Polymer matrix composites are suitable materials for medical applications, such as denture base resin polymethyl methacrylate (PMMA). This includes light weight and high strength. This paper describes the effect of selected weight fractions (1, 2, 3, 4 & 5) % wt of nano(Alumina AL2O3, Zirconia ZrO2, Hydroxyapatite HA and Halloysite nanoClay) reinforcements on the biopolymer matrix (PMMA). Some tribology tests were used to evaluate the prepared system (impact strength, hardness surface, and wear rate) tests. The samples were fabricated by (Hand Lay-Up) with different particle reinforcement percentages. All tests were accomplished at room temperature, and samples were developed according to the ASTM standard. The weight fraction of (4% for AL

This work aims to investigate the tensile and compression strengths of heat- cured acrylic resin denture base material by adding styrene-butadiene (S- B) to polymethyl methacrylate (PMMA). The most well- known issue in prosthodontic practice is fracture of a denture base. All samples were a blend of (90%, 80%) PMMA and (10%, 20%) S- B powder melted in Oxolane (Tetra hydro furan). These samples were chopped down into specimens of dimensions 100x10x2.5mm to carry out the requirements of tensile tests. The compression strength test specimens were shaped into a cylinder with dimensions of 12.7mm in diameter and 20mm in length. The experimental results show a significant increase in both tensile and compression strengths when compared to cont

Objective(s): The aim of this study is to compare the impact strength of a heat cured denture-base acrylic resin
reinforced with metal wire and glass fibers.

Methodology: Forty five specimens were prepared from pink heat cure acrylic resin. Specimens were grouped into;
group-I (control group) which consists of 15 specimens with no reinforcement, group-II which consists of 15 specimens
reinforced with metal wire, and group-III consists of 15 specimens reinforced with glass fibers. Specimens were tested
by using charpy impact machine.

Results: The result showed that there was a highly significant difference in impact strength value among the testing
groups at (P < 0.001).

Conclusion: The impact str

One of the rules concerning the control of civil transactions is the rule of no harm and harm, which was enacted by our Holy Prophet Muhammad (peace be upon him and his family). Scholars singled it out by research and investigation, and classified by non-scientists independent messages, showing the status of al-Qaeda in terms of its perception, meaning, branches and results, and the importance of this rule in the payment of damage and compensation for it has been provided by the Iraqi legislator generous within the provisions of Iraqi law in all its branches of public and private, as applied The judiciary Iraq The provisions of this rule have been issued and numerous decisions have been made to compensate for the damage and to give to ev

New polydentate ligand namely bis(N-carboxylatoethyl)-0,0`-dipyridinium) L was synthesised from the reaction of 0,0`-dipyridine with ethyl chloropropionate. Polymeric complexes of general formulae [Cr2(L)(N3)0]Cl2.H2O, Na2[Ag2(L)(N3)0].H2O and [M2(L)(N3)0].nH2O, where (M= Mn(II), Fe(II), Co(II), Ni(II), Cu(II), Zn(II) and Cd(II); (where n = 2;1;1;1;4;1 and 1, respectively)) are reported. The mode of bonding and overall geometry of the complexes were determined through physico-chemical and spectroscopic methods. These studies revealed octahedral geometry complexes. Molecular structure for the complexes has been optimised by CS Chem 3D Ultra Molecular Modelling and Analysis Program and supported a six coordinate geometry.

The aim of this work is to produce samples from Iraqi raw materials like Husyniat Bauxite (raw and burnt) and to study the effect of some additives like white Doekhla kaolin clays and alumina on that material properties were using sodium silica as a binding material. Five mixtures were prepared from Bauxite (raw and burnt) and kaolin clays, with an additive of (40) ml from sodium silica and alumina of (2.5, 5, 7.5,10 wt %) percentage as a binding material. the size grading was through sieving. The formation of all specimens was conducted by a measured gradually semi-dry pressing method under a compression force of (10) Tons and humidity ratio ranging from (5-10) % from mixture weight. Drying all specimens was done and then they were burn

In this paper, some chalcone derivatives (C1, C2) were synthesized based on the reaction of equal amount of substituted acetophenone and substituted banzaldehyde in basic medium. Oxazine and thiazine derivatives were prepared from the reaction of chalcones (C1-C2) with urea and thiourea respectively in a basic medium. Pyrazole derivatives were prepared based on the reaction of chalcones with hydrazine mono hydrate or phenyl hydrazine in the presence of glacial acetic acid as a catalyst. The new synthesized compounds were identified using various physical techniques like1 H-NMR and FT-IR spectra.

In this paper the new starting material 2-(5-chloro-1H-benzo[d]imidazole-2-yl) aniline (1) was synthesized by the condensation reaction of 4-chloro-o-phenylenediamine and anthranilic acid .The new Mannich base derivatives were synthesized using formaldehyde and different secondary amines to synthesize a new set of benzimidazole derivatives(2-5). Also, the new Schiff-base derivatives (6-10) were synthesized from the reaction of compound (1) with various aromatic aldehydes and the closure-ring was done successfully using mercapto acetic acid to get the new thiazolidine derivatives(11-12).These new compounds were characterized using some physical techniques like:FT-IR Spectra and 1HNMR Spectra.

Nanocrystalline copper sulphide (Cu2-xS) powders were synthesized by chemical precipitation from their aqueous solutions composed of different molar ratio of copper sulfate dehydrate (CuSO4.5H2O) and thiorea (NH2)2CS as source of Cu+2, S-2 ions respectively, and sodium ethylene diamine tetra acetic acid dehydrate (EDTA) as a complex agent. The compositions, morphological and structural properties of the nanopowders were characterized by energy dispersive spectroscopy (EDS), scanning electron microscope (SEM), and X-ray diffraction (XRD), respectively. The compositional results showed that the copper content was high and the Sulfur content was low for both CuS and Cu2S nanopowders. SEM images shows that all products consist of aggregate o