This study was conducted on the possibility of manufacturing kids’ foods fortified by legumes. Three raw materials of boiled vegetables (carrots, potatoes and zucchini) were used, one of the pre-boiled legumes was added to the mixture, which included chickpeas, lentils, mung, soybean, fenugreek, by the percentage of 5% and 10%. The results of the chemical analysis showed no statistically significant differences (P <0.05) between the coefficients of moisture, ash and fiber. However, the ash ratio increased from 0.76 to 0.88% and fiber from 0.43 to 0.87%. As for protein and fat, A8 coefficient (add 10% soybean bean) recorded highest ratio of 2.54 and 0.71% respectively, the results of the analysis of mineral elements showed that the A8 coefficient were significantly higher in calcium, phosphorus and potassium content, which reached (10.64, 18.26, 145.53) Mg/100G, respectively, while (A10) coefficient significantly exceeded in iron content which was 0.89 mg per 100 gram. The sensory evaluation results referred that the mixtures having 5% of the laboratory-grown legumes got the highest sensory valuation scores. The results of the microbial analysis referred to possibility of, well-protected kids’ food mixtures for 24 hour in a refrigerator after preparation, where the microbial numbers are within the allowed limits for human consumption
FORTIFYING KIDS’ FOOD WITH LABORATORY GROWN-LEGUMES
AND STUDYING OF MICROBIAL AND NUTRITIONAL PROPERTIES
Kids’ food
laboratory-grown legumes
nutritional
microbial characteristics
Publication Date
Tue Jan 18 2022
Journal Name
Materials Science Forum
The Effect of Gamma Radiation on the Manufactured HgBa<sub>2</sub>Ca<sub>2</sub>Cu<sub>2.4</sub>Ag<sub>0.6</sub>O<sub>8+δ</sub> Compound
Gamma doses radiation
crystal size
strain
degree of crystallinity
Scherrer
crystallinity and Williamson equations.
In this article four samples of HgBa2Ca2Cu2.4Ag0.6O8+δ were prepared and irradiated with different doses of gamma radiation 6, 8 and 10 Mrad. The effects of gamma irradiation on structure of HgBa2Ca2Cu2.4Ag0.6O8+δ samples were characterized using X-ray diffraction. It was concluded that there effect on structure by gamma irradiation. Scherrer, crystallization, and Williamson equations were applied based on the X-ray diffraction diagram and for all gamma doses, to calculate crystal size, strain, and degree of crystallinity. I