(Cu1-x,Agx)2ZnSnSe4 alloys have been fabricated with different Ag content(x=0, 0.1, and 0.2) successfully from their elements. Thin films of these alloys have been deposited on coring glass substrate at room temperature by thermal evaporation technique under vacuum of 10-5Torr with thickness of 800nm and deposition rate of 0.53 nm/sec. Later, films have been annealed in vacuum at (373, and 473)K, for one hour. The crystal structure of fabricated alloys and as deposited thin films had been examined by XRD analysis, which confirms the formation of tetragonal phase in [112] direction, and no secondary phases are founded. The shifting of main polycrystalline peak (112) to lower Bragg’s angle as compared to Cu2ZnSnSe4 angle refers to incorpora

Thin films of Zinc Selenide ZnSe have been prepared by using thermal evaporation in vacuum technique (10-5Torr) with thickness (1000, 2700, 4000) A0 and change electrode material and deposited on glass substrates with temperature (373K) and study some electrical properties at this temperature . The graphs shows linear relation between current and voltage and the results have shown increases in the value of current and electrical conductivity with increase thickness and change electrode material from Aluminum to Copper

Silver sulfide and the thin films Ag2Se0.8Te0.2 and Ag2Se0.8S0.2 created by the thermal evaporation process on glass with a thickness of 350 nm were examined for their structural and optical properties. These films were made at a temperature of 300 K. According to the X-ray diffraction investigation, the films are polycrystalline and have an initial orthorhombic phase. Using X-ray diffraction research, the crystallization orientations of Ag2Se and Ag2Se0.8Te0.2 & Ag2Se0.8S0.2 (23.304, 49.91) were discovered (XRD). As (Ag2Se and Ag2Se0.8Te0.2 & Ag2Se0.8S0.2) absorption coefficient fell from (470-774) nm, the optical band gap increased (2.15 & 2 & 2.25eV). For instance, the characteristics of thin films made of Ag2Se0.8Te0.2 and Ag2Se0.8S0.2

Structural and optical properties of CdO and CdO0.99Cu0.01 thin
films were prepared in this work. Cadmium Oxide (CdO) and
CdO0.99Cu0.01semiconducting films are deposited on glass substrates
by using pulsed laser deposition method (PLD) using SHG with Qswitched
Nd:YAG pulsed laser operation at 1064nm in 6x10-2 mbar
vacuum condition and frequency 6 Hz. CdO and CdO0.99Cu0.01 thin
films annealed at 550 C̊ for 12 min. The crystalline structure was
studied by X-ray diffraction (XRD) method and atomic force
microscope (AFM). It shows that the films are polycrystalline.
Optical properties of thin films were analyzed. The direct band gap
energy of CdO and CdO0.99Cu0.01 thin films were determined from
(αhυ)1/2 v

The present work involved synthesis of new thiozolidinone derivatives,These derivatives could be divided into three type of compounds; quinolin-2-one[V]a,b ,Schiff bases[VI]a,b and imide compounds[VII]a-d. The reaction p-Hydroxyacetophenone with thiosemicarbazide led to formation thiosemicarbazon compound [II], the reacted of thiosemicarbazone with chloro acetic acid in CH3CO2Na led to yield 4- thiazelidinone compound[III] in addition, thiosemicarbazide was POCl3 to [III] give [IV] compound used intermediates to synthesis new compounds of reacted with two type of coumarin in glacial acetic acid to give quinolin-2-one[V]a,b, The later compound refluxing with different benzaldehyde in dry benzene and glacial acetic acid give Schiff bases[VI]a

Worldwide attention is being focused on  nanocrystalline  zeolites  and they are replacing conventional ones due to their pronounced potential in many fields. In this study, NaY zeolite has been prepared hydrothermally using sol –gel method and modified to the proton type by ion –exchange process. Characterization is made using X-ray diffraction (XRD), thermogravimetric analysis (TGA),  Fourier transform infrared spectroscopy (FTIR),  Atomic force microscopy (AFM), Brunauer –Emmet- Teller (BET) nitrogen adsorption method, Ammonia Temperature programmed desorption (NH₃-TPD) and Scanning electron microscopy( SEM).  The effect of aging time, silica to alumina ratio is studied and the results sh

This work comprises the synthesis of new thioxanthone derivatives containing C-substituted thioxanthone. To obtain these derivatives, the o-mercapto benzoic acid was chosen as the starting material, which was reacted with dry benzene in sulfuric acid (98 %) to produce the thioxanthone (1). The 2,7-(disulfonyl phosphine imine) thioxanthone (4-8) were prepared from reaction of compound (1) with chlorosulfonic acid gave 2,7-(disulfonyl chloride) thioxanthone (2). Treatment of (2) with sodium azide to produce 2,7-(disulfonyl azide) thioxanthone (3). Condensation of (3) with phosphorus compounds afforded compounds (4-8). The 2,7-(disulfonamide) thioxanthone (9-21) was obtained when co

In the present paper we report the synthesis of a new ligand [HL][(2-1-[(2-hydroxy-benzylidene)-hydrazono]-ethyl) benzene-1, 3, 5-triol and its complexes with (Mn", Fe", Cd", and Hg") The ligand was prepared in two steps. In the first step a solution of salicylaldehyed in methanol reacted under reflux with hydrazinemonohydrate to give an intermediate compound which reacted in the second step with 2, 4, 6-trihydroxidernonohydrate giving the tientioned ligand. The complexes were synthesis by direct reaction of the corresponding metal chloride with ligand. The ligand and the complexes have been characterized by spectroscopic methods [" H NMR, IR, UV-Vis,, atomic absorption], HPLC microanalysis along with conductivity measurements. From the abo

The reaction of(2-oxo-2H-chromen-3-Carbonyl chloride)(k1) with hydrazine in boiling ethanol gives the hydrazide(K2).When compound (k2) reacts with various aromatic aldehydes ,the corres ponding Schiff bases(k3–k4) achieve new series of thiazotidines (k5–k6) and azetidinones (k7–k8) obtained from the reactions of appropriate Schiff bases with mercapto acetic acid and chloro acetyl chloride respectively. All the compounds are characterized by FT-IR,1H-NMR and GC-Ms.