In this research, a novel thin film Si-GO10 and nanopowders Si-GO30 of silica-graphene oxide (GO) composite were prepared via the sol–gel method and deposited on glass substrates using spray pyrolysis. X-ray diffraction (XRD) results showed a relatively strong peak in the graphite layer that corresponds to the (002) plane. Transmission electron microscope (TEM) images showed that SiO2 nanoparticles were randomly distributed on the surface of GO plates, and the particle size in these nanopowders was below 50 nm. Field emission scanning electron microscopy (FESEM) analysis demonstrated that silica nanoparticles on the surface of GO plates exhibited almost spherical and rod-like nanoparticle shape, which in turn confirmed the formation of SiO2–GO nano-hybrids. Photocatalytic investigations revealed that the composite materials exhibit high activity for dye adsorption and decomposition. Si-GO10 thin film did not undergo degradation after 120 min; however, for Si-GO30 nanopowder, the adsorption peak intensity was reduced to 665 nm, indicating a decrease in the dye concentration in the solution. Fourier transform infrared scan (FTIR) analysis demonstrated that carboxylic functional groups are decreased by increasing silica particles. Photoluminescence (PL) spectrum in Si-GO10 thin film showed a sharp emission peak at about 665 nm. This spectrum completely disappeared in Si-GO30 nanopowders. Results of the antibacterial properties emphasized that Si-GO30 nanoparticle would prevent Escherichia coli growth after 20 h. The presented methodology allows for the synthesis of GO supported silicon dioxide nanoparticles for promising applications in photocatalytic and antibacterial fields.
(8)
(5)
A great deal of attention has recently been given to the use of polyvinyl alcohol and its suitably modified derivatives as aqueous and coating phase corrosion inhibitors because of their polymeric nature, relatively high aqueous phase solubility, and biodegradable properties. The purpose of this study was to investigate the thermal stability and inhibition efficiency of modified polyvinyl alcohol/carboxymethyl cellulose. Gold or silver nanoparticles were used to accomplish this goal. In the current study, polyvinyl alcohol reacted with newly synthesized compounds [I-VI] in DMF to produce modifications of polyvinyl alcohol [VII-XII]. To create [XIII-XVIII], modified polyvinyl alcohol is blended with carboxymethyl cellulose. Then, ble
... Show More
(1)
(16)
(15)
By unusual method for separating two isomers of a substituted nitro-coumarin using a soxhlet extractor and in controlling temperature to get a selective nitration reaction, several new Schiff base coumarins were synthesized from nitro coumarins as starting material, which were reduced by Fe in glacial acetic acid to produce corresponding amino coumarin derivatives. Then the latter was reacted with different aromatic aldehydes to produce the desired Schiff bases derivatives. After characterization by Fourier transform infrared (FT-IR), Proton nuclear magnetic resonance (1HNMR) and Carbon-13 nuclear magnetic resonance (C-NMR), all these compounds were evaluated as potential Antimicrobial and Antioxidant Agents.
(14)
(7)
SnS has been widely used in photoelectric devices due to its special band gap of 1.2-1.5 eV. Here, we reported on the fabrication of SnS nanosheets and the effect of synthesis condition together with heat treatment on its physical properties. The obtained band gap of the SnS nanosheets is in the rage of 1.37-1.41 eV. It was found that the photo-current density of a thin film comprised of SnS nanosheets could be enhanced significantly by annealing treatment. The maximum photo-current density of the stack structure of FTO/SnS/CdS/Pt was high as 389.5 mu A cm(-2), rendering its potential application in high efficiency solar hydrogen production.
(12)
(12)
In this study, synthesis of polymer Nanocomposites through the blending of prepared polymers with polyvinyl alcohol (a synthetic polymer) or chitosan (a natural polymer) then mixed with nano oxide silica by many steps. The new compound [I] was obtained via reaction of 3,3’-dimethoxybiphenyl-4,4’-diamine as starting material with malic anhydride in DMF then treatment with ammonium persulfate (NH4 )2 S2 O8 (as the initiator) in order to produce polymer [II]. Also, we prepared new polymers [III-V] by using the same starting material (3,3’-dimethoxybiphenyl-4,4’-diamine) with glutaric acid or adipic acid or isophthalic acid in DMF and pyridine. In this study, new polymer blending [VI-IX] and [X-XIII] were synthesized from a prepared pol
... Show More
(8)
Newly acid hydrazide was synthesized from ethyl 2-(2,3-dimethoxyphenoxy) acetate (2), which is cyclized to the corresponding 4-amino-1,2,4-triazole (3). Five newly azo derivatives (4a-e) were synthesized from this 1,2,4-triazole by converting the amine group to diazonium salt then reacted with various substituent phenol,as well three newly imine derivatives (5a-c) were synthesized from reacting the amine group of compound (3) with three aryl aldehyde. The thermal electro conductivity of these compounds was tested at 30, 50, 75 and 100 áµ’C. compound 4a showed interesting electro conductivity at 75áµ’C as well 5a at 75áµ’C while 5b showed significant conductivity at 100 áµ’C