ZnS:Ce3+ nanoparticles were prepared by a simple microwave irradiation method under mild condition. The starting materials for the synthesis of ZnS:Ce3+ quantum dots were zinc acetate (R & M Chemical) as zinc source, thioacetamide as a sulfur source, cerium chloride as cerium source and ethylene glycol as a solvent. All chemicals were analytical grade products and used without further purification. The quantum dots of ZnS:Ce3+ with cubic structure were characterized by X-ray powder diffraction (XRD), the morphology of the film is seen by scanning electron microscopy (SEM) also by field effect scanning electron microscopy (FESEM) and XRD. Upon exposure to 460 nm light at zero bias voltage, ZnS:Ce3+/p-Si showed a high sensitivity of 4000% an

This study thoroughly investigates the potential of niobium oxide (Nb2O5) thin films as UV-A photodetectors. The films were precisely fabricated using dc reactive magnetron sputtering on Si(100) and quartz substrates, maintaining a consistent power output of 50W while varying substrate temperatures. The dominant presence of hexagonal crystal structure Nb2O5 in the films was confirmed. An increased particle diameter at 150°C substrate temperature and a reduced Nb content at higher substrate temperatures were revealed. A distinct band gap with high UV sensitivity at 350 nm was determined. Remarkably, films sputtered using 50W displayed the highest photosensitivity at 514.89%. These outstanding optoelectronic properties highlight Nb2O5 thin f

Klebsiella pneumoniae has been found in the urinary tract of some bladder cancer patients. Bacterial presence within tumor tissue may affect the tumor-microenvironment and consequently influence cancer behavior, development, and treatment response. This study investigated mesenchymal and stemness transdifferentiation of bladder cancer cell line due to environmental stress of K. pneumoniae. Cultures of urothelial bladder cancer cell line (T24) were infected with K. pneumoniae with different multiplicity of infection (MOI) for two and four days. Transdifferentiation-associated features were morphologically assessed.

Moreover, transdifferentiation markers were estimated using Q-PCR and immunohistoc

This paper includes the synthesis of some new nucleoside analogues starting with 2-substituted benzimidazole derivative (7-9), that synthesized by condensation of O-phenylenediamine with p-chloro benzaldehyde and two substituted benzoic acid , which on nucleophilic substitution with propargyl bromide gave a new N-substituted compounds (10-12). D-Fructose and D-galactose were chosen as a sugar moiety which were protected, brominated and azotated to give azido sugars (5) and (6), then they were subjected to 1,3-dipolar cycloaddition reaction with N-substuted compounds afforded bloked nucleoside analoges (13-16), which after hydrolysis gave our target the free nucleoside analogues (17-20). All prepared compounds were identified by FT-IR

The polymer was used to inhibit the corrosion of copper metal in salt media in different concentrations at room temperature using potentiometric polarization measurement. The polymer was prepared by mixing (0.1 M) 4-Hydroxy aniline (C6H7NO) with (0.25M) of ammonium persulfate as the initiator using the electro-deposition technique. The polymer’s results showed that copper in (3.5%) NaCl had good corrosion resistance. The findings demonstrate that the %IE for polymer-induced copper corrosion is 89.32% at 10 ppm concentration as a result of the 4-hydroxy aniline polymer’s adsorption from salt solution on the surface of copper metal. The numbers from the polarization method and the acquired standard data agree well. The coated copper by po

The polymer was used to inhibit the corrosion of copper metal in salt media in di erent concentrations at room temperature using potentiometric polarization measurement. The polymer was prepared by mixing (0.1 M) 4-Hydroxy aniline (C6H7NO) with (0.25M) of ammonium persulfate as the initiator using the electro-deposition technique. The polymer’s results showed that copper in (3.5%) NaCl had good corrosion resistance. The ndings demonstrate that the %IE for polymer-induced copper corrosion is 89.32% at 10 ppm concentration as a result of the 4-hydroxy aniline polymer’s adsorption from salt solution on the surface of copper metal. The numbers from the polarization method and the acquired standard data agree well. The coated copper by poly