Acrylic polymer/cement nanocomposites in dark and light colors have been developed for coating floors and swimming pools. This work aims to emphasize the effect of cement filling on the mechanical parameters, thermal stability, and wettability of acrylic polymer. The preparation was carried out using the casting method from acrylic polymer coating solution, which was added to cement nanoparticles (65 nm) with weight concentrations of (0, 1, 2, 4, and 8 wt%) to achieve high-quality specifications and good adhesion. Maximum impact strength and Hardness shore A were observed at cement ratios of 2 wt% and 4 wt%, respectively. Changing the filling ratio has a significant effect on the strain of the nanocomposites. The contact angle was i

Phenytoin selective electrodes were constructed based on penytoin-phosphotungstate (Ph-PT) complex with different plasticizers; di-butyl phosphate (DBP), tri-butyl phosphate (TBP), di-butyl phthalate (DBPH),and o-nitro phenyl octyl ether (NPOE) phthalate. The electrodes based on DBPH, ONPOE plasticizers gave Narnistain slope which are, 56.4 and 55.3mV/decade with detection limit of 1.9x10-5 M , 1.8x10-5 and concentration range 10-1 to 10-4 M and pH range 3.0 – 8.0. The electrodes based on TBP and DBP showed non-Nernistain slopes, 40.2,40.5 mV/decade for both plasticizers. Interfering of some cations was investigated and shows no interfering with electrodes response. Potentiometric methods were used for measuring phenytion in

It is generally accepted that there are two spectrophotometric techniques for quantifying ceftazidime (CFT) in bulk medications and pharmaceutical formulations.  The methods  are described as simple, sensitive, selective, accurate and efficient techniques. The first method used an alkaline medium to convert ceftazidime to its diazonium salt, which is then combined with the 1-Naphthol (1-NPT) and 2-Naphthol (2-NPT) reagents. The azo dye that was produced brown  and red in color with absorption intensities of ƛmax 585 and 545nm respectively. Beer's law was followed in terms of concentration ranging from  (3-40) µg .ml^-1 For (CFT-1-NPT) and (CFT-2-NPT), the detection limits were 1.0096 and 0.8017 µg.ml^-1, respec

Objective: To determine the quality assurance for maternal and child health care services in Baghdad City.
Methodology: A descriptive study is conducted throughout the period of November 28th 2008 to October 10th
2009. A simple random sample of (349) is selected through the use of probability sampling approach. The study
sample was divided into four groups which include (220) consumers, (35) medical staff, (72) nursing staff and (22)
organization structure (primary health care centers). Data were collected through the use of assessment tools. It was
comprised of four questionnaires and overall items included in these questionnaires are (116) items. The study
included assessment of organization structure. Data were colle

The aim of this study was to develop a sensor based on a carbon paste electrodes (CPEs) modified with used MIP for determination of organophosphorus pesticides (OPPs). The modified electrode exhibited a significantly increased sensitivity and selectivity of (OPPs). The MIP was prepared by thermo-polymerization method using N,N-diethylaminoethymethacrylate (NNDAA) as functional monomer, N,N-1,4-phenylenediacrylamide (NNPDA) as cross-linker, the acetonitrile used as solvent and (Opps) as the template molecule. The three OPPs (diazinon, quinalphos and chlorpyrifos) were chosen as the templates, which have been selected as base analytes which used widely in agriculture sector. The extraction efficiency of the imprinted polymers has been evaluat

Bauxite residue (red mud) is a waste material from alumina refineries in the Bayer process, containing significant quantities of valuable metals, notably scandium (Sc). The objective of this study is to recover Sc (III) from Hungarian bauxite residue by using hydrometallurgical processes, including solvent extraction and leaching. Red mud directly leached with hydrochloric acid to generate the leachate solution. The significant iron content (~38 %) in red mud makes it hard to recover scandium selectively due to comparable physicochemical characteristics. According to the findings, Fe (III) could be effectively extracted from hydrochloric acid leachate as HFeC14 using diethyl ether before Sc extraction. Protocol B demonstrated superior recov

Bauxite residue (red mud) is a waste material from alumina refineries in the Bayer process, containing significant quantities of valuable metals, notably scandium (Sc). The objective of this study is to recover Sc (III) from Hungarian bauxite residue by using hydrometallurgical processes, including solvent extraction and leaching. Red mud directly leached with hydrochloric acid to generate the leachate solution. The significant iron content (~38 %) in red mud makes it hard to recover scandium selectively due to comparable physicochemical characteristics. According to the findings, Fe (III) could be effectively extracted from hydrochloric acid leachate as HFeC14 using diethyl ether before Sc extraction. Protocol B demonstrated superior recov

The electrospun nanofibers membranes have gained considerable interest in water filtration applications. In this work, the fabrication and characterization of the electrospun polyacrylonitrile-based nonwoven nanofibers membrane are reported. Then, the membrane's performance and antifouling properties were evaluated in removing emulsified oil using a cross flow filtration system. The membranes were fabricated with different polyacrylonitrile (PAN) concentrations (8, 11, and 14 wt. %) in N, N-Dimethylformamide (DMF) solvent resulted in various average fiber sizes, porosity, contact angle, permeability, oil rejection, and antifouling properties. Analyses of surface morphology of the fabricated membranes before and after oil removal revealed