In this report Silver doped Tin Sulfide (SnS) thin films with ratio of (0.03) were prepared using thermal evaporation with a vacuum of 4*10-6 mbar on glass with (400) nm thickness and the sample annealing with ( 573K ). The optical constants for the wavelengths in the range (300-900) nm and Hall effect for (SnS and SnS:3% Ag) films are investigated and calculated before and after annealing at 573 K. Transition metal doped SnS thin films the regular absorption 70% in the visible region, the doping level intensification the optical band gap values from 1.5- 2 eV. Silver doped tin sulfide (SnS) its direct optical band gap. Hall Effect results of (SnS and SnS:3% Ag) films show all films were (p-type) electrical conductivity with resistivity of

Porous silicon (P-Si) has been produced in this work by photoelectrochemical (PEC) etching process. The irradiation has been achieved using diode laser of (2 W) power and 810 nm wavelength. The influence of various irradiation times on the properties of P-Si material such as P-Si layer thickness, surface aspect, pore diameter and the thickness of walls between pores as well as porosity and etching rate was investigated by depending on the scanning electron micrograph (SEM) technique and gravimetric measurements.

ZnTe possesses the proper optoelectronic properties as a candidate for device development. The structure and optical properties of ZnTe semiconductor thin films of 500 nm were studied using thermal evaporation technique. The influence of annealing temperatures on ZnTe thin films in the range ( R.T - 473 K). XRD and surface morphological analyses are used to examine the films. The ZnTe films are comparatively polycrystalline and cubic in phase, according to the XRD analysis. with a lattice constant of 0.61 nm upon an (111) orientation. The intensities of all the peaks rapidly increase though they show the same tendencies; it shows the crystallinity of the films becomes higher crystal size diameters (from 8.41 to 12.18nm) both increas

The addition of organic-inorganic hybrid nanoparticles presents a promising avenue for enhancing both the ionic conductivity at room temperature and the mechanical resilience of solid polymer electrolytes (SPEs). In this study, a novel nanocomposite solid polymer electrolytes (NSPEs) based on poly(ethylene oxide)-lithium difluoro(oxalato)borate (PEO20-LiDFOB) incorporating polyhedral oligomeric silsesquioxane-poly(ethylene glycol) (POSS-PEG(13.3)) hybrid nanoparticles were developed. And also reported the effect of POSS-PEG(13.3) hybrid nanoparticles on the structural, thermal, electrical, mechanical, and electrochemical properties of the (PEO20-LiDFOB) SPE. X-ray diffraction (XRD), differential scanning calorimetry analysis (DSC) and polar

Background: White spot lesions are esthetic problems caused by subsurface enamel demineralization that seen as white opacity. Aim of the study: This study aimed to evaluate and to compare the color change after the treatment of the white spot lesions with resin ‹nϔ‹Žtrƒt‹on and micro abrasion. Materials and Methods: rt‹ϔ‹…‹ƒŽ white spot lesions were generated on 48 premolar teeth by the use of a demineralization solution. The teeth were randomly divided using the Diagnodent into three study groups (16 teeth for each group) depending on the depth of the induced lesions: outer enamel, inner enamel and outer dentine. Then each group was fatherly subdivided into two groups (8 teeth for each group) the ϔ‹rst group was treated wit

Objectives: To assess the performance of a novel resin-modified glass-ionomer cement (pRMGIC) bonded to various tooth tissues after two-time intervals. Methods: 192 sound human molars were randomly assigned to 3 groups (n = 64): sound enamel, demineralised enamel, sound dentine. Sixty-four teeth with natural carious lesions including caries-affected dentine (CAD) were selected. All substrates were prepared, conditioned and restored with pRMGIC (30% ethylene glycol methacrylate phosphate (EGMP, experimental), Fuji II LC (control), Fuji IX, and Filtek™ Supreme with Scotchbond ™ Universal Adhesive. Shear bond strength (SBS) was determined after 24 h and three months storage in SBF at 37C. The debonded surfaces were examined using stereomi