Films of CdSe have been prepared by evaporation technique with thickness 1µm. Doping with Cu was achieved using annealing under argon atmosphere . The Structure properties of these films are investigated by X-ray diffraction analysis. The effect of Cu doping on the orientation , relative intensity, grain size and the lattice constant has been studied. The pure CdSe films have been found consist of amorphous structure with very small peak at (002) plane. The films were polycrystalline for doped CdSe with (1&2wt%) Cu contents and with lattice constant (a=3.741,c=7.096)A°, and it has better crystallinty as the Cu contents increased to (3&5wt%) Cu. The reflections from [(002), (102). (110), (112), and (201)]planes are more prominen

The CdSe pure films and doping with Cu (0.5, 1.5, 2.5, 4.0wt%) of thickness 0.9μm have been prepared by thermal evaporation technique on glass substrate. Annealing for all the prepared films have been achieved at 523K in vacuum to get good properties of the films. The effect of Cu concentration on some of the electrical properties such as D.C conductivity and Hall effect has been studied.
It has been found that the increase in Cu concentration caused increase in d.c conductivity for pure CdSe 3.75×10-4(Ω.cm)-1 at room temperatures to maximum value of 0.769(Ω.cm)-1 for 4wt%Cu.All films have shown two activation energies, where these value decreases with increasing doping ratio. The maximum value of activation energy was (0.319)eV f

n-Hexane conversion enhancement was studied by adding TCE (Trichloro-ethylene) on feed stream using 0.3%Pt/HY zeolite catalyst. All experiments were achieved at atmospheric pressure and on a continuous laboratory unit with a fixed bed reactor at a temperature range 240-270◦C, LHSV 1-3h-1, H2/nC6 mole ratio 1-4.
By adding 435 ppm of TCE, 49.5 mole% conversion was achieved at LHSV 1h-1, temperature of 270ºC and H2/nC6 mole ratio of 4, while the conversion was 18.3 mol% on the same catalyst without adding TCE at the same conditions. The activation energy decreased from 98.18 for pure Pt/HY zeolite to 82.83 kJ/mole by adding TCE. Beside enhancement the activity, selectivity and product distribution enhanced by providing DMB (Dimethyl b

The researcher  tried to show the importance of obligation with the rules of professional conduct set by the Association of Accountants and Auditors of Iraqis when expressing an opinion the financial statements submitted tax administration and enhance the confidence of these lists, and adopted in the tax settling accounts process and its impact on tax revenues, and touched a researcher at the theoretical side of the search to the problem of research and of my Is there a trace of non- not to obligation by the rules of professional conduct in Iraq affect the tax revenue with the rules of professional conduct in tax revenue for companies research sample, the research aims to study the rules of professional conduct set by the Associatio

An essential tool for studying the web is its ability to show how energy moves through an ecosystem. Understanding and elucidating the relationship between species variety and their placement within the inclusive trophic dynamics is also beneficial. A food web ecological model with prey and two rival predators under fear and wind flow conditions is developed in this article. The boundedness and positivity of the system’s solution are established mathematically. The stability and existence constraints of the system’s equilibria are examined. The proposed system’s persistence limitations are established. Additionally, the bifurcation analysis of every potential equilibrium is examined using the Sotomayor theorem. To describe the

In this study, gold nanoparticle samples were prepared by the chemical reduction method (seed-growth) with 4 ratios (10, 12, 15 and 18) ml of seed, and the growth was stationary at 40 ml. The optical and structural properties of these samples were studied. The 18 ml seed sample showed the highest absorbance. The X- ray diffraction (XRD) patterns of these samples showed clear peaks at (38.25^o, 44.5^o, 64.4^o, and 77.95^o). The UV-visible showed that the absorbance of all the samples was in the same range as the standard AuNPs. The field emission-scanning electron microscope (FE-SEM) showed the shape of AuNPs as nanorods and the particle size between 30-50 nm. Rhodamine-610 (RhB) was prepared at 10<

Abstract:

The current research included " Diagnosis of the reality of the gap for the requirements of Business Continuity Management System According to International Standard (ISO 22301: 2012) in Midland Refineries Company (Daura Refinery) " , for development of an administrative system for Business Continuity is considered a priority in the present day, and in the light of the organizations dependence on computers and information technology in work and communication with others . the international legitimacy (represented by the international organization for standardization (ISO)) remains the basis for matching and commitment , and the importance of the application of Business Continuity Management Syst

The purpose of this paper is to preparing exercises for using the (Blazepod) device for advanced basketball players, and then identifying the effect of using the (Blazepod) device in developing some of the player's defensive movement for advanced basketball players. 12 players from the Adhamiya Sports Club, the category of applicants for the 2022/2023 sports year, where they were chosen in a deliberate manner from the community of origin represented by clubs, and the researchers used the defender player's movement test, and the results of the study showed that the special exercises prepared by the researcher using the (Blazepod) device affected the development Defensive skills (the movement of the defending player) greatly increased among a

     In the present work, a kinetic study was performed to the extraction of phosphate from Iraqi Akashat phosphate ore using organic acid. Leaching was studied using lactic acid for the separation of calcareous materials (mainly calcite). Reaction conditions were 2% by weight acid concentration and 5ml/gm of acid volume to ore weight ratio. Reaction time was taken in the range 2 to 30 minutes (step 2 minutes) to determine the reaction rate constant k based on the change in calcite concentration. To determine value of activation energy when reaction temperature is varied from 25 to 65 , another investigation was accomplished. Through the kinetic data, it was found that selective leaching was controlled by

     In the present work, a kinetic study was performed to the extraction of phosphate from Iraqi Akashat phosphate ore using organic acid. Leaching was studied using lactic acid for the separation of calcareous materials (mainly calcite). Reaction conditions were 2% by weight acid concentration and 5ml/gm of acid volume to ore weight ratio. Reaction time was taken in the range 2 to 30 minutes (step 2 minutes) to determine the reaction rate constant k based on the change in calcite concentration. To determine value of activation energy when reaction temperature is varied from 25 to 65 , another investigation was accomplished. Through the kinetic data, it was found that selective leaching was controlled by surface chemical reactio