Everywhere carriers incur a measure of liability for the safety of the goods. Carriers are liable for any damage or for the loss of the goods that are in their possession as carriers unless they prove that the damage or loss is attributable to certain excepted causes. Damaged and lost items can unfortunately be a common problem when shipping freight. Legal responsibilities arise due to loss or damage during transit while cargo is in their care. This study intends to investigate the nature of the liability of the maritime carrier when this liability is realized, and the extent to which it can be paid or disposed of given the risks realized from the transportation process, which may result in damage or loss of the goods, and the damag

Shear lag is the phenomenon that occurs when a supported slender member undergoes deformation from lateral loading, causing in-plane non-uniform distribution of stresses that results in reducing the member’s minimum strength capacity. This paper investigates the behaviour of shear distribution in steel I-section and box girders when subjected to both static and impact loadings. Three-dimensional finite element analysis models were prepared in Strand7 and validated against experimental results providing a basis for further comparison research into shear lagging effects. A parametric study was conducted comparing the effects of impact loading through certain specified velocities at the midspan of restrained ends. It provided new ins

The structural, optical properties of cupper indium gallium selenite (CuIn1-xGaxSe) have been studied. CuIn1-xGaxSe thin films for x=0.6 have been prepared by thermal evaporation technique, of 2000±20 nm thickness, with rate of deposition 2±0.1 nm/sec, on glass substrate at room temperature. Heat treatment has been carried out in the range (373-773) K for 1 hour. It demonstrated from the XRD method that all the as-deposited and annealed films have polycrystalline structure of multiphase. The optical measurement of the CIGS thin films conformed that they have, direct allowed energy gap equal to 1.7 eV. The values of some important optical parameters of the studied films such as (absorption coefficient, refractive index, extinction coeffici

CdSe alloy has been prepared successfully from its high purity elements. Thin films of this alloy with different thicknesses (300,700)nm have been grown on glass substrates at room temperature under very low pressure (10-5)Torr with rate of deposition (1.7)nm/sec by thermal evaporation technique, after that these thin films have been heat treated under low pressure (10-2)Torr at (473,673)K for one hour. X-ray patterns showed that both CdSe alloy and thin films are polycrystalline and have the hexagonal structure with preferential orientation in the [100] and [002] direction respectively. The optical measurements indicated that CdSe thin films have allowed direct optical energy band gap, and it increases from (1.77- 1.84) eV and from

In the present work, pulsed laser deposition (PLD) technique was applied to a pellet of Chromium Oxide (99.999% pure) with 2.5 cm diameter and 3 mm thickness at a pressure of 5 Tons using a Hydraulic piston. The films were deposited using Nd: YAG laser λ= (4664) nm at 600 mJ and 400 number of shot on a glass substrate, The thickness of the film was (107 nm). Structural and morphological analysis showed that the films started to crystallize at annealing temperature greater than 400 oC. Absorbance and transmittance spectra were recorded in the wavelength range (300-
4400) nm before and after annealing. The effects of annealing temperature on absorption coefficient, refractive index, extinction coefficient, real and imaginary parts of d