrease when the dosi

This study was carried out in Plant Tissue Culture Labs, College of Agricultural Engineering Sciences, University of Baghdad from November 2018 to June 2019. Fresh stem cuttings, 5 cm long were selected from 6-month old C-35 Citrange rootstock. Five concentrations of BA (0, 1, 1.5, 2 and 2.5 mg.L-1) were studied and addition of meta-Topolin (mT) at four concentrations (0, 1, 5 and 10 mg.L-1) was also studied to find out its effect individually on shoot number and shoot length in multiplication stage. Rooting media supplemented with four concentrations of IBA (0, 1, 2 and 3 mg.L-1) was also studied to find out its effect on rooting percentage, root number and root length. Results showed that BA as concentration of 2.5mg.L-1 significantly gav

The inhibitive action of polyvinyl alcohol –sodium nitrite (PVASN) composite on the corrosion of mild steel in simulated cooling water (SCW) has been investigated by weight loss and potentiodynamic polarization. The effect of composite concentration (PVA/SN) , pH, and exposure time on corrosion rate of mild steel were verified using 2 levels factorial design and surface response analysis through weight loss approach, while the electrochemical measurements were used to study the behavior of mild steel in (SCW) with pH between 6 and 8 and in absence and presence of (PVA) in solution containing different concentration of NaNO2. It was verified that all three main variables studied were statistically significant while their interaction is

This study synthesized polyacetal from the reaction of polyvinyl alcohol with para-nitrobenzaldehyde. Polyacetal/polyvinylpyrrolidone polymer blends were prepared using solution casting. Gold nanoparticles (AuNPs) and silver nanoparticles (AgNPs) were biosynthesized using onion peel extract as the reducing agent. Nanocomposites were fabricated by blending polyacetal/PVP with AuNPs and AgNPs at different ratios. XRD and FESEM characterized the AuNPs and AgNPs. FTIR, FESEM, TGA, and DSC characterized the polyacetal, polymer blends, and nanocomposites. DSC and TGA confirmed the improved thermal stability of the polymer blends and nanocomposites. Nanocomposites demonstrated higher efficacy in inhibiting lung cancer cell lines compared t