Wastewater discharge containing organic dyes may pose a hazard to the environment, which necessitates that dye removal must occur prior to wastewater release into water bodies. Herein, copper oxide nanoparticles (CuO NPs) were prepared by a green precipitation method to enable decolorization of a cationic dye (methyl violet; MV) from aqueous media. Complementary tools were employed to characterize the CuO NPs adsorbent: spectroscopy (FTIR and UV-VIS), microscopy (FESEM and TEM), XRD, BET surface area analysis, and point of zero charge (pHPZC) via potentiometry. The FTIR bands at 722, 663, 569, and 465 cm−1 correspond to the vibrational modes of CuO NPs, along with the optical absorbance band at 275 nm that supports the formation of Cu

Electrodeposition of metal oxides on graphite electrodes can improve their ability to remove organic substances. In this work, multicomponent oxides of Mn, Co, and Ni were electrochemically deposited on both the anode and cathode of graphite electrodes to enhance their performance in removing phenol. Formation of the deposit was achieved within 2 h in current densities of 20, 25, 30, and 35 mA/cm2 for better composite properties. The deposited layer was characterized by testing the surface structure, morphology, composition, and roughness. X-ray diffraction (XRD), scanning electron microscopy (SEM), energy dispersive X-ray (EDX), and Atomic force microscopy (AFM) techniques facilitated these tests. The composite electrodes have synthesized

Fabrication of porous clay refractory insulating specimens from Iraqi kaolin with different percentage of Expanded Polystyrene (EPS) waste crumbs additions were investigated. After mixing and forming by hand molding, the specimens was dried and fired at 1300 oC. The structural, physical, mechanical and thermal properties of the refractory insulating products were measured. Maximum addition of EPS (1.25 wt%) lead to reduce the linear shrinkage to less than 1.7% and increased apparent porosity up to 50 %. As well as, the density, Modulus of rupture and thermal conductivity were reduced to 1.39 g/cm3, 4.1 MPa and 0.21 W/m.K, respectively. The final outcome, addition of EPS showed good results in the formation of pores without distorting the

Some mechanical and thermal properties of mullite samples prepared by mixing different phases of alumina and silica powders have been studied according to ASTM methods the cold crushing strength of the sintcred bodies.With different porosity, at room temperature was in the range(18-54)Mpa

Klebsiella pneumoniae causes lethal nosocomial infections, mostly affecting patients with severe burns. More than 80% of its isolates have shown resistance to routinely used antibiotics in parallel with increased infection rates. The study aimed to determine the molecular typing and genetic relatedness of K. pneumoniae. Therefore, 20 multidrug resistant (MDR) K. pneumoniae already isolated from infected burned wounds in two major hospitals of Al-Kut city east Iraq were subjected to genotyping analysis. The random amplified polymorphic DNA (RAPD)-based polymerase chain reaction (PCR) technique was used along with three oligonucleotide primers (P13, OPX-04, and OPY-01). The amplicons’ patterns of the electrophoresis-gel were analyzed by the

Background: This study aimed to use the combined mesio-distal crowns widths of maxillary incisors and first molars as predictors to the combined mesio-distal crowns widths of maxillary and mandibular canines and premolars. Materials and methods: The sample included 110 Iraqi Arab subjects with an age ranged between 17-25 years and class I skeletal and dental relations. The crown widths of maxillary teeth and mandibular canines and premolars were measured at the largest mesio-distal dimension on the study casts using digital electronic caliper with 0.01 mm sensitivity. Pearson’s correlation coefficient was used to determine the relation between the combined mesio-distal crowns widths of maxillary incisors and first molars and the combined