Nanocrystalline copper sulphide (Cu2-xS) powders were synthesized by chemical precipitation from their aqueous solutions composed of different molar ratio of copper sulfate dehydrate (CuSO4.5H2O) and thiorea (NH2)2CS as source of Cu+2, S-2 ions respectively, and sodium ethylene diamine tetra acetic acid dehydrate (EDTA) as a complex agent. The compositions, morphological and structural properties of the nanopowders were characterized by energy dispersive spectroscopy (EDS), scanning electron microscope (SEM), and X-ray diffraction (XRD), respectively. The compositional results showed that the copper content was high and the Sulfur content was low for both CuS and Cu2S nanopowders. SEM images shows that all products consist of aggregate o

Some esters were prepared from reaction of different molecular weight of PVA with some acid chloride (prepared by reaction of acid with thionyl chloride or phosphorous pentachloride)in the presence of pyridine. The thermal and reological properties were studied. The increasing Of bulky groups decreasing stability of the thermal and reological properties.

In this work, prepared new ligand namely 5-(2,4-dichloro-phenyl)-1,3,4-oxadiazole-2-(3H)-thion, was obtained from the 2,4-dichlorobenzoyl chloride with hydrazine, after that reaxtion with CS2/KOH in methanol.

Background: The ultimate purpose of this prospective study is to estimate and measure swelling associated with surgical extrac¬tion of impacted mandibular third molars in different four post-operative times and to identify the risk factors associated with determination of their risk degree. Material and Methods: In this prospective cohort study 159 consecutive cases in which removal of impacted lower third molars in 107outpatients were evaluated. Five groups of variables have been studied which are regarded as a potential factor for swelling after mandibular third removal which will enable the surgeon to predict and counsel high risk patients in order to offer a preventive strategy. Results: Facial measurements were carried out on 1st, 2

A series of Schiff base-bearing salicylaldehyde moiety compounds (1-4) had been designed, synthesized, subjected to insilico ADMET prediction, molecular docking, characterization by FT-IR, and CHNS analysis techniques, and finally to their Anti-inflammatory profile using cyclooxygenase fluorescence inhibitor screening assay methods along with standard drugs, celecoxib, and diclofenac. The ADMET studies were used to predict which compounds would be suitable for oral administration, as well as absorption sites, bioavailability, TPSA, and drug likeness. According to the results of ADME data, all of the produced chemicals can be absorbed through the GIT and have passed Lipinski’s rule of five. Through molecular docking with PyRx 0.8, these

The synthesis of zeolite NaX from locally available kaolin has been studied. The operating conditions for zeolite NaX production from kaolin with good crystallinity were as follows; a gel formation step of metakaolin in alkaline medium in presence of additional silica to crystallize the zeolite was achieved at 60 oC for 1 hr,and with stirring. In ageing step of the reactants at room temperature for 5 days and crystallization step at 87±2 oC for 24 hr. The catalytic activity of catalyst prepared from local kaolin was studied by using cumene cracking as a model for catalytic cracking and compared with standard HY zeolite and HX zeolite catalysts. The activity test was carried out in a laboratory continuous flow unit with fixed bed reactor

The synthesis of zeolite NaX from locally available kaolin has been studied. The operating conditions for zeolite NaX production from kaolin with good crystallinity were as follows; a gel formation step of metakaolin in alkaline medium in presence of additional silica to crystallize the zeolite was achieved at 60 oC for 1 hr,and with stirring. In ageing step of the reactants at room temperature for 5 days and crystallization step at 87±2 oC for 24 hr. The catalytic activity of catalyst prepared from local kaolin was studied by using cumene cracking as a model for catalytic cracking and compared with standard HY zeolite and HX zeolite catalysts. The activity test was carried out in a laboratory continuous flow unit with fixed bed re

A multistep synthesis was established for the preparation of a new vanillic acid-1, 2, 4-1triazole-3-thiol conjugate (4). Finally, several aromatized aldehydes reacted with compound (4) to produce Schiff bases derivatives (5–11). The purpose of this research is to prepare new vanillic acid derivatives with 1, 2, 4-triazole-3-thiol heterocyclic ring structures and to evaluate their antimicrobial activity in a preliminary assessment. Fourier-transform infrared (FT-IR) and proton nuclear magnetic resonance spectroscopy (¹H-NMR) were used to verify the structures of the newly synthesized compounds. all the final synthesized compounds (